Plastic and nonmetallic article shaping or treating: processes – With severing – removing material from preform mechanically,... – Forming continuous work followed by cutting
Reexamination Certificate
2002-03-26
2003-07-08
Eashoo, Mark (Department: 1732)
Plastic and nonmetallic article shaping or treating: processes
With severing, removing material from preform mechanically,...
Forming continuous work followed by cutting
C264S210700, C264S211000, C264S288400, C264S294000
Reexamination Certificate
active
06589463
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to a mono-axially oriented polyethylene terephthalate (PET) film with extraordinary mechanical strength in the machine direction (MD). A novel process is described that produces film from which tape for various applications can be manufactured. The tape is thinner but stronger than conventional tape.
BACKGROUND OF THE INVENTION
For some polyester films, high strength is, in general, required in the longitudinal direction, namely the winding direction of the film products, due to application demands. However, resistance against impact and other tearing stresses are also required. Accordingly, in many applications, polyester films or tapes having extremely high tensile strengths in the longitudinal direction with a high tear strength in the transverse direction, sufficient resistance to the stresses of folding, and tearing and impact in all directions, i.e., no tendency towards fibrillation are in demand in the market. Moreover, good dimensional stability or low thermal shrinkage, in addition to the above-mentioned characteristics, is also required.
Films which fulfill the above-mentioned requirements are usually biaxially stretched films of polyethylene terephthalate. In order to stretch film biaxially, however, a transverse (TD) stretching apparatus called a “tenter” is required. This apparatus has the drawback not only of high cost, but also requires lower production speed. Moreover, other problems, such as breaking at the time of stretching, or the like are apt to occur. In U.S. Pat. No. 2,556,295 and U.S. Pat. No. 3,627,579, processes for producing films having the above-mentioned properties by uniaxially stretching polyethylene terephthalate are described. According to these processes, tapes or films having less tendency to fibrillation have been obtained by performing the uniaxial stretching in two steps in the first patent is required, while, in the second patent, the use of a polymer with a high degree of polymerization is required. However, these processes have drawbacks also. The first puts more weight on fibers as seen from the examples thereof, but the strength in the transvere direction, required for films, is insufficient and heat shrinkage is also poor. The second process cannot meet both the properties of high strength and antifibrillation completely because these two properties have been shown to be mutually opposite in direction. Further, the strength is insufficient in the direction perpendicular to the stretching direction.
In contrast, British Patent No. 1,136,133 and Japanese Patent Publication No. 29398/1971, describe attempts to improve the drawbacks of conventional uniaxially stretched polyethylene terephthalate films by using polyethylene-1,2-diphenoxyethane-4,4′-dicarboxylate instead of polyethylene terephthalate as a raw material polymer, and uniaxially stretching the layer of the polymer. Of these two patents, the former prevents fibrillation by carrying out a heat treatment to increase the degree of crystallization before MD stretching and the latter prevents fibrillation by dividing MD stretching into two steps and inserting a heat treatment step between these two steps.
However, the processes of these two patents have drawbacks in that, if the degree of preliminary crystallization and the temperature of the intermediate heat treatment are lowered, sufficient reduction of the fibrillation effect cannot be attained. If these parameters are elevated, uniform stretchability becomes worse. This results in non-uniform stretching and strength in the transverse direction (T.D.) is lowered, which occurs because of the preliminary crystallization treatment.
In U.S. Pat. No. 4,286,011 to Wong, there is described the use of a polyester film that includes a mixture of PET and sufficient polytetramethylene terephthalate to increase film tear strength. The film may be unoriented, uniaxially oriented and biaxially oriented in the TD direction only. A tenter frame is used.
In U.S. Pat. No. 3,734,994 to D. L. Blecha, there is described a two stage draw process for producing polyethylene terephthalate film, but there is no heat set step or edge restraint.
SUMMARY OF THE INVENTION
The present invention provides a process for producing mono-axially oriented polyethylene terephthalate film having increased mechanical strength in the machine direction which comprises the steps of
drying substantially homopolymer or copolymer polyethylene terephthalate resin having an intrinsic viscosity in the range of about 0.65 to about 0.85 dg/cc and then blending the dried resin with from about 0.5 to about 4.0%, preferably from about 1 to about 3.0% by weight of anti-block additive;
extruding the resin blend to re-melt the resin and make it homogeneous;
casting a film web with the resin blend;
orienting the film immediately after casting it to produce a film of uniform thickness, by drawing the film at a ratio of from about 3.5 to about 4.5 times, preferably about 4.0 times, while constraining the web along its edges to prevent shrinkage in the TD direction;
allowing the film web to relax to a lower tension, cooling the film web, further relaxing the film web and then quenching it to room temperature;
subjecting the film web to a second orientation step under similar conditions to the first step except that the film is drawn at a draw ratio of about 1.025 to about 1.150, and at a draw temperature that is slightly higher than used in the first draw, e.g. about 90 to about 120° C., preferably about 100° C., preferably at a draw ratio of about 1.05 times while constraining the web along its edges to prevent shrinkage in the TD direction;
allowing the film to relax and annealing the film to a temperature in the range of from about 100 to about 180° C., preferably about 150° C. and then relaxing it further and cooling it to a temperature near room temperature; and
trimming and winding the film web into rolls.
The process of the present invention produces a product with superior properties. In particular the film does not fibrillate which makes it very useful in the production of tape for a variety of commercial purposes, such as tear tape for packaging. Examples of tear tape applications can be found in U.S. Pat. Nos. 5,806,281 of Krul et al.; 5,730,354 of O'Connor; 5,464,151 of Parker et al.; 4,844,962 of May et al.; and 5,203,935 of May et al. The disclosures of these patents are incorporated herein by reference.
DETAILED DESCRIPTION OF THE INVENTION
The film is first cast at an ambient temperature that is as low as is feasible and which is dependant on the environmental conditions in which the process is operated. It has been found that the process requires orienting the film immediately after casting, to as high a “Draw Ratio” as is practical, usually in the range of about 3.5 to about 4.5 times and preferably 4.0 times, and at a temperature as low as possible, but usually in the range of from about 70 to about 85° C., preferably about 70° C. without undue force being applied to draw the film web. The film web is held at almost constant width by constraining devices known in the art, examples of which are described in U.S. Pat. No. 4,477,407 issued Oct. 16, 1984 to Hetherington et. al., the disclosures of which are incorporated herein by reference. This patent describes an apparatus and process using a narrow gap draw for orienting a polymeric film. Another example of constraining means known in the art is found in Levy U.S. Pat. No. 4,428,724, the disclosures of which are incorporated herein by reference, which patent describes a microgrooved prcessing roll that reduces the air layer between the polymeric film being processed and the roll. This arrangement aids heat transfer, provides transverse shrinkage restraint and increases processing speed.
After this MD orientation step, the film is trimmed and wound for further processing. At this point in the process, the film has a medium strength in proportion to the draw ratio used. The film is now subjected to a second smaller draw ratio MD orientation process, again holding th
Rossi Sharon Anne
Vogt Oliver Harold
DuPont Canada Inc.
Eashoo Mark
LandOfFree
High tensile strength polethylene terephthalate film and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High tensile strength polethylene terephthalate film and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High tensile strength polethylene terephthalate film and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3104009