High strength plastic film and process for its production

Details High strength plastic film and process for its production High strength plastic film and process for its production

2000-05-25

2002-03-19

Nutter, Nathan M. (Department: 1711)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

Mixing of two or more solid polymers; mixing of solid...

C525S221000, C525S222000, C525S227000, C525S229000, C525S240000

Reexamination Certificate

active

06359074

ABSTRACT:

The invention relates to a plastic film comprising mainly of polyethylene, which has been stretched in order to increase its strength, and which also contains an acetate polymer, such as vinyl acetate. A process for the production of such a plastic film is also described.
Polyethylene is commonly used in the production of plastic films. The film is usually produced from polyethylene granules by the blown film extrusion process. It is already known that the weldability of this blown polyethylene film can be improved by admixing a suitable amount of acetate granules to the polyethylene granules in the film blowing process. The resulting films are easy to weld, in comparison to a blown polyethylene film.
Polyethylene films produced by the film blowing process exhibit to some degree inadequate strength. To improve the strength of such films, they are stretched. Such stretched films have, of course, the drawback that they can no longer be welded, even if additives that promote the weldability, such as acetate granules, are added to the film. For this reason no additives, for example no acetate granules, up to the present invention, have been included in the film when high strength plastic films are stretched in an additional working step after or during the blown film extrusion process. The strength of the plastic film is a function of how much the film can be stretched. Of course, there are natural limits to the stretchability of polyethylene films.
This invention seeks to provide a film based on polyethylene that exhibits maximum strength.
This invention provides a polyethylene film which is stretched in order to increase its strength, and which includes an effective amount of an acetate polymer.
Preferably, the polyethylene film includes up 10% by weight of acetate polymer. More preferably, the polyethylene film contains from about 2% to about 5% by weight of acetate polymers.
It was found surprisingly that plastic films made of polyethylene, to which an effective amount of acetate polymer is added, exhibit an improved stretchability. The invention is based on the knowledge that the addition of acetate polymer significantly reduces the formation of crystalline structures in the polyethylene film, so that the polyethylene film has an amorphous structure. The resulting films are easier to stretch during processing. When the films of this invention are stretched, it is found that the limit of stretchability of the film is improved to the point that it is possible to obtain plastic films having higher strength.
The distinction between these films and conventional plastic films to which acetate is added lies in the fact that they are substantially unweldable after stretching. In accordance with the invention, the addition of acetate granules has nothing to do at all with the improvement of the welding properties of the film, but rather only with the improvement of the stretchability of the film. The fact that the incorporation of an acetate polymer, typically vinyl acetate, could be used to improve film stretchability, and thus film strength, was unknown prior to this invention.
In accordance with the preferred embodiments, the polyethylene film contains up to 10% by wt. acetate polymer, preferably 2-5% by wt. acetate polymer.
A preferred process for producing a high strength plastic film includes the following steps:
(a) mixing polyethylene granules with acetate polymer granules, in the desired ratio;
(b) producing a film from the mixed granules using the blown film extrusion process; and.
(c) stretching the resulting film.
It can thus be seen that the improved films of this invention are produced by more or less conventional blown film preparation techniques.


REFERENCES:
patent: 3975463 (1976-08-01), Hirata et al.
patent: 4537935 (1985-08-01), Yoshimura et al.
patent: 4814124 (1989-03-01), Aoyama et al.
patent: 4945127 (1990-07-01), Kagawa et al.

Affiliated with

Also associated with

Rating

High strength plastic film and process for its production does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with High strength plastic film and process for its production, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High strength plastic film and process for its production will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2826387