Stock material or miscellaneous articles – All metal or with adjacent metals – Composite; i.e. – plural – adjacent – spatially distinct metal...
Reexamination Certificate
1999-04-23
2004-05-11
Dunn, Tom (Department: 1725)
Stock material or miscellaneous articles
All metal or with adjacent metals
Composite; i.e., plural, adjacent, spatially distinct metal...
C428S629000, C428S653000, C164S100000, C164S101000, C123S193200, C123S041840, C123S668000
Reexamination Certificate
active
06733903
ABSTRACT:
SPECIFICATION
Insert of pour-around die casting, rust preventive oil for insert of pour-around die casting, and method for pouring around an insert
BACKGROUND OF THE INVENTION
The present invention relates to a technique for incorporating an insert of pour-around die casting (hereinafter sometimes referred to simply as “insert”) with an aluminum alloy, more specifically an insert of pour-around die casting of an aluminum alloy, a rust preventive oil for preventing the insert from rusting, and a method for incorporating the insert with an aluminum alloy die casting.
It has been recently increased to produce cylinder blocks for internal combustion engines having a cylinder liner of a cast iron excellent in abrasion resistance incorporated with a light-weight aluminum alloy die casting. For such a type of incorporated die castings, it is essential that the insert of pour-around die casting is firmly incorporated with the aluminum alloy, and it is not permissible that with the use of the insert, the die casting productivity is inhibited and the rate of casting defects is increased.
Since the production of the insert of pour-around die casting and the production of the aluminum alloy die casting are separately conducted, it is usual that the insert is produced at first and then subjected to die casting after a substantial interval of time. If the surface of the insert is rusted, not only the adhesion with the aluminum alloy deteriorates but also the appearance of the die casting is poor. Accordingly, it is desirable to prevent the insert from rusting during at least the above interval.
The incorporation of the insert of pour-around die casting (by pouring a molten metal around an insert in a mold) has been made by the following methods.
(1) an insert is subjected to indirect rust-preventive treatment by use of an evaporative rust preventive agent, an evaporative rust preventive paper, an evaporative rust preventive film or the like,
(2) a rust preventive oil coated on the insert is removed just before the die casting, and
(3) die casting is made without removing the rust preventive oil.
However, the above method (1) brings about problems such as a reduction of productivity and an increase of packaging cost, and besides, adequate preventive effects can not be obtained. Further, the above method (2) brings about problems such as necessity of equipments for removal of the rust preventive oil and spaces thereof, and besides, reduction of workability and productivity. Further, the above method (3) brings about problems that, since large amounts of gas and burning residue are produced when the rust preventive oil is contacted with the molten aluminum alloy, formation of casting defects and reduction of adhesion are caused.
Further, adequate studies have not been made on the influences of the rust preventive oil composition and the film thickness on the gas and the burning residue generated when the rust preventive oil is contacted with the aluminum alloy melt, and also the influences of the gas and the burning residue on the die casting properties. For such reasons, it has not generally been practiced to employ a method for incorporating an insert of pour-around die casting coated with a rust preventive oil, directly with an aluminum alloy die casting.
However, in recent years, since the production of incorporated cylinder blocks for mass-produced automobiles has been increased, it is strongly demanded to produce the incorporated die castings of a high quality at a high productivity.
SUMMARY OF THE INVENTION
Accordingly, it is an object of the present invention to sufficiently prevent an insert of pour-around die casting from rusting during the period from its production to die casting, and to provide the insert by which an incorporated die casting of a high quality can be produced even if the insert is directly subjected to die casting, and a rust preventive oil for the insert used therefor, and a method for incorporating it.
In order to accomplish the above object, the present invention provides an insert of pour-around die casting, which is incorporated with an aluminum alloy die casting and has an organic film formed on a surface of the insert, wherein the organic film comprises a higher fatty acid ester, a petroleum sulfonate and a mineral oil and has a thickness of from 0.5 to 2 &mgr;m.
The present invention also provides a solvent-dilution type rust preventive oil of pour-around die casting, which comprises a higher fatty acid ester, a petroleum sulfonate, a mineral oil and a solvent and has a viscosity of from 1 to 5 cSt at 40° C.
The present invention further provides a method for incorporating an insert of pour-around die casting with an aluminum alloy die casting, which comprises coating a rust preventive oil which contains a higher fatty acid ester, a petroleum sulfonate, a mineral oil and a solvent and has a viscosity of from 1 to 5 cSt at 40° C. to form an organic film having a thickness of from 0.5 to 2 &mgr;m on a surface of the insert; placing the insert in a mold; and pouring an aluminum alloy around the insert for die casting.
In the present invention, the higher fatty acid ester in the organic film imparts a rust preventive performance and a low residue property, the petroleum sulfonate improves the rust preventive performance of the higher fatty acid ester, and the mineral oil functions as a rust preventive auxiliary. Further, by adjusting the thickness of the organic film to from 0.5 to 2 &mgr;m, the desired rust preventive performance can be securely obtained, and at the same time, the gas amount generated at the time of die casting and the burning residue amount tend to be low. Accordingly, even if direct die casting is carried out without removing the organic film, casting defects of the incorporated die casting such as voids and pinholes will not be increased, and the insert and the aluminum alloy thus incorporated or integrated can be firmly bonded, whereby the incorporated die casting of a high quality can be produced with a high productivity.
Further, by adjusting the viscosity of the rust preventive oil of the present invention at 40° C. to from 1 to 5 cSt, it is possible to control the thickness as coated to from 0.5 to 2 &mgr;m.
MODE FOR CARRYING OUT THE INVENTION
Hereinafter, the present invention will be described in further detail with reference to preferred embodiments.
The rust preventive oil of the present invention is a solvent-dilution type rust preventive oil, which contains a higher fatty acid ester, a petroleum sulfonate, a mineral oil and a solvent and has a viscosity adjusted to be from 1 to 5 cSt at 40° C.
In this case, it is preferred that the higher fatty acid ester has a weight-average molecular weight of from 300 to 600. If the weight-average molecular weight is less than 300, the gas amount generated when this oil is contacted with the aluminum alloy melt tends to be large, and if it exceeds 600, the burning residue amount tends to be large.
Further, the rust preventive oil of the present invention may preferably contain a higher fatty acid salt having a weight-average molecular weight of from 300 to 600 in addition to the above components, by which it is possible to impart water resistance to the formed organic film.
If the viscosity is less than 1 cSt, it is difficult to adjust the thickness of the formed organic film to not less than 0.5 &mgr;m, and if it exceeds 5 cSt, the formed organic film tends to exceed 2 &mgr;m.
As the composition of the rust preventive oil of the present invention, the higher fatty acid ester is preferably contained in an amount of from 3 to 8 vol %, more preferably from 3 to 6 vol %, most preferably from 3 to 5 vol %, the petroleum sulfonate is contained in an amount of from 2 to 5 vol %, more preferably from 2 to 4 volt % most preferably from 2 to 3 vol %, and the mineral oil is contained in an amount of from 5 to 15 vol %, more preferably from 5 to 10 vol %, most preferably from 5 to 8 vol %.
Incidentally, it can be said that the rust preventive oil of the present invention is similar to solvent-dilution t
Nobumoto Akinari
Saito Giichiro
Suzuki Takahiro
Dunn Tom
Lin I.-H.
Smith , Gambrell & Russell, LLP
Teipi Industry Co., Ltd.
LandOfFree
Insert of pour-around die casting, rust preventive oil for... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Insert of pour-around die casting, rust preventive oil for..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Insert of pour-around die casting, rust preventive oil for... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3213607