Electric lamp and discharge devices – With gas or vapor – Having electrode lead-in or electrode support sealed to...
Reexamination Certificate
1999-06-22
2003-07-08
Patel, Vip (Department: 2879)
Electric lamp and discharge devices
With gas or vapor
Having electrode lead-in or electrode support sealed to...
C313S631000, C313S633000, C313S634000, C313S332000
Reexamination Certificate
active
06590340
ABSTRACT:
BACKGROUND OF THE INVENTION
The invention relates to a high-pressure gas discharge lamp comprising:
a lamp vessel which is closed in a vacuumtight manner and has a quartz glass wall enclosing a discharge space;
metal foils embedded in the wall of the lamp vessel and each connected to a respective external current conductor;
tungsten electrode rods each connected to a respective one of said metal foils and projecting from the wall of the lamp vessel into the discharge space;
an ionizable filling in the discharge space;
the lamp being defined by the following relation
f
inw
>=40%
in which:
f
inw
=fraction of length of the electrode rod enclosed in the wall of the lamp vessel.
A high-pressure gas discharge lamp of this type is known from U.S. Pat. No. 5,462,277. The known lamp is suitable for use as a vehicle headlamp and has electrode rods of a thickness of 250 &mgr;m which may or may not have an envelope at their free ends and may be made of, for example, thoriated tungsten.
Stringent requirements are imposed on the speed with which the lamp, after it has been ignited, provides a large fraction of the luminous flux during stable operation. It is also necessary that the lamp can be ignited while it is still hot due to a previous operating period. The lamp is ignited at a voltage of several kV and a frequency of several kHz in order to comply with these requirements.
In the manufacture of the known lamp, a seal is made in which one or several of said metal foils are enclosed in the wall. During this operation, the quartz glass is softened at the area where this seal is to be created in the presence of the metal foil, the external current conductor and the electrode rod. Subsequently, the lamp, or the lamp-to-be, cools down. Due to its relatively high coefficient of linear thermal expansion (approximately 45*10
−7
K
−1
), the electrode rod then contracts more strongly than the quartz glass in which it is embedded. Quartz glass is a glass having an SiO
2
content of at least 98% by weight, the coefficient of expansion of the glass is approximately 6*10
−7
K
−1
. For a good adhesion between the rod and the quartz glass, obtained by an additive to the electrode rod tungsten, such as thorium oxide, a coating of quartz glass around the rod is obtained, which is mechanically unconnected with the quartz glass of the wall. If the electrode rod and the quartz glass adhere insufficiently to each other, a capillary space is created due to shrinkage around this rod. No such capillary space is created around the metal foil, often a molybdenum foil, because of the foil shape.
In the known lamp, there is often a good adhesion between the rod and the quartz glass and thus there is a coating of quartz glass around the rod. The quartz glass coating of the electrode rods in the known lamp enhances their thermal capacity (the energy which is necessary for the same rise of temperature) and also increases their thermal conductance (the quantity of heat which can be depleted per unit of time). On the other hand, their electrical conductivity is not affected. The higher thermal capacity retards the rise of temperature of the rods during ignition of the lamp, so that the permanent contact with the embedded metal foil enables the surrounding quartz glass of the wall to assume a higher temperature and to expand, also because of the heat developed in this foil due to the passage of current.
It has been found that the coatings of species of one type of lamp may have alternating lengths. This may be due to small variations of temperature of the quartz glass when the seal is being made. It is a drawback that the absence of a coating or an insufficient coating results in rejects during the lamp production and that the known lamp has only a short lifetime when there is no or not enough quartz glass coating and when this lamp is often switched on and switched off after a short operating period.
When such a lamp without coating is ignited, the temperature of the electrode rods rises steeply owing to the high current flowing through them and owing to heat transfer from the discharge. The quartz glass does not instantaneously follow this temperature rise. Owing to their higher temperature and their higher coefficient of expansion, the rods will come into contact with the quartz glass and exert pressure on it. It was found that damage, such as microcracks, then occurred in the quartz glass, which microcracks generally increase in number and size during subsequent ignition periods. This leads to a (premature) end of the lifetime of the lamp owing to leakage, causing constituents of the filling to escape so that the lamp no longer ignites, or the lamp vessel is broken.
Lamps complying with the relation f
inw
>=40% have a greater risk of occurrence of the above-mentioned detrimental phenomena, unless special circumstances are created, for example, a quartz glass coating around the electrode rod.
Another drawback is that the coating leads to unwanted and troublesome reflections of the light generated in the discharge.
SUMMARY OF THE INVENTION
It is an object of the invention to provide a high-pressure gas discharge lamp having a simple construction and counteracting said drawbacks.
According to the invention, the electrode rods have first parts projecting into the discharge space, which first parts are at least substantially made of tungsten, and second parts enclosed at least partly in the wall, which second parts are made of elements chosen from the group of tungsten having a thickness ranging between 120 &mgr;m and 180 &mgr;m, molybdenum having a thickness ranging between 120 &mgr;m and 350 &mgr;m and tungsten-molybdenum alloys having a thickness ranging between 120 &mgr;m and 350 &mgr;m, said first and second parts contacting and being connected to each other via facing ends.
Since the electrodes are composed of a first and a second part, it is possible to adapt the electrodes to the circumstances. The first part is made in conformity with the end of the electrode of the known lamp projecting into the discharge space, so that, during its lifetime, it can withstand the heat developed by the high starting currents and the discharge. The second part is designed in such a way that the problem of leakage or breakage of the lamp owing to expansion and, consequently, exertion of pressure on the quartz glass by the second part of the electrode rod during (re)ignition of the lamp at least substantially does not occur anymore.
It has been found that in lamps complying with the relation f
inw
>=40%, the occurring problems of leakage at least substantially do not occur in electrode rods having relatively small thicknesses of the second parts enclosed in the wall. In lamps having electrode rods with second parts of tungsten having a thickness of 180 &mgr;m, it was found that leakage of the lamp only occurred sporadically. At thicknesses of less than 180 &mgr;m, the absolute value of the expansion, and hence the pressure exerted by the electrode rods on the quartz glass, is so small that any further damage, such as microcracks, no longer occurs.
In lamps having electrode rods with second parts of both tungsten-molybdenum alloys and molybdenum having a thickness of 350 &mgr;m, it was found that leakage of the lamp only occurred sporadically. The risk of leakage or breakage of the lamp is considerably reduced if the thickness of these second parts is chosen to be smaller than 350 &mgr;m. The successful use of relatively large thicknesses with second parts of molybdenum or tungsten-molybdenum alloys is based on the ductility of these materials. When exerting pressure on the quartz glass, due to expansion by the electrodes, this pressure will be more evenly distributed due to deformation of the relatively ductile material than when using electrodes which are made of, for example, the much less ductile tungsten.
However, for second parts made of both tungsten, tungsten-molybdenum alloys and molybdenum having thicknesses of less than 120 &mgr;m, the electrodes only hav
Eijsermans Joseph F. R.
Jörres Angela
Seebode Dorothea
Dicran Halajian
Koninklijke Philips Electronics , N.V.
Patel Vip
Quarterman Kevin
LandOfFree
High pressure discharge lamp with tungsten electrode rods... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High pressure discharge lamp with tungsten electrode rods..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High pressure discharge lamp with tungsten electrode rods... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3074950