High strength polyethylene naphthalate fiber

Details High strength polyethylene naphthalate fiber High strength polyethylene naphthalate fiber

2001-10-04

2003-01-28

Edwards, Newton (Department: 1774)

Stock material or miscellaneous articles

Coated or structually defined flake, particle, cell, strand,...

Rod, strand, filament or fiber

C428S395000, C152S451000

Reexamination Certificate

active

06511747

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to a high strength polyethylene naphthalate fiber useful for the reinforcement of rubber products such as tires.
BACKGROUND OF THE INVENTION
A polyethylene-2,6-naphthalate has a higher glass transition temperature, crystallization temperature, melting temperature and melting viscosity, as compared to a comparable polyethylene terephthalate, and thus, it is generally spun at a temperature higher than the spinning temperature (310 to 320° C.) of a conventional polyethylene terephthalate. However,at a high spinning temperature, heat decomposition takes place to some extent, resulting in a reduction of the intrinsic viscosity, which makes it difficult to prepare a polyethylene-2,6-naphthalate yarn having the original high strength (see Japanese Patent Publication Nos. 72-35318, 73-64222 and 75-16739).
Japanese Patent No. 2945130 describes a method of making polyethylene naphthalate fibers having high tenacity and high modulus by way of controlling the spinning speed and spinning draft ratio and changing the drawing temperature stepwise, instead of raising the spinning temperature. According to this method, however, uniform spinning cannot be accomplished and the drawing process itself is difficult to control because of a high first-step drawing temperature of more than 150° C.
The present inventors have endeavored to develop an improved polyethylene-2,6-naphthalate fiber and have discovered that a high strength fiber can be prepared by way of controlling the properties of polyethylene-2,6-naphthalate polymer itself and the drawing conditions while maintaining a relatively low spinning temperature.
SUMMARY OF THE INVENTION
It is, therefore, an object of the present invention to provide a high strength polyethylene naphthalate fiber having high tenacity and improved dimensional stability, suitable for use as a reinforcing cord.
In accordance with one aspect of the present invention, there is provided a polyethylene naphthalate fiber prepared by a method comprising the steps of:
(A) melt-spinning a solid-phase polymerized polyethylene-2,6-naphthalate chip, composed of 95 mol % or more of ethylene-2,6-naphthalate units as the recurring unit, and having a manganese content of 30 to 70 ppm, an antimony content of 180 to 300 ppm and an intrinsic viscosity of 0.90 to 1.00, through a spinneret at a spinning draft ratio ranging from 400 to 900 to form a molten spun yarn,
(B) rapid-cooling and solidifying the spun yarn by passing it through a solidification zone,
(C) withdrawing the solidified yarn at such a rate that an undrawn yarn having a birefringence of 0.005 to 0.025 is formed, and
(D) subjecting the undrawn yarn to a multi-stage-drawing process to a total draw ratio of 6.5 or more to obtain a fiber, wherein the temperature of the second drawing stage is maintained in the range of 150 to 180° C.; said fiber having (1) an intrinsic viscosity of 0.70 to 0.77, (2) a tenacity of at least 9.5 g/d, (3) an elongation of at least 9.5%, (4) a birefringence of at least 0.45, (5) a density of 1.355 to 1.368, (6) a melting point of 270 to 275° C., and (7) a shrinkage of 2 to 3%.


REFERENCES:
patent: 4101525 (1978-07-01), Davis et al.
patent: 5397527 (1995-03-01), Rim et al.
patent: 5637385 (1997-06-01), Mizuki et al.
patent: 5750644 (1998-05-01), Duh
patent: 5955196 (1999-09-01), Sakellerides
patent: 6351933 (2002-03-01), Reuter

Affiliated with

Also associated with

Rating

High strength polyethylene naphthalate fiber does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with High strength polyethylene naphthalate fiber, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High strength polyethylene naphthalate fiber will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3006776