ABSTRACT:
High-Tc superconducting ceramic oxide products and macroscopic and microscopic methods for making such high-Tc superconducting products. Completely sealed high-Tc superconducting ceramic oxide provides are made by a macroscopic process including the steps of pressing a superconducting ceramic oxide powder into a hollow body of a material inert to oxygen; heat treating the superconducting ceramic oxide powder packed body under conditions sufficient to sinter the ceramic oxide powder; and then sealing any openings of the body. Optionally, a waveform or multiple pulses of alternate magnetic filed can be applied during the heat treatment. The microscopic method of producing a high-Tc superconducting ceramic oxide product includes the steps of making a high-Tc superconducting ceramic oxide thin film; optionally sintering the deposited thin film in a magnetic filed; and removing partial oxygen content of the thin film by a scanning tunneling electron treatment machine to form a microscopic insulation layer between two high-Tc superconducting domains of the thin film.
REFERENCES:
patent: 3158794 (1964-11-01), Swartz
patent: 4924091 (1990-05-01), Hansma et al.
patent: 4952554 (1990-08-01), Jin et al.
patent: 4960752 (1990-10-01), Ashok et al.
patent: 4970197 (1990-11-01), Shiota et al.
patent: 5004722 (1991-04-01), Tallman
patent: 5047633 (1991-09-01), Finlani et al.
patent: 5051397 (1991-09-01), Sato et al.
patent: 5073209 (1991-12-01), Giancola
patent: 5075286 (1991-12-01), Powell et al.
patent: 5096882 (1992-03-01), Kato et al.
patent: 5098878 (1992-03-01), Hirschmann et al.
patent: 5116810 (1992-05-01), Joshi et al.
patent: 5166919 (1992-11-01), Eigler
patent: 5204315 (1993-04-01), Ito et al.
patent: 5219832 (1993-06-01), Zhou
patent: 5232906 (1993-08-01), Yamamoto et al.
patent: 5244876 (1993-09-01), Preisler et al.
patent: 5304534 (1994-04-01), Ciszek
patent: 5304602 (1994-04-01), Yamamoto et al.
patent: 5380702 (1995-01-01), Henty
patent: 5756427 (1998-05-01), Zhou
patent: 02 82286 (1988-09-01), None
patent: 03 05820 (1989-03-01), None
patent: 04 28244 (1991-05-01), None
patent: 52 17438 (1993-08-01), None
patent: WO 88 09312 (1988-12-01), None
patent: WO 92 22931 (1992-12-01), None
Babic, E. et al (1994) “Magnetoresistance and V-I curves of Ag-sheathed (Bi, Pb)2Sr2Ca2Cu3O10+ytape” Physical Review B 49(21):15312-15316.
Calestani, G. et al (1993) “Effects of simultaneous Pb/Bi and Y/Ca substitution on structural and superconducting properties of B12-xPbxSr2Y0.2Ca2O2” Physica C 206:33-42.
Calestani, G et al (1993) “Effects of simultaneous Pb/Bi and Y/Ca substitution on structural and superconducting properties of the 2212 BSCCO phase” Journal of Alloys and Compounds 195:315-322.
Chandra, B., T.K. Dey (1993) “Heat conducting in vanadium substituted (Bi0.8Pb0.2-yVv)2Sr2Ca2Cu3Ox sintered pellets between to and 150 K” Cryogenics 33(10):980-985.
Che, G.C. et al (1989) “Composition and superconductivity in Bi-Sr-Ca-Cu-O and substituted systems” J.Master. Sc. 24:125-1728.
Chen, F. et al (1991) “Biaxially aligned high Tcsuperconductors” Appl. Phys. Lett. 58(5):531-533.
Charambach, A. (1991) “Electrophoresis” Encyclopedia of Physics, 2ndEdition, pp. 324-325.
Chu, C.T., B. Dunn (1989) “Fabrication of Yba2Cu3O7-ysuperconducting coatings by electrophoretic deposition” Appl. Phys. Lett. 55(5):492-494.
Dou, S.X. et al. (1992) “Improvement of flux pinning in the Ag-clad Bi-Pb-Sr-Ca-Cu-O wires through the use of a short period mely processing” Appl. Phys. Let. 60(23):2929-2931.
Ehmann, A. et al. (1993) “Bi cuprates of type 1212-new family of superconductors in the Bi series” Journal of Alloys and Compounds 195:57-60.
Fung, P.C.W. et al. (1990) “Vanadium substituted 2212 and 2223 superconducting ceramics” Solid State Communications 75(3):211-216.
