Hydraulic cement with accelerated high strength development

Details Hydraulic cement with accelerated high strength development Hydraulic cement with accelerated high strength development

1996-12-04

2000-11-21

Marcantoni, Paul

Compositions: coating or plastic

Coating or plastic compositions

Inorganic settable ingredient containing

106695, 106715, 106735, 106736, 106739, C04B 0732

Patent

active

06149724&

ABSTRACT:
A method of manufacturing cements based on calcium sulfoaluminate by forming a clinker through calcining a selection of typical cement precursor raw materials to temperatures of more than 1200.degree. C. in an industrial kiln, preferably with a preheater (typically of the cascading cyclone type) and precalciner, selected in such a manner that the clinker thus produced has a high content of calcium sulfoaluminate, tricalcium silicate and dicalcium silicate with no other calcium aluminates and, preferably during or prior to the grinding thereof, adding to the clinker thus produced (with the above recited basic components), effective amounts of calcium oxide or hydroxide and calcium sulfate, in order to activate said clinker. Upon said grinding, a temperature of about 100 to 125.degree. C. is to be attained for a time long enough to convert gypsum to the hemihydrate form, thus making sure that the calcium sulfate present in the thus obtained cement product is in a condition to react quickly during the hydration of said cement; thereby giving rise to the early formation of ettringite; for which the presence of a pH above 12 is needed. Also claimed is the novel activated cement resulting from the calcination and grinding methods of this invention.

REFERENCES:
patent: 3147129 (1964-09-01), Armstrong
patent: 3251701 (1966-05-01), Klein
patent: 3857714 (1974-12-01), Mehta
patent: 3860433 (1975-01-01), Ost et al.
patent: 4002484 (1977-01-01), Baudouin
patent: 4286991 (1981-09-01), Galer et al.
patent: 4404031 (1983-09-01), Sudoh et al.
patent: 4419136 (1983-12-01), Rice
patent: 4957556 (1990-09-01), Kunbargi
patent: 5356472 (1994-10-01), Odler
Chem. Abstracts vol. 105 No. 14, Oct. 6, 1986 Abstract No. 119076m.
T.A. Atakuziev et al. p. 302 XP002041126 (& SUR44 121 A) Jul. 15, 1986.
Chemical Abstracts vol. 109 No. 10 (Sep. 5, 1988) Abstract No. 78698X.
X Li et al. p. 340 XP000019927 {CN 103 649 A Dec. 9, 1987.
X. Li et al. p. 340. XP000019927 {CN 103 649 A (ID.) (Dec. 9, 1987)}.

Affiliated with

Also associated with

Rating

Hydraulic cement with accelerated high strength development does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Hydraulic cement with accelerated high strength development, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Hydraulic cement with accelerated high strength development will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-1253322