ABSTRACT:
A zirconia type sintered body consisting essentially of 50 to 98% by weight of zirconia (ZrO.sub.2) containing 1.5 to 5 mole % of yttria (Y.sub.2 O.sub.3) and 50 to 2% by weight of alumina (Al.sub.2 O.sub.3), spinal (MgAl.sub.2 O.sub.4) or mullite (3Al.sub.2 O.sub.3.2SiO.sub.2), and having a three-point bending strength of at least 1700 MPa is provided. This sintered body is prepared by a process wherein a powdery composition consisting essentially of 50 to 98% by weight of (a1) a powder of zirconia containing 1.5 to 5 mole % of yttria or (a2) a mixture comprising 1.5 to 5 mole % of yttria powder and 95 to 98.5 mole % of a zirconia powder and 2 to 50% by weight of (b) a powder of an alumina type oxide selected from alumina, and alumina-magnesia type oxide, an alumina-silica type oxide, a mixture of alumina and magnesia and a mixture of alumina and silica is subjected to a hot isotactic pressing treatment under a pressure of at least 50 MPa at temperature of 1300.degree. C. to 1700.degree. C. or a monoaxially compression-sintering treatment under a pressure of at least 20 MPa at a temperature of 1400.degree. C. to 1700.degree. C.
REFERENCES:
patent: 4108652 (1978-08-01), Ogawa et al.
patent: 4221650 (1980-09-01), Friese et al.
patent: 4314827 (1982-02-01), Leitheiser et al.
patent: 4316964 (1982-02-01), Lange
patent: 4336339 (1982-06-01), Okumiya
patent: 4383957 (1983-05-01), Yamakawa
patent: 4461843 (1984-07-01), McGarvy et al.
patent: 4506024 (1985-03-01), Claussen et al.
patent: 4518397 (1985-05-01), Leitheiser et al.
patent: 4518398 (1985-05-01), Tanaka et al.
patent: 4543341 (1985-09-01), Barringer et al.
Lange, Transformation Toughening, In Journal of Materials Science, 17(1982) 247-254.
Tsukidate Takaaki
Tsukuma Koji
Ueda Kuniyoshi
Derrington James
Toyo Soda Manufacturing Co. Ltd.
LandOfFree
High-strength zirconia type sintered body and process for prepar does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High-strength zirconia type sintered body and process for prepar, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High-strength zirconia type sintered body and process for prepar will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2396981