High-temperature wear-resistant sintered alloy

Details High-temperature wear-resistant sintered alloy High-temperature wear-resistant sintered alloy

1997-04-14

1999-09-07

Mai, Ngoclan

Specialized metallurgical processes, compositions for use therei

Compositions

Consolidated metal powder compositions

75231, 75243, C22C 3300

Patent

active

059490039

ABSTRACT:
The invention relates to a sintered alloy. This sintered alloy includes 3-13.4 wt % of W, 0.4-5.6 wt % or 0.8-5.9 wt % of V, 0.2-5.6 wt % of Cr, 0.1-0.6 wt % or 0.6-5.0 wt % of Si, 0.1-0.6 wt % or 0.2-1.0 wt % of Mn, 0.6-2.2 wt % of C, and a balance of Fe. The sintered alloy includes first and second phase which are distributed therein, in a form of spots, respectively. The second phase is in an amount of from 20 to 80 wt %, based on the total weight of the first and second phases. The first phase contains 3-7 wt % of W, 0.5-1.5 wt % of optional V, up to 1 wt % of Cr, 0.1-0.6 wt % or 0.6-5.0 wt % of Si, 0.1-0.6 wt % or 0.2-1.0 wt % of Mn, up to 2.2 wt % of C, and a balance of Fe. The second phase contains 3-15 wt % of W, 2-7 wt % of V, 1-7 wt % of Cr, 0.1-0.6 wt % or 0.6-5.0 wt % of Si, 0.1-0.6 wt % or 0.2-1.0 wt % of Mn, up to 2.2 wt % of C, and a balance of Fe. When the manganese contents of the first and second phases and the total of the sintered alloy are respectively in a range of from 0.2 to 1.0 wt %, sulfur is respectively contained therein in an amount of from 0.1 to 0.6 wt %. The sintered alloy has wear-resistant at high temperature and good compatibility without damaging mating part that is in contact with the sintered alloy.

REFERENCES:
patent: 4121927 (1978-10-01), Lohman et al.
patent: 4504312 (1985-03-01), Oaku et al.
patent: 4505988 (1985-03-01), Urano et al.
patent: 4552590 (1985-11-01), Nakata et al.
patent: 5031878 (1991-07-01), Ishikawa et al.
patent: 5462573 (1995-10-01), Baker et al.
patent: 5756909 (1998-05-01), Liimatainen et al.
Foreign Search Report.

Affiliated with

Also associated with

Rating

High-temperature wear-resistant sintered alloy does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with High-temperature wear-resistant sintered alloy, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High-temperature wear-resistant sintered alloy will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-1806104