High stack factor amorphous metal ribbon and transformer cores

Stock material or miscellaneous articles – All metal or with adjacent metals – Composite; i.e. – plural – adjacent – spatially distinct metal...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C164S463000, C336S234000, C428S606000, C428S687000, C428S900000, C428S928000, C428S937000

Reexamination Certificate

active

06299989

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a high stack factor amorphous metal transformer core, and to a process for constructing a high stack factor amorphous metal transformer core. The process uses high lamination factor amorphous metal ribbon (the term lamination factor is generally used to express the smoothness and uniformity of the ribbon, whereas the term stack factor is applied to cores made from ribbon); that is, amorphous metal ribbon with a highly smooth surface and a highly uniform thickness as measured across the ribbon width. High stack factor amorphous metal ribbon can be efficiently packed, by winding or stacking operations, into compact transformer core shapes. The transformer core can then be clamped, to further reduce overall dimensions, and annealed, to relieve residual mechanical stresses and to generate a desired magnetic anisotropy, without detriment to the final magnetic properties.
High stack factor amorphous metal transformer cores will have smaller core build dimensions, yet will maintain the same core net area, when compared to conventional amorphous metal transformer cores. The smaller core build will result in a smaller amorphous metal transformer core, which, in turn, allows for a reduction in size or quantity of other transformer components. For example, a high stack factor amorphous metal transformer will contain smaller coil windings, will be housed in a smaller tank, and, if used in liquid filled transformers, will be filled with less oil. These factors all contribute to a reduced amorphous metal transformer cost.
2. Description of the Prior Art
Amorphous metal transformer cores can be manufactured by winding a single amorphous metal ribbon, or by winding a package consisting of multiple layers of amorphous metal ribbons, into the shape of an annulus. The annulus is then cut along a radial line, creating a single joint. The annulus can be opened at the joint to accommodate placement of the primary and secondary coils, and then closed to recreate the original annulus shape.
Another approach to manufacturing amorphous metal transformer cores is to cut a single amorphous ribbon, or to cut a package consisting of multiple layers of amorphous ribbons, to predetermined lengths. The cut amorphous metal ribbons are then wrapped around a mandrel, or are stacked and wrapped around a mandrel, to create a tightly wound core form. The individual lengths of the amorphous metal ribbon are wrapped about the mandrel such that the cut ends form a distributed series of joints aligned in a localized region of the core. The core can then be opened, by separating the distributed joints, to accommodate placement of the primary and secondary coils, and then closed to recreate the original wrapped core shape.
U.S. Pat. Nos. 4,734,975, 5,261,152 and 5,329,270 disclose amorphous metal transformer cores constructed from groups of amorphous metal ribbon, cut to predetermined length, and wrapped around a mandrel to form a distributed joint core. These patents are incorporated herein by reference for their teachings as to how to produce amorphous metal transformer cores.
Cores manufactured in these manners, with conventional amorphous metal ribbon, are limited to stacking factors of about 86% or less. Accordingly, cores built with these limitations are much larger than conventional silicon steel transformers, use more amorphous metal, more conductor (copper or aluminum) for the primary and secondary coils, more steel for the tank, and, if used in liquid filled transformers, more oil to fill the tank. These factors all contribute to increased materials usage in transformer manufacturing and increased transformer cost. Manufacturing cost penalties range from 20 to 50% (or more).
In addition, the increased size of the transformer is undesirable in many locations and applications where space is limited. The cost and size penalties limit the number of applications, and hence the market size, for amorphous metal transformers.
INVENTION
Amorphous metal ribbon has been produced on a commercial scale with lamination factors, as determined by ASTM A 900-91, between about 0.80 and 0.86. This ribbon has been produced by a single roller, single nozzle slot process, as described in U.S. Pat. No. 4,142,571. U.S. Pat. Nos. 4,865,644 and 5,301,742 teach that space factors (lamination factors) of between about 0.85 and 0.95 can be achieved in amorphous alloy ribbon through the use of a nozzle with multiple slots located in close proximity to each other, but that conventionally processed amorphous alloy ribbons are limited to lamination factors of between about 0.75 and 0.85.
Amorphous metal ribbon of the current invention is cast by a single roller, single slot process, but unexpectedly exhibits lamination factor greater than 0.86. (The term lamination factor is generally used to express the smoothness and uniformity of the ribbon, whereas the term stack factor is applied to cores made from ribbon.) Indeed, lamination factors as high as 92% have been attained. This is achieved by creating highly smooth ribbon surfaces and a highly uniform thickness as measured across the ribbon width.
Highly uniform thickness across the ribbon width is maintained by careful control of the nozzle slot geometry. Ribbon center to ribbon edge thickness uniformity is maintained by ensuring that the nozzle slot remains substantially rectangular. Nozzle material, design and fixturing were chosen in order to control thermomechanical distortion so that the slot width varied by no more than about 5% along its length. Although it is desirable to have a nozzle that is inherently dimensionally stable, clamping the nozzle in such a way as to minimize distortion was found to provide additional control of slot dimensions.
In order to maintain highly uniform ribbon edge to ribbon edge thickness, it is also necessary to control the separation between the nozzle and the wheel so that it varies no more than about 5% from one end of the slot to the other. The present invention utilized a means of adjusting the nozzle position relative to the wheel based on edge to edge measurements of cast ribbon so as to minimize edge to edge thickness variation.
Maintaining highly smooth ribbon surfaces requires that the nozzle surface and wheel surface be smooth. Smooth nozzle surfaces were achieved by machining the nozzle slot surfaces in contact with molten metal during the casting process to achieve a surface roughness surface roughness, Ra, of less than about 5 micrometers. To ensure that a smooth nozzle surface was maintained during the casting process, a protective atmosphere of inert or reducing gas was utilized so as to minimize reactions between the nozzle and the molten metal which can degrade the original surface finish. In addition, the use of the protective atmosphere minimizes the accumulation of slag particles on the nozzle which increase the roughness of the cast ribbon. A smooth casting wheel surface was maintained by the continuous application of an abrasive material with a very fine abrasive particle size, less than about 60 micrometers in mean particle size.
The high lamination factor ribbon permits the construction of high stack factor transformer cores of the present invention. Transformer cores having the high lamination factor amorphous metal ribbon can be made using conventional core building techniques known to those skilled in the art. Cores made with the high lamination factor ribbon can then be clamped, to further reduce overall dimensions, and annealed, to relieve residual mechanical stresses and to generate a desired magnetic anisotropy, without detriment to the final magnetic properties. Transformer cores of the current invention with stack factors of 86% or greater can be designed and produced.


REFERENCES:
patent: 4142571 (1979-03-01), Narasimhan
patent: 4734975 (1988-04-01), Ballard et al.
patent: 4865644 (1989-09-01), Charles
patent: 5261152 (1993-11-01), Simozaki et al.
patent: 5301742 (1994-04-01), Sato et al.
patent: 5329270 (1994-07-01), Freeman
patent: 5

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

High stack factor amorphous metal ribbon and transformer cores does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with High stack factor amorphous metal ribbon and transformer cores, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High stack factor amorphous metal ribbon and transformer cores will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2554921

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.