ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates generally to solid oxide fuel cells, and more particularly to such fuel cells having thin film electrolytes and thick film electrodes.
There is considerable current research and industrial activity on the development of PEM-based fuel cell systems for Micro-Power applications. The most common PEM systems proposed would use either hydrogen or methanol as a fuel. Hydrogen represents a challenge for fuel handling and distribution. Methanol may be promising in a Direct Methanol PEM fuel cell, but a reduction to commercial practice has not been demonstrated to date. Further, methanol has a relatively low (approximately one half) specific energy as compared to other hydrocarbon fuels such as, for example, butane, propane, gasoline, and diesel. Reported power densities from PEM cells seldom exceed 400 mW/cm2.
Solid Oxide fuel cells (SOFC) have been shown to offer the potential for internal reforming, as well as reported power densities as high as 1900 mW/cm2. A schematic representation of an SOFC is shown in
FIG. 1
, wherein V
0
oo
stands for oxygen vacancy. The oxygen reduction reaction (taking place at the cathode) is:
O
2
+4
e
−
→2O
2−
.
The O
2−
ion is transferred from the cathode through the electrolyte to the anode. Some typical fuel oxidation reactions (taking place at the anode) are:
2H
2
+2O
2−
→2H
2
O+4
e
−
(1)
2CO+2O
2−
→2CO
2
+4
e
−
(2)
The oxidation reaction at the anode, which liberates electrons, in combination with the reduction reaction at the cathode, which consumes electrons, results in a useful electrical voltage and current through the load.
The application of “thin film” processing techniques has been reported to reduce the practical operating temperature of SOFC from a range of 800° C. to 1100° C., down to about 500° C. or less.
It has also generally been believed that a “thin” electrolyte layer should not be too thin, and thicknesses less than 10 &mgr;m have been discouraged in order to avoid the possibility of short circuiting. Some researchers have attempted to provide an improved colloidal deposition technique over the prior technique—prior attempts to use colloidal deposition to deposit films thicker than 10 &mgr;m in a single step coating had previously resulted in cracking of the film after drying.
The “thin” film SOFCs are not, however, the SOFCs having the highest demonstrated performance to date. The higher performance/higher power density SOFCs are generally operated at higher temperatures, and use cermets and thick film processes for anode and cathode fabrication. These high performance SOFCs use “thin” film electrolytes; however, these “thin” film electrolytes generally have thicknesses of about 40 &mgr;m or more and are fabricated by electrochemical vapor deposition (EVD), tape casting, and other ceramic processing techniques.
A known thin film SOFC
100
is shown in FIG.
2
. SOFC
100
comprises a substrate
102
having thereabove a nitride layer
104
, a thin film nickel anode
106
, a thin film electrolyte
108
, and a thin film silver cathode
110
.
Some previously known SOFCs have been electrolyte supported (wherein the electrolyte layer provided some structural integrity and was thicker than either the anode or the cathode); cathode supported (wherein the cathode layer provided some structural integrity and was thicker than either the anode or the electrolyte); or anode supported (wherein the anode layer provided some structural integrity and was thicker than either the cathode or the electrolyte).
Fabrication has generally been recognized to be one of the major problems inherent with SOFC. This is due to the fact that all of the components (anode, cathode, electrolyte, interconnect material, etc.) should be compatible with respect to chemical stability and mechanical compliance (eg. thermal expansion coefficients). The layers also should be deposited such that suitable adherence is achieved without degrading the material due to use of too high a sintering temperature. These requirements have heretofore rendered successful and cost effective production of high performance SOFCs very difficult.
Thus, it would be desirable to provide a SOFC and method of fabricating a SOFC which overcome the above-mentioned drawbacks.
SUMMARY OF THE INVENTION
The present invention addresses and solves the above-mentioned problems and meets the objects and advantages enumerated hereinbelow, as well as others not enumerated, by providing a fuel cell, preferably a solid oxide fuel cell, comprising a thin film electrolyte layer having a first surface and a second surface, the first surface being opposed to the second surface. A thick film anode layer is disposed on the first surface; and a thick film cathode layer is disposed on the second surface.
A method of making the fuel cell of the present invention comprises the step of creating a well in one side of a dielectric or semiconductor substrate. A thin film solid oxide electrolyte layer is deposited on the surface of the well. An electrode layer is applied in the electrolyte coated well. A counter well is created in the other side of the substrate, the counter well abutting the electrolyte layer. The method further comprises the step of applying a counter electrode layer in the counter well.
REFERENCES:
patent: 4629537 (1986-12-01), Hsu
patent: 5190834 (1993-03-01), Kendall
patent: 5234722 (1993-08-01), Ito et al.
patent: 5284698 (1994-02-01), Marshall et al.
patent: 5395704 (1995-03-01), Barnett et al.
patent: 5518830 (1996-05-01), Worrell et al.
patent: 5527633 (1996-06-01), Kawasaki et al.
patent: 5656387 (1997-08-01), Barnett et al.
patent: 5741406 (1998-04-01), Barnett et al.
patent: 5750013 (1998-05-01), Lin
patent: 5783324 (1998-07-01), Binder et al.
patent: 5968673 (1999-10-01), Aizawa et al.
patent: 6004696 (1999-12-01), Barnett et al.
patent: 6007683 (1999-12-01), Jankowski et al.
patent: 6013386 (2000-01-01), Lewin et al.
patent: 6127058 (2000-10-01), Pratt et al.
patent: 6139985 (2000-10-01), Borglum et al.
patent: 6156448 (2000-12-01), Greiner
patent: 6214485 (2001-04-01), Barnett et al.
patent: 6232009 (2001-05-01), Batawi
patent: 6479178 (2002-11-01), Barnett
patent: 6509113 (2003-01-01), Keegan
patent: 2002/0025458 (2002-02-01), Faville et al.
patent: 1922970 (1969-12-01), None
patent: 516417 (1992-12-01), None
patent: WO 94/22178 (1994-09-01), None
patent: WO 97/30485 (1997-08-01), None
patent: WO00/45457 (2000-08-01), None
Barnett, Scott A. and Tsepin Tsai, “Bias Sputter Deposition of Dense Yttria-Stabilized Zirconia Films on Porous Substrates”,J. Electrochem. Soc., vol. 142, No. 9, Sep. 1995, p. 3084-3087.
Pham, A.Q., T.H. Lee, R.S. Glass, “Colloidal Spray Deposition Technique for the Processing of Thin Film Solid Oxide Fuel Cells”, Lawrence Livermore National Laboratory Preprint No. UCRL-JC-135760, Aug. 31, 1999.
Alan F. Jankowski, Robert T. Graff, Jeffrey P. Hayes and Jeffrey D. Morse, “Testing of Solid-Oxide Fuel Cells for Micro to Macro Power Generation”, Lawrence Livermore National Laboratory Preprint No. UCRL-JC-134198, May 1999.
J. Will, et al. Fabrication of thin electrolytes for second-generation solid oxide fuel cells. Solid State Ionics 131 (2000) 79-96, no month.
P. Charpentier, et al. Preparation of thin film SOFCs working at reduced temperature. Solid State Ionics 135 (2000) 373-380, no month.
Dove Tracy
Hewlett--Packard Development Company, L.P.
Ryan Patrick
LandOfFree
Hybrid thin film/thick film solid oxide fuel cell and method... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Hybrid thin film/thick film solid oxide fuel cell and method..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Hybrid thin film/thick film solid oxide fuel cell and method... will most certainly appreciate the feedback.