Haldar, P. et al. (1995) Oral Presentation at DOE HTS Wire Development Workshop, St. Petersburd, Florida, Jan. 31-Feb. 1, 1995.
Hein, M. et al. (1989) “Electrophoretic disposition of textured Yba2CU3O7-x films on silver substrates” J. Apply. Phys. 66(12):5940-5943.
Ho, J.C. et al. (1991) Melt-textured thick films of Bi1.7Pb0.3Sr2CaCu2OySuperconductor Science and Technology 4:507-508.
Kao, C.H. et al. (1994) “A Study of Bi-Pb-Sr-Ca-Cu-O/Ag tape prepared by the jelly-roll process” Supercond. Sci. Technol. 7:470-472.
Kao, C.H. et al (1993) “Fabrication of Bi1.7Pb0.4Sr1.6Ca3.6Oysuperconducting films on silver substrates by electrophoretic desposition technique” Journal of Materials Science Letters 12:1793-1794.
Leghissa, M. et al (1993) “Observation of a disordered vortex state in Bi2Sr2CaCu2O8=xsingle crystals containing columnar defects” Physical Review B 48(2):1341-1344.
Liu, H.K. et al. (1991) “Fabrication of Ag-Sheathed Bi-Superconducting Tapes and Coils.” J. Mater. Res. 6:2287-2290.
Liu, R.S. et al. (1990) “Superconductivity up to 105K in the new High-TcTI-V-Sr-Ca-Cu-O and TI-V-Sr-Ca-Y-Cu-O Systems” Solid State Communications 76(11): 1261-1265.
Maley, M.P. et al (1990) “Oral Presentation at DOE HTSC Wire Development Workshop”, Jan., Florida.
Nojima, H. et al. (1990) “Fabrication of Y-Ba-Cu-O Superconducting Films on Cu Substrates by an Electrophoretic Desposition Technique” Japanese Journal of Applied Physics 29(9):1655-1658.
Pont, M. et al (1993) “Effects of Cr and V substitution on the properties of bulk TI-based superconductors” Cryogenics 33(1):91-96.
Ren, Z.F., J.H. Wang (1993) “Superior flux pinning inin situsynthesized silver-sheathed superconducting tape OF Ti0.5Pb0.5Sr1.6Ca0.8Y0.2Cu2Oy” Appl. Phys. Lett. 62(23):3025-3027.
Rose-Innes, A.C., E.H. Rhoderick (1978) “The Mixed State” Introduction to Superconductivity, vol. 6, pp. 183-197.
Sarkar, P. et al. (1991) “Fabrication of textured Bi-Sr-Ca-Cu-O thick film by electrophoretic deposition” J. Apply. Phys. 69(3):1775-1777.
Sengupta, S. et al (1993) “Effective Activation Energy in the Bi-Sr-Ca-Cu-O Systems” IEEE Transactions of Applied Superconductivity 3(1):1226-1228.
Shaked, H. et al Physica C—Crystal Structures of High-Tc Superconducting Copper-Oxides, pp. 1-71.
Sheahen, T.P. (1994) “Introduction to High-Temperature Superconductivity”.
Thompson, J.R. et al(1992) “Enhanced current density Jc and extended irreversibility in single-crystal Bi2Sr2Ca1Cu2O8via linear defects from heavy ion irradiation” Appl. Phys. Lett. 60(18):2306-2308.
Tilley, D.R., J. Tilley (1990) Superfluidity and Superconductivity, Third Edition, pp. 208-224.
Zhou, D., N.S. Sullivan (1989) “Collective Quantum Tunneling Model of High TcSuperconductors” Physica C162-164:813-814.
Woolf, L.D. et al (1991) “Fabrication of Long Length bi-2223 Superconductor Tape Using A Continuous Electrophoretic Coating Process” Appl. Phys. Letter 58:534-536.
Xin, Y. et al (1990) “Optimum Fabrication Process and Some Relevant Analysis for the Vanadium-Lead Doubly Substituted 2223 Superconducting Ceramics” Solid State Communications 76(12):1347-1350.
Xue, J.S. et al. (1991) “Crystal Growth and characterization of superconducting lead cuprates” Journal of Crystal Growth 113:371-378.
Xin, Y. et al (1990) Vanadium-Lead Substituted 2223 Bi-Sr-Ca-Cu-O Superconductors Solid State Communications 76(12):1351-1356.
Kopec Mark
Saliwanchik Lloyd & Saliwanchik
LandOfFree
High-TC superconducting ceramic oxide products and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High-TC superconducting ceramic oxide products and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High-TC superconducting ceramic oxide products and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3443339