Specialized metallurgical processes – compositions for use therei – Processes – Free metal or alloy reductant contains magnesium
Patent
1974-03-21
1976-01-20
Andrews, M. J.
Specialized metallurgical processes, compositions for use therei
Processes
Free metal or alloy reductant contains magnesium
75170, C22C 1902
Patent
active
039334813
ABSTRACT:
A continuous process for producing novel aligned composites of a Co-Si eutectoid type alloy having significant tensile strength is provided. The process comprises forming a melt of a Co.sub.3.sub.-x M.sub.x Si.sub.1.sub.-y N.sub.y alloy where M represents certain elements substituting for Co and x has a value ranging up to 0.6, where N represents certain elements substituting for Si and y has a value ranging up to 0.2, unidirectionally cooling said melt through a thermal gradient at a velocity which produces a solid having elongated columnar macro-grains aligned substantially parallel to each other, and unidirectionally cooling said macro-grain solid through said thermal gradient at said velocity which on reaching transformation temperature directionally transforms said solid into an aligned solid composite consisting essentially of at least two phases, the ratio of said thermal gradient to said velocity being greater than 150.degree.C/cm.sup.2 /hr. The phases are in the form of substantially uniform alternating lamellae parallel to each other and have an average interlamellar spacing less than 3 microns. The composite is substantially or completely free of dendrites.
REFERENCES:
patent: 3694193 (1972-09-01), Carpay et al.
Andrews M. J.
Binkowski Jane M.
Cohen Joseph T.
General Electric Company
Squillaro Jerome C.
LandOfFree
High-temperature eutectoid alloy and process of making does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High-temperature eutectoid alloy and process of making, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High-temperature eutectoid alloy and process of making will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1694049