ABSTRACT:
BACKGROUND OF INVENTION
1. Field of the Invention
The invention relates to superhard polycrystalline material elements for wear, cutting, drawing, and other applications where engineered superhard surfaces are needed. The invention particularly relates to polycrystalline diamond and polycrystalline diamond-like (collectively called PCD) elements with greatly improved wear resistance and methods of manufacturing them.
2. Description of Related Art
Polycrystalline diamond and polycrystalline diamond-like elements are known, for the purposes of this specification, as PCD elements. PCD elements are formed from carbon based materials with exceptionally short inter-atomic distances between neighboring atoms. One type of diamond-like material similar to PCD is known as carbonitride (CN) described in U.S. Pat. No. 5,776,615. In general, PCD elements are formed from a mix of materials processed under high-temperature and high-pressure into a polycrystalline matrix of inter-bonded superhard carbon based crystals. A common trait of PCD elements is the use of catalyzing materials during their formation, the residue from which, often imposes a limit upon the maximum useful operating temperature of the element while in service.
A well known, manufactured form of PCD element is a two-layer or multi-layer PCD element where a facing table of polycrystalline diamond is integrally bonded to a substrate of less hard material, such as tungsten carbide. The PCD element may be in the form of a circular or part-circular tablet, or may be formed into other shapes, suitable for applications such as hollow dies, heat sinks, friction bearings, valve surfaces, indentors, tool mandrels, etc. PCD elements of this type may be used in almost any application where a hard wear and erosion resistant material is required. The substrate of the PCD element may be brazed to a carrier, often also of cemented tungsten carbide. This is a common configuration for PCD's used as cutting elements, for example in fixed cutter or rolling cutter earth boring bits when received in a socket of the drill bit, or when fixed to a post in a machine tool for machining. These PCD elements are typically called polycrystalline diamond cutters (PDC).
There are numerous variations in the methods of manufacture of these PDC elements. For example various ranges of average diamond particle sizes may be utilized in the manufacture to enhance wear properties as shown in U.S. Pat. Nos., 4,861,350; 5,468,268; and 5,545,748 all herein incorporated by reference for all they disclose. Also, methods to provide a range of wear resistance across or into the working surface of a PDC are shown in U.S. Pat. Nos. 5,135,061 and 5,607,024 also herein incorporated by reference for all they disclose. However, because the wear resistance is varied by changing the average size of the diamond particles, there is an inherent trade-off between impact strength and wear resistance in these designs. As a consequence, the PDC elements with the higher wear resistance will tend to have poor impact strength, which for PDC's used in drilling applications, is often unacceptable.
Typically, higher diamond volume densities in the diamond table increases wear resistance at the expense of impact strength. However, modern PDC elements typically utilize often complex geometrical interfaces between the diamond table and the substrate as well as other physical design configurations to improve the impact strength. Although this allows wear resistance and impact strength to be simultaneously maximized, the tradeoff still exists, and has not significantly changed for the past several years prior to the present invention.
Another form of PCD element is a unitary PCD element without an integral substrate where a table of polycrystalline diamond is fixed to a tool or wear surface by mechanical means or a bonding process. These PCD elements differ from those above in that diamond particles are present throughout the element. These PCD elements may be held in place mechanically, they may be embedded within a larger PCD element that has a substrate, or, alternately, they may be fabricated with a metallic layer which may be bonded with a brazing or welding process. A plurality of these PCD elements may be made from a single PCD, as shown, for example, in U.S. Pat. Nos. 4,481,016 and 4,525,179 herein incorporated by reference for all they disclose.
PCD elements are most often formed by sintering diamond powder with a suitable binder-catalyzing material in a high-pressure, high-temperature press. One particular method of forming this polycrystalline diamond is disclosed in U.S. Pat. No. 3,141,746 herein incorporated by reference for all it discloses. In one common process for manufacturing PCD elements, diamond powder is applied to the surface of a preformed tungsten carbide substrate incorporating cobalt. The assembly is then subjected to very high temperature and pressure in a press. During this process, cobalt migrates from the substrate into the diamond layer and acts as a binder-catalyzing material, causing the diamond particles to bond to one another with diamond-to-diamond bonding, and also causing the diamond layer to bond to the substrate.
The completed PCD element has at least one body with a matrix of diamond crystals bonded to each other with many interstices containing a binder-catalyzing material as described above. The diamond crystals comprise a first continuous matrix of diamond, and the interstices form a second continuous matrix of interstices containing the binder-catalyzing material. In addition, there are necessarily a relatively few areas where the diamond to diamond growth has encapsulated some of the binder-catalyzing material. These “islands” are not part of the continuous interstitial matrix of binder-catalyzing material.
In one common form, the diamond body constitutes 85% to 95% by volume and the binder-catalyzing material the other 5% to 15%. Such an element may be subject to thermal degradation due to differential thermal expansion between the interstitial cobalt binder-catalyzing material and diamond matrix beginning at temperatures of about 400 degrees C. Upon sufficient expansion the diamond-to-diamond bonding may be ruptured and cracks and chips may occur.
Also in polycrystalline diamond, the presence of the binder-catalyzing material in the interstitial regions adhering to the diamond crystals of the diamond matrix leads to another form of thermal degradation. Due to the presence of the binder-catalyzing material, the diamond is caused to graphitize as temperature increases, typically limiting the operation temperature to about 750 degrees C.
Although cobalt is most commonly used as the binder-catalyzing material, any group VIII element, including cobalt, nickel, iron, and alloys thereof, may be employed.
To reduce thermal degradation, so-called “thermally stable” polycrystalline diamond components have been produced as preform PCD elements for cutting and/or wear resistant elements, as disclosed in U.S. Pat. No. 4,224,380 herein incorporated by reference for all it discloses. In one type of thermally stable PCD element the cobalt or other binder-catalyzing material in conventional polycrystalline diamond is leached out from the continuous interstitial matrix after formation. Numerous methods for leaching the binder-catalyzing material are known. Some leaching methods are disclosed, for example, in U.S. Pat. Nos. 4,572,722 and 4,797,241 both herein incorporated by reference for all they disclose.
While leaching the binder-catalyzing material may increase the temperature resistance of the diamond to about 1200 degrees C., the leaching process also removes the cemented carbide substrate. In addition, because there is no integral substrate or other bondable surface, there are severe difficulties in mounting such material for use in operation.
The fabrication methods for this “thermally stable” PCD element typically produce relatively low diamond volume densities, typically of the order of 80 volume % or less. This low diamond volume density enables
Griffin Nigel Dennis
Hughes Peter Raymond
Camco International (UK) Limited
Daly Jeffery E.
Turner Archene
LandOfFree
High volume density polycrystalline diamond with working... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High volume density polycrystalline diamond with working..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High volume density polycrystalline diamond with working... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3050859