Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – At least one aryl ring which is part of a fused or bridged...
Reexamination Certificate
1994-07-22
2001-09-18
Mulcahy, Peter D. (Department: 1713)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
At least one aryl ring which is part of a fused or bridged...
C524S462000
Reexamination Certificate
active
06291566
ABSTRACT:
FIELD OF THE INVENTION
The invention generally relates to flash-spinning polymeric film-fibril strands. More particularly, the invention concerns an improvement in such a process which permits flash-spinning of the strands from hydrocarbon/co-solvent spin liquids which, if released to the atmosphere, would not detrimentally affect the earth's ozone layer. Strands produced by flash-spinning from hydrocarbon/co-solvent spin liquids have higher tenacity and improved fibrillation over strands produced by flash-spinning from 100% hydrocarbon spin liquids.
BACKGROUND OF THE INVENTION
U.S. Pat. No. 3,081,519 (Blades et al.) describes a flash-spinning process for producing plexifilamentary film-fibril strands from fiber-forming polymers. A solution of the polymer in a liquid, which is a non-solvent for the polymer at or below its normal boiling point, is extruded at a temperature above the normal boiling point of the liquid and at autogenous or higher pressure into a medium of lower temperature and substantially lower pressure. This flash-spinning causes the liquid to vaporize and thereby cool the exudate which forms a plexifilamentary film-fibril strand of the polymer. Preferred polymers include crystalline polyhydrocarbons such as polyethylene and polypropylene.
According to Blades et al. in both U.S. Pat. No. 3,081,519 and U.S. Pat. No. 3,227,784, a suitable liquid for the flash spinning desirably (a) has a boiling point that is at least 25° C. below the melting point of the polymer; (b) is substantially unreactive with the polymer at the extrusion temperature; (c) should be a solvent for the polymer under the pressure and temperature set forth in the patent (i.e., these extrusion temperatures and pressures are respectively in the ranges of 165 to 225° C. and 545 to 1490 psia); (d) should dissolve less than 1% of the polymer at or below its normal boiling point; and should form a solution that will undergo rapid phase separation upon extrusion to form a polymer phase that contains insufficient solvent to plasticize the polymer. Depending on the particular polymer employed, the following liquids are useful in the flash-spinning process: aromatic hydrocarbons such as benzene, toluene, etc.; aliphatic hydrocarbons such as butane, pentane, hexane, heptane, octane, and their isomers and homologs; alicyclic hydrocarbons such as cyclohexane; unsaturated hydrocarbons; halogenated hydrocarbons such as trichlorofluoromethane, methylene chloride, carbon tetrachloride, chloroform, ethyl chloride, methyl chloride; alcohols; esters; ethers; ketones; nitrites; amides; fluorocarbons; sulfur dioxide; carbon disulfide; nitromethane; water; and mixtures of the above liquids. The patents illustrate certain principles helpful in establishing optimum spinning conditions to obtain plexifilamentary strands. Blades et al. state that the flash-spinning solution additionally may contain a dissolved gas, such as nitrogen, carbon dioxide, helium, hydrogen, methane, propane, butane, ethylene, propylene, butene, etc to assist nucleation by increasing the “internal pressure” and lowering the surface tension of the solution. Preferred for improving plexifilamentary fibrillation are the less soluble gases, i.e., those that are dissolved to a less than 7% concentration in the polymer solution under the spinning conditions. Common additives, such as antioxidants, UV stabilizers, dyes, pigments and the like also can be added to the solution prior to extrusion.
U.S. Pat. No. 3,227,794 (Anderson et al.) discloses a diagram similar to that of Blades et al. for selecting conditions for spinning plexifilamentary strands. A graph is presented of spinning temperature versus cloud-point pressure for solutions of 10 to 16 weight percent of linear polyethylene in trichlorofluoromethane. Anderson et al. describe in detail the preparation of a solution of 14 weight percent high density linear polyethylene in trichlorofluoromethane at a temperature of about 185° C. and a pressure of about 1640 psig which is then flash-spun from a let-down chamber at a spin temperature of 185°C. and a spin pressure of 1050 psig. Very similar temperatures, pressures and concentrations have been employed in commercial flash-spinning of polyethylene into plexifilamentary film-fibril strands, which were then converted into sheet structures.
