ABSTRACT:
Liquid compositions suitable for hot post-mold coating of cured sheet molding compound (SMC) parts comprise a reaction product of an epoxide and an unsaturated carboxylic acid mixed with a low shrink additive. These liquid compositions are used to smooth surfaces, fill porosity and other voids and to eliminate or reduce sink marks. Coatings typically are cured in less than two minutes and appear able to provide many features of normal painting without paint facilities except possibly those needed for touch-up.
The application method used to date has been to compression mold an SMC part in the usual way, separate the mold halves, inject the liquid composition and reclose the mold for a second cure cycle. A unique feature of the liquid composition is its ability to adhere to an uncleaned SMC molding.
REFERENCES:
patent: 3066112 (1962-11-01), Bowen
patent: 3179623 (1965-04-01), Bowen
patent: 3256226 (1966-06-01), Fekete et al.
patent: 3301743 (1967-01-01), Fekete et al.
patent: 3367992 (1968-02-01), Beardon
patent: 3466259 (1969-09-01), Jernigan
patent: 3793398 (1974-02-01), Hokamura
patent: 3836600 (1974-09-01), Brewbaker et al.
patent: 4010289 (1977-03-01), Kobayashi et al.
patent: 4081578 (1978-03-01), Vanessen
Randolph et al, Plastics Engineering Handbook, Reinhold N.Y. (1960) pp. 218-220.
The General Tire & Rubber Company
Thurlow Jeffery R.
LandOfFree
In-mold coating of sheet molding compound moldings does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with In-mold coating of sheet molding compound moldings, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and In-mold coating of sheet molding compound moldings will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-608251