High peel strength rubber/textile composites

Fabric (woven – knitted – or nonwoven textile or cloth – etc.) – Coated or impregnated woven – knit – or nonwoven fabric which... – Coated or impregnated natural fiber fabric

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C442S168000, C442S169000, C442S164000, C442S171000, C442S173000, C442S176000, C442S179000, C442S180000

Reexamination Certificate

active

06686301

ABSTRACT:

FIELD OF THE INVENTION
This invention relates to adhesion promotion compositions which provide excellent adhesive characteristics between rubber and textile substrates. Such compositions comprise specific mixtures of aminosilanes and other organosilanes or specific compounds having both an aminosilane moiety and a group having an affinity for rubber compositions. These inventive compositions may be utilized to activate a textile surface for further contact with a rubber alone or a resorcinol-formaldehyde latex (RFL) or similar type of adhesive compound to which a rubber may subsequently be adhered. The methods utilizing these particular adhesion promotion compositions are also contemplated within this invention.
DISCUSSION OF THE PRIOR ART
It has long been known that adhering a textile, particularly one composed of filaments having high tenacity to a rubber enhances the modulus and tensile strength of the rubber component and provides long-lasting durability, particularly in high friction applications. Examples of such applications include fan and timing belts within automobile engines; vehicle tires; conveyor belts; and the like. The main requirement of such textile-reinforced rubber articles has been the strength of adhesion between the textile and the rubber. Without any primer treatment, the textile will not effectively adhere to the rubber. A weak bond between the two components results in separation of the two layers and mechanical failure of the resulting composite. Thus, it has been and is necessary to provide a textile treatment to enhance the adhesion of these two distinct components.
Previous methods of providing such adherence between rubber and textile layers include coating or impregnating the textile layer with a formaldehyde latex (such as a resorcinol-formaldehyde vinyl-pyridine rubber latex or RFL), pre-coating with an RFL latex and an amino functional polyacrylate, as in U.S. Pat. No. 5,654,099, to Pelton, and in European Patent Application 665,390, to Tsubakimoto Chain Company, or utilizing a pre-activated textile which has reactive pendant groups to facilitate adhesion between the fabric surface and the reactive sites on the rubber layer, all of the aforementioned references being herein entirely incorporated by reference. The RFL coating method results in a composition which does not always provide sufficient adhesion between layers. Pre-activated textiles, such as a polyester fibers coated with an epoxy adhesion enhancer, are typically used in combination with an RFL treatment to further improve the textile adhesion to rubbers. Although such pre-activated textiles perform well in many cases, there remains a need for less expensive methods and compositions for adhesion promotion between rubber and textile layers in order ultimately to produce a reinforced, long-lasting, and durable rubber product.
Also worth mentioning are U.S. Pat. No. 5,064,876, to Hamada et al., and U.S. Pat. No. 5,082,738, to Swofford, both of which teach a primer composition for promoting adhesion for polymer films. Such disclosed compositions comprise aminofunctional silanes. However, neither of these references teach the application of textiles to rubber formulations for reinforcement purposes nor do they teach or fairly suggest the necessary combination of an amine functional group and another organo-functional group, in particular a reactive group having an affinity for rubber, as is now required within the inventive composition and method.
DESCRIPTION OF THE INVENTION
It is thus an object of the invention to provide improved adhesion for a long-lasting and durable textile-reinforced rubber product. A further object of the invention is to provide a relatively inexpensive method of achieved such improved adhesion. Another object of the invention is to