Abrading – Abrading process – Glass or stone abrading
Reexamination Certificate
2000-01-27
2002-02-26
Hail, III, Joseph J. (Department: 3723)
Abrading
Abrading process
Glass or stone abrading
C451S037000, C451S057000
Reexamination Certificate
active
06350176
ABSTRACT:
ORIGIN OF THE INVENTION
The invention described herein was made by employees of the United States Government. The invention may be manufactured and used by or for the governmental purposes without the payment of royalties thereon or therefor.
FIELD OF THE INVENTION
The present invention relates to polishing an optic surface and more particularly to polishing an optic surface on an aluminum monolith.
BACKGROUND OF THE INVENTION
Metallic mirrors have been widely used for instruments in space and military applications. System performance of the instruments is largely dependent upon the reflective surface of the mirror. Performance of the optical mount, and its thermal and mechanical characteristics also have effects on the performance of the optical component. In actuality the optical mount has a significant impact on performance of the optical system in achieving objectives of any scientific and engineering experiment. When both optical mount and mirror substrate are of the same material there is uniformity of thermal properties. Also the high thermal conductivity of a metal mirror helps decrease cooling time in cryogenic applications.
Many spacecraft systems utilize aluminum materials for structural components in cases of cold or cryogenic use. Aluminum materials may also be used for mirrors as aluminum offers numerous benefits because of its machinability, lightweight, and low cost.
Due to light scattering which results from poorly polished surfaces, however, bare aluminum cannot be readily implemented as an acceptable mirror material for UV, IR and visible applications. The scattering lowers the signal-to-noice ratio and throughput.
Existing technology attempts to remedy this dilema by electroplating a thin layer of electroless nickel to the entire component surface and then optically polishing the plated nickel. The result creates a tradeoff whereby surface roughness is decreased while thermal and mechanical stability of the optic are severely compromised at all but room temperatures. This is especially true for aluminum optics that have been light-weighted. Further complicating matters is the fact that the mount is usually an integrally machined part of an aluminum optic. While these characteristics are great for dimensional requirements and ease of design, they create havoc on the optical performance once all surfaces are evenly plated with nickel. The electroless nickel platings also can cause bi-metalic stresses to deteriorate optical performance. Another problem of plating aluminum with electroless nickel is that manufacturing costs grow because nickel polishes more slowly than conventional optical materials.
One prior technique has overcome such problems yet provides inferior optical performace to one proposed by the present invention. For example, see “Diamonds turn infrared mirrors smooth”, by Daniel Vukobratovich, et al, Optoelectronics World, page S25-S28, October 1998. The prior technique plates an aluminum substrate with an amorphous layer of high-purity aluminum. Then the plated substrate is diamond-turned to produce a mirror with surface roughness of 30 angstroms rms with surface accuracy in terms of surface figure error of 0.380 wave peak-to-valley. This plated substrate is theoretically bimetallic and should experience the bimetallic deformation to some degree. By comparison the present invention provides an aluminum mirror of about 5 angstroms rms surface roughness with surface accuracy in terms of surface figure error as low as one-fifteenth of a wave peak-to-valley without any bimetallic deformations.
In addition to superior optical performance, this invention provides the following advantages by eliminating the electroless nickel plating from the aluminum mirrors:
(1) Drastic cost savings during fabrication.
(2) Reduced risk associated with polishing through nickel to the aluminum. This requires that the part be stripped of the remaining nickel and re-plated. To do so, the optical surface must again be prepared for plating because the stripping procedure etches the aluminum.
(3) Drastic performance improvements. Properly heat-treated bare aluminum performs well in cryogenic conditions without the nickel plating.
(4) Reduced cost of final component characterizations. Plated mirrors that show abnormalities are often tested and retested to determine the impact on the system performance. If the problem is identified to be with the nickel plating as is often the case, then the process must be completely repeated by stripping the mirror and starting over.
Properly implemented, therefore, the proposed innovation will eliminate many of the associated problems now common with current aluminum mirror technology, delivering aluminum optics with superior accuracy.
Accordingly, it is an object of this invention to provide a high quality optically polished aluminum mirror.
It is another object of this invention is to provide a process for producing the high quality optically polished surface on an aluminum monolith.
SUMMARY OF THE INVENTION
This invention presents a high quality optically polished aluminum mirror and a novel method of optically polishing aluminum monolith in a conventional polishing manner by employing modern techniques with a combination of compatible ingredients. In other words, this invention combines diamond turning and conventional polishing along with newly adopted materials for the polishing to accomplish a significant improvement in surface precision of bare aluminum for optical purposes.
This present invention provides an aluminum mirror of less than about 30 angstroms rms and preferably about 5 angstroms rms surface roughness with surface accuracy in terms of surface figure error as low as one-fifteenth of a wave peak-to-valley. The inventors used commercial grade aluminum, for example, 6061T6 aluminum, to produce the aluminum mirror presented by this invention. Inventors believe that further polishing of the aluminum mirror mentioned above with the polishing process proposed by this invention can produce an aluminum mirror of higher quality.
The polishing process proposed by this invention can be applied to other optically feasible substrates including glass, nickel, stainless steel, and many other glasses or metal materials.
Step one of this innovative polishing method is pre-polishing to produce a pre-polished surface having a surface roughness of not more than about 100 angstroms rms with a surface accuracy in terms of surface figure error of not more than about one-half of a wave peak-to-valley.
The pre-polishing of the surface of the metallic monolith may be effected by diamond turning. The process of diamond turning is a precision method of producing accurate mirrored surfaces of optical quality (for some wavelengths) on bare aluminum and other materials. It is successful because the turning or cutting action of the sharp diamond tool serves to peel thin layers of aluminum from the surfaces at such small portions as to produce a polished finish whereby other machining processes actually tear the material away from the substrate. The amount of material removed on the typical final cut is 0.0001 inch. The diamond turning process allows surface figure errors of approximately 0.5 of a wave peak-to-valley over components up to four inches in diameter and surface roughness of generally 100 angstroms. The precision degrades slightly as the size of the component grows beyond four inches.
Following the pre-polishing process, the polishing method proceeds with fabrication of a polisher. To fabricate the polisher, select grade of pitch used exclusively for optical fabrication is melted and poured onto a cast iron lap. The pitch is allowed to cool, and then shaped and grooved according to the optician's discretion. Once fabricated, the polisher is installed on a machine spindle, which is a part of a polishing tool assembly. The polishing process continues with applying an appropriate amount of a polishing agent to the surface of the polisher and placing the optical monolith onto the polisher. A pivot pin is then lowered into a pre-drilled sm
Lyons, III James J.
Zaniewski John J.
Hail III Joseph J.
Ojini Anthony
Park Chan K.
The United States of America as represented by the Administrator
LandOfFree
High quality optically polished aluminum mirror and process... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High quality optically polished aluminum mirror and process..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High quality optically polished aluminum mirror and process... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2938884