Plastic and nonmetallic article shaping or treating: processes – Forming continuous or indefinite length work – Layered – stratified traversely of length – or multiphase...
Reexamination Certificate
2001-07-27
2003-10-28
Mackey, James P. (Department: 1722)
Plastic and nonmetallic article shaping or treating: processes
Forming continuous or indefinite length work
Layered, stratified traversely of length, or multiphase...
C264S171270, C264S173120, C264S173160, C264S209100, C425S113000, C425S133100, C425S19200R, C425S380000, C425S462000
Reexamination Certificate
active
06638463
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to an extrusion die module. Specifically, the present invention relates to an extrusion die module having a flat compression seal and a conical or otherwise angled spillover surface. In addition, the present invention relates to a hybrid disk-cone extrusion die module having a spillover surface surrounded by a planar seal surfance. Further, the present invention relates to a method for utilizing an extrusion die module with a conical or otherwise angled spillover surface to minimize the die surface area wetted by an intermediate layer in an extrusion process involving at least three layers.
BACKGROUND OF THE INVENTION
An extrusion die for extruding melt material for the creation of flexible films has typically included at least one module having one or a plurality of flow channels to distribute melt over a spillover surface. The melt material may generally flow from the flow channels onto the spillover surface to be extruded therefrom to form a flexible film. In a typical flexible film “bubble” extruder, the module allows molten material to flow over a spillover surface to a gap between a die module and a central mandrel, whereupon a tube of plastic material may be extruded through an annular portion of the extrusion die. The concept also applies to extrusion blow molding parisons, wire coating, pipe extrusion, tube extrusion, etc. Moreover, a plurality of modules may be stacked in series to extrude a plurality of layers into a tubular structure. Each successive module may add a layer to the film structure when the molten material solidifies.
Extrusion die modules are typically nested cylinders, flat disk, or conical die modules. A flat disk module may allow a molten material to flow through flow channels directly onto a flat spillover surface located adjacent to the central mandrel. Each type of module typically consists of a pair of matching portions, or matching halves, that may be disposed one atop of another to form internal flow channels and spillover surfaces within the module. The matching halves may be bolted together to form a single extrusion die module, whereby the molten material may enter via the flow channels and may be extruded annularly after flowing over the spillover surface.
In melt extrusion, it is often desirable to streamline the flow of material from the flow surface of the module to the flow surface of the annular portion of the extrusion die. For example, the material flow may be streamlined by changing the flow direction angle of the material through the module and over the spillover surface by as small an angle as possible at any given point in the material flow. Flat disk extrusion dies are typically unable to generate a large degree of streamlined material flow because the plastic material generally flows through the flow channels of the module and over the spillover surface until it meets the annular portion of the extrusion die. At the annular portion of the extrusion die, the plastic material flow direction changes approximately 90 degrees to flow along the central mandrel that is located perpendicular to the spillover surface of the die module. Conical extrusion die modules are typically better adapted for promoting streamline material flow. The conical portion allows the flow direction angle to change less than 90 degrees as the material flows over the spillover surface and into the gap between the die module and the mandrel.
Moreover, conical extrusion die modules are capable of having a smaller wetted diameter and a smaller overall diameter than similar flat disk extrusion die modules. For example, the flow path of a conical extrusion die module with a flow path entirely at 45 degrees to the module axis needs only to be 71% (sine(45°)) of the radial length of a flat disk extrusion die module with the same area of spillover surface. Reducing both the wetted diameter and the overall die diameter has a number of benefits. For example, less wetted diameter means less hydraulic force is exerted by the melt material. Also, less overall module diameter means less module weight to support, move, and otherwise handle. Similarly, less overall module diameter means less thermal mass to heat and cool, thereby allowing for faster startups and changeovers and better thermal control. Each of the above effects may vary proportionally to the diameter of the die module squared (d
2
) thus enabling a small reduction in diameter to have a significant positive effect.
Leakage of molten material from the modules may cause many problems. For example, the plastic may leak out of the module to the ambient environment, thereby wasting material and creating potential housekeeping and safety issues. Additionally, the plastic material may degrade into carbon, gels, gas, and/or material of altered physical, chemical, and/or optical properties. Backflow of the degraded material may contaminate the extruded product. Further, plastic materials, such as PVdC and PVC, may form corrosive byproducts, if allowed to leak and degrade, and may lead to corrosion of the extrusion die. A damaged extrusion die is even more susceptible to leakage, leading to more degradation, thereby leading to further corrosion. Moreover, plastic flow outside of the flow channel may act as a hydraulic fluid under pressure to exert forces against adjacent extrusion die modules or other equipment. Consequently, the adjacent die modules may separate, causing further leakage and larger separating forces to be generated. Commonly, seal means are used to prevent plastic flow from leaking or otherwise leaving the flow channel areas of the modules.
A number of seal means for extrusion die modules are presently used. For example, flat surface to flat surface compression seals may be utilized for flat disk dies. Moreover, matched taper seals may be utilized for conical dies. Flat surface to flat surface compression seals are generally more effective than matched taper seals because the matched channels that are cut into matching conical die module halves may move out of alignment as the seals undergo surface wear. Surface wear is particularly damaging for conical dies having the flow channels disposed on the spillover surface(s). Because the flow channels are disposed on the angled portion of the spillover surface(s) of the conical die, surface wear causes the flow channels of the matching module portions to fall out of alignment. As the conical die channels move out of alignment, the degradation areas may increase and the problems discussed above may intensify. Conversely, as flat surface compression seal surfaces undergo surface wear, the matched channels that may be cut into the adjacent dies generally maintain their alignment, because the matching module portions are horizontal and the dislocation effect is minimized.
In multi-layer plastic extrusion, it is often desirable to combine certain material layers as early in the coextrusion system as possible. For example, it is desirable to encapsulate degradation-prone layers with more stable layers as soon as possible. Therefore, the more stable layers protect the degradation-prone layers from the heat of the extrusion system and decrease the time that the degradation-prone material is exposed to the heated surfaces of the extrusion system. In a standard flat disk die, the amount of time that a degradation-prone material may be exposed to heat of the annular portion of the die is related to the thickness of the extrusion die module itself.
When flat disk die modules and conical die modules are stacked in series, the distances that the degradation-prone material is exposed to the surfaces of the extrusion die module is related to the type of die module and order of placement of the die modules in the series. Material layers basically enter the annular portion of the extrusion die from the extrusion die modules separated by a distance approximately equal to the thickness of one die module, in the case of a first flat disk die module positioned downstream of a second flat disk die module. Similarly, material l
Blemberg Robert John
Davidson Randolph L.
Leyson Joseph
Mackey James P.
Pechiney Emballage Flexible Europe
LandOfFree
Hybrid disk-cone extrusion die module having a spillover... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Hybrid disk-cone extrusion die module having a spillover..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Hybrid disk-cone extrusion die module having a spillover... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3166625