Although trichlorofluoromethane has been a very useful solvent for flash-spinning plexifilamentary film-fibril strands of polyethylene, and has been the dominant solvent used in commercial manufacture of polyethylene plexifilamentary strands, the escape of such a halocarbon into the atmosphere has been implicated as a source of depletion of the earth's ozone layer. A general discussion of the ozone-depletion problem is presented, for example, by P.S. Zurer, “Search Intensifies for Alternatives to Ozone-Depleting Halocarbons”,
Chemical
&
Engineering News
, pages 17-20 (Feb. 8, 1988).
Clearly, what is needed is a flash-spinning process which uses a spin liquid which does not have the deficiencies inherent in the prior art. It is therefore an object of this invention to provide an improved process for flash-spinning plexifilamentary film-fibril strands of a fiber-forming polyolefin, wherein the spin liquid used for flash-spinning is not a depletion hazard to the earth's ozone layer. It is also an object of this invention to provide an improved process for flash-spinning plexifilamentary film-fibril strands of fiber-forming polyolefin, wherein the resulting flashspun plexifilaments have increased tenacity and improved fibrillation. Others objects and advantages of the present invention will become apparent to those skilled in the art upon reference to the detailed description of the invention which hereinafter follows.
SUMMARY OF THE INVENTION
In accordance with the invention, there is provided an improved process for flash-spinning plexifilamentary film-fibril strands of a fiber-forming polyolefin. Preferably, the polyolefin is polyethylene or polypropylene.
In one embodiment, the invention comprises an improved process for flash-spinning plexifilamentary film-fibril strands wherein polyethylene is dissolved in a hydrocarbon/co-solvent spin liquid to form a spin mixture containing 8 to 35 percent of polyethylene by weight of the spin mixture at a temperature in the range of 130 to 300° C. and a mixing pressure that is greater than 1500 psig, preferably greater than the cloud-point pressure of the spin mixture, which spin mixture is flash-spun at a spin pressure of greater than 1500 psig into a region of substantially lower temperature and pressure. The improvement comprises the spin liquid consisting essentially of a hydrocarbon spin liquid containing 4 to 5 carbon atoms and having an atmospheric boiling point less than 45° C. and a co-solvent spin liquid having an atmospheric boiling point less than 100° C., preferably between −100° C. and 100° C. The amount of the co-solvent spin liquid to be added to the C
4-5
hydrocarbon spin liquid must be greater than 10 percent by weight of the C
4-5
hydrocarbon spin liquid and the co-solvent spin liquid and must be sufficient to raise the cloud-point pressure of the resulting spin mixture by more than 200 psig, preferably more than 500 psig, at the polyethylene concentration and the spin temperature used for flash-spinning.
Preferably, the C
4-5
hydrocarbon spin liquid is selected from the group consisting of isobutane, butane, cyclobutane, 2-methyl butane, 2,2-dimethyl propane, pentane, methyl cyclobutane and mixtures thereof. Presently, the most preferred hydrocarbon spin liquids are butane, pentane and 2-methyl butane. Preferably, the co-solvent spin liquid comprises an inert gas such as carbon dioxide; a hydrofluorocarbon such as pentafluoroethane (hereinafter “HFC-1251”), 1,1,1,2-tetrafluoroethane (hereinafter “HFC-134a”), 1,1-difluoroethane (hereinafter “HFC-152a”) and their isomers; a hydrochlorofluorocarbon; a perfluorinated hydrocarbon; a polar solvent such as methanol, ethanol, propanol, isopropanol, 2-butanone, and tert-butyl alcohol; and
Samuels Sam Louis
Shin Hyunkook
E. I. Du Pont de Nemours and Company
Mulcahy Peter D.
LandOfFree
Hydrocarbon/co-solvent spin liquids for flash-spinning... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Hydrocarbon/co-solvent spin liquids for flash-spinning..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Hydrocarbon/co-solvent spin liquids for flash-spinning... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2465710