Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
2000-01-04
2001-10-09
Kulkosky, Peter F. (Department: 1615)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C528S158000, C525S144000, C526S062000, C526S208000
Reexamination Certificate
active
06300427
ABSTRACT:
BACKGROUND OF THE INVENTION
This invention relates to a method of inhibiting the formation of scale on reactor surfaces that are in contact with polymerizing vinyl monomers. In particular, it relates to the use of a terpolymer, which is the condensation reaction product of an aromatic compound, a carbonyl compound, and a thiourea, for that purpose.
When vinyl monomers are polymerized, scales of the polymer adhere to the reactor walls and to reactor components, such as stirrers. The deposition of this scale reduces the yield of the polymer, reduces heat transfer efficiency during heating and cooling of the reactor, and lowers monomer efficiency and general process control. Some of the scale flakes off during polymerization of the monomer and mixes with the rest of the polymer, which makes the polymer less processable and reduces its quality. For example, when vinyl chloride monomer (VCM) is polymerized, scales of polyvinyl chloride (PVC) can flake off and form “fish eyes” in the PVC.
Cleaning the reactor to remove this scale is normally required after each batch, resulting in considerable reactor downtime as well as increased cost in producing the polymer. Because VCM can become entrapped in the scale, the physical removal of the scale by an operator could result in the exposure of the operator to the harmful monomer.
EP 343,706 teaches that polythioureas of the general formula [NHRNHC(S)]n (where R is an arylene group substituted by a carboxylic acid group) can be used to reduce scale formation in vinyl chloride polymerization reactors. JP 01,217,016 discloses a scale preventing compound comprising an alkali metal xanthogenate, polyethyleneimine, and a dialdehyde. In JP 59,32,482, dithiocarboxylic acids or salts containing OC(═S)S or NC(═S)S groups and/or (RO)2P(S)SR derivatives are disclosed as scale preventing agents. U.S. Pat. No. 4,431,783 discloses that naphthol/formaldehyde condensates formed by a base-catalyzed process are effective scale-preventing agents vinyl chloride polymerization reactors. While many of these scale prevention agents are effective in preventing scale, they can alter the color of the resulting PVC, giving it a yellowish tinge. Customers of high quality PVC prefer a pure white or colorless PVC and regard any color in the PVC as an indication of inferior quality.
SUMMARY OF THE INVENTION
We have discovered a scale prevention agent for use in the polymerization of VCM and other vinyl monomers that is very effective in preventing the formation of scale on reactor components that come in contact with the VCM. Because there is little or no scale, there are fewer fish eyes.
The scale prevention agent of this invention is a terpolymer of an aromatic compound, a carbonyl compound, and a thiourea derivative. It is easily prepared from commercially available, inexpensive, non-toxic materials and can be applied in an aqueous medium, thereby avoiding the use of potentially harmful and flammable organic solvents. Quite unexpectedly, the scale preventing agent of this invention does not impart any color to the resulting PVC.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The terpolymer used in the process of this invention is the condensation reaction product of an aromatic compound, a carbonyl compound, and a thiourea. The aromatic compound contains the group:
where Q is OR or SR and R is hydrogen, alkyl from C
1
to C
15,
or aryl, alkaryl, or aralkyl from C
6
to C
15
. The Q group is preferably OR and the R group is preferably hydrogen as phenols are more readily available and work well. Preferred aromatic compounds include:
where Z is O or NOH, each R
1
is independently selected from OH, R, SO
3
R, and CO
2
R, and each R
2
is independently selected from R
1
, SH, SR, haloalkyl from C
1
to C
15
, and alkoxyaryl, naphthyl, and polycyclic aryl from C
6
to C
15
. Examples of suitable aromatic compounds include salicylic acid, 1-naphthol, thiosalicylic acid, hydroxybenzenesulfonic acid isomers, 4-hydroxybenzoic acid, 2′-hydroxypropiophenone oxime, and 2′-hydroxypropiophenone; 2′-hydroxypropiophenone and 1-naphthol are preferred due to their low cost, low toxicity, and good performance in the terpolymer condensate. Mixtures of the aromatic compounds can also be used.
The carbonyl compound can be an aliphatic mono or dialdehyde, an aromatic aldehyde, or an aliphatic mono or diketone. Compounds, such as trioxane, that form the carbonyl compound under the reaction conditions are also contemplated. Preferred carbonyl compounds have the general formula:
where each R
2
is independently selected as hereinabove defined and n is an integer from 1 to 10. Examples of suitable carbonyl compounds include acetaldehyde, glyoxal, benzaldehyde, dialkyl ketones such as acetone and methyl ethyl ketone, diaryl ketones such as benzophenone and ring-hydroxylated and sulfonated benzophenones, alkyl aryl ketones such as acetophenone, ring-hydroxylated acetophenones, and ring-sulfonated acetophenones, and formaldehyde and oligomers thereof, such as trioxane. Preferably, the carbonyl compound is formaldehyde or an oligomer thereof as those compounds have low cost, high reactivity, and are readily available. Mixtures of carbonyl compounds are also contemplated.
The thiourea has the general formula
where each R
2
is independently selected from NH
2
and the hereinabove definition. Examples of suitable thioureas include thiourea, thiocarbamide, monomethyl thiourea, 1,3-dimethyl-2-thiourea, 1-phenyl-2-thiourea, semicarbazide, thiosemicarbazide, and thiocarbohydrazide. The preferred thioureas are thiourea and thiosemicarbazide because they work the best, are inexpensive, and are readily available. Mixtures of thioureas can also be used.
The terpolymer is made by preparing a mixture of its three components. For every mole of the aromatic compound, about 0.1 to about 10 moles of the carbonyl compound and about 0.1 to about 10 moles of the thiourea can be used. If less than 0.1 moles of the carbonyl compound is used, the terpolymers produced will have a lower molecular weight than desired, and if more than 10 moles of the carbonyl compound is used, the terpolymer will have low solubility. If less than 0.1 moles of the thiourea is used, the terpolymer will be less effective in preventing scale formation and, if more than 10 moles of the thiourea is used, the terpolymer will be less soluble. Preferably, for each mole of the aromatic compound, about 0.1 to about 5 moles of the carbonyl compound and about 0.1 to about 5 moles of the thiourea are used.
The condensation reaction of the terpolymer components is carried out in an acidic medium which also acts as the catalyst. Mineral acids, such as hydrochloric acid and sulfuric acid, and organic acids, such as acetic acid, can be used. The strength of the mineral acid can vary in the range of about 1M to about 6M. Typically, about 50 to about 500 wt % of a catalyst is used, based on the total weight of the terpolymer components.
The condensation reaction of the terpolymer components can be performed in water or polar organic solvent such as an alcohol (e.g., methanol, ethanol, propanol), a ketone (e.g., acetone, methyl ethyl ketone), an ester (e.g., ethyl acetate), or a dipolar aprotic solvent, such as sulfolane, tetrahydrofuran, N,N-dimethylformamide, N-methylpyrrolidone, cyclohexanone, dimethoxyethane, or diethyleneglycol dimethyl ether. Water is the preferred solvent because it is nonflammable and is not hazardous to the operator. Mixed solvent systems comprising combinations of solvents, including combinations of organic solvents with water, can also be used. It is preferable to choose a solvent system such that the terpolymer product, once it is formed, is insoluble in the solution and precipitates.
The preparation of the terpolymer is described in the Indian Journal of Chemistry, Vol 22A, pages 117 to 119, (1983), herein incorporated by reference. Typically, the aromatic compound, the carbonyl compound, and the thiourea taken together constitute from about 5 to about 50 wt % of the reaction system weight. T
Hichri Bib
Krishnamurti Ramesh
Nagy Sandor
Wang Qi
Brookes Anne E.
Fuerle Richard D.
Kulkosky Peter F.
Occidental Chemical Corporation
LandOfFree
Inhibiting scale in vinyl monomer polymerization does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Inhibiting scale in vinyl monomer polymerization, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Inhibiting scale in vinyl monomer polymerization will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2594589