C210S483000, C210S488000, C210S489000, C210S490000, C210S500210, C210S500230, C210S500360, C210S645000, C264S041000, C422S042000, C422S045000, C422S048000
Reexamination Certificate
active
06409921
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to a process for producing a hydrophobic membrane using a thermally induced phase separation process, the membrane having a sponge-like, open-pored, microporous structure. The invention relates further to an integrally asymmetrical, hydrophobic membrane for gas exchange that is composed primarily of at least one polymer selected from the group of polyolefins and has a first and a second surface, the membrane having a support layer with an open-pored, microporous structure and adjacent to this support layer at least at one of the surfaces a separation layer with denser structure, and to the use of such membrane for blood oxygenation.
2. Description of Related Art
In a multitude of applications in the fields of chemistry, biochemistry, or medicine, the problem arises of separating gaseous components from liquids or adding such components to the liquids. For such gas exchange processes, there is increasing use of membranes that serve as a separation membrane between the respective liquid, from which a gaseous component is to be separated or to which a gaseous component is to be added, and a fluid that absorbs or releases this gaseous component. The fluid in this case can be either a gas or a liquid containing the gas component to be exchanged or capable of absorbing it. Using such membranes, an exchange surface can be provided for gas exchange and, if required, direct contact between the liquid and fluid can be avoided.
An important application of membrane-based gas exchange processes in the medical field is for oxygenators, also called artificial lungs. In these oxygenators, which are used in open-heart operations, for example, oxygenation of blood and removal of carbon dioxide from the blood take place. Generally, bundles of hollow-fiber membranes are used for such oxygenators. Venous blood flows in the exterior space around the hollow-fiber membranes, while air, oxygen-enriched air, or even pure oxygen is passed through the lumen of the hollow-fiber membranes. Via the membranes, there is contact between the blood and the gas, enabling transport of oxygen into the blood and simultaneously transport of carbon dioxide from the blood into the gas.
In order to provide the blood with sufficient oxygen and at the same time to remove carbon dioxide from the blood to a sufficient extent, the membranes must ensure a high degree of gas transport: a sufficient amount of oxygen must be transferred from the gas side of the membrane to the blood side and, conversely, a sufficient amount of carbon dioxide from the blood side of the membrane to the gas side, i.e., the transfer rates, expressed as the gas volume transported per unit of time and membrane surface area from one membrane side to the other, must be high. A decisive influence on the transfer rates is exerted by the porosity of the membrane, since only in the case of sufficiently high porosity can adequate transfer rates be attained.
A number of oxygenators are in use that contain hollow-fiber membranes with open-pored, microporous structure. One way to produce this type of membrane for gas exchange, such as for oxygenation, is described in DE-A-28 33 493. Using the process in accordance with this specification, membranes can be produced from meltable thermoplastic polymers with up to 90% by volume of interconnected pores. The process is based on a thermally induced phase separation process with liquid-liquid phase separation. In this process, a homogeneous single-phase melt mixture is first formed from the thermoplastic polymer and a compatible component that forms a binary system with the polymer, the system in the liquid state of aggregation having a range of full miscibility and a range with a miscibility gap, and this melt mixture is then extruded into a bath that is essentially inert with respect to the polymer and has a temperature lower than the demixing temperature. In this way, a liquid-liquid phase separation is initiated and the thermoplastic polymer solidified to form the membrane structure.
An improved process for producing such membranes, which permits specific adjustment of the pore volume, size, and wall, is disclosed in DE-A-32 05 289. In this process, 5-90% by weight of a polymer is dissolved, by heating to above the critical demixing temperature T
c
, in 10-95% by weight of a mixture of two compounds that are liquid and miscible at the solution temperature, whereby the employed mixture of polymer and compounds A and B has a miscibility gap in the liquid state of aggregation, compound A is a solvent for the polymer, and compound B increases the phase separation temperature of a solution consisting of the polymer and compound A. The solution is then given shape and by cooling brought to demixing and solidifying, and the compounds A and B are subsequently extracted.
The membranes disclosed in accordance with DE-A-28 33 493 or DE-A-32 05 289 have an open-pored, microporous structure and also open-pored, microporous surfaces. On the one hand, this has the result that gaseous substances, such as oxygen or carbon dioxide, can pass through the membrane relatively unrestricted and the transport of a gas then takes place as a Knudsen flow or Knudsen diffusion, combined with relatively high transfer rates for gases. On the other hand, however, in extended use of these membranes in blood oxygenation or generally in gas exchange processes with aqueous liquids, blood plasma or a portion of the liquid can penetrate into the membrane and, in the extreme case, exit on the gas side of the membrane, even if in these cases the membranes are produced from hydrophobic polymers, in particular polyolefins. This results in a drastic decrease in gas transfer rates. For medical applications for blood oxygenation, this is termed plasma breakthrough.
The plasma breakthrough time of such membranes, as producible in accordance with DE-A-28 33 493 or DE-A-32 05 289, is sufficient in most cases of conventional blood oxygenation to oxygenate a patient in a normal open-heart operation. However, the desire exists for membranes with higher plasma breakthrough times in order to attain higher levels of safety in extended heart operations and to rule out the possibility of a plasma breakthrough that would require immediate replacement of the oxygenator. A frequently demanded minimum value in this connection for the plasma breakthrough time is 20 hours. The aim, however, is also to be able to oxygenate premature infants or in general patients with temporarily restricted lung function long enough until the lung function is restored, i.e., to be able to conduct long-term oxygenation. Prerequisites for this are appropriately long plasma breakthrough times.
From EP-A-299 381, hollow-fiber membranes for oxygenation are known that have plasma breakthrough times of more than 20 hours, i.e., there is no plasma breakthrough even under extended use. With the otherwise porous membrane with cellular structure, this is attained by a barrier layer that has an average thickness, calculated from the oxygen and nitrogen flow, not exceeding 2 &mgr;m and is substantially impervious to ethanol. The membrane is essentially free of open pores, i.e., pores that are open both to the outside and to the inside of the hollow-fiber membrane. The membranes in accordance with EP-A-299 381 have a porosity of at most 50% by volume, since at higher porosity values the pores are interconnected and communication occurs between the sides of the hollow-fiber membranes, resulting in plasma breakthrough. In the barrier layer, the transport of gases to be exchanged is effected by solution diffusion.
The production of these membranes is conducted via a melt-drawing process, i.e., the polymer is first melt-extruded to a form a hollow fiber and then hot- and cold-drawn. In this case, only relatively low porosity values are obtained, which means that, in conjunction with the transport occurring in the barrier layer via solution diffusion, the attainable transfer rates for oxygen and carbon dioxide remain relatively low. Mo
Hornscheidt Ralf R.
Kessler Erich
Lang Armin J.
Müller Marcus O.
Wiese Frank
Kim John
Membrana GmbH
LandOfFree
Integrally asymmetrical polyolefin membrane for gas exchange does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Integrally asymmetrical polyolefin membrane for gas exchange, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Integrally asymmetrical polyolefin membrane for gas exchange will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2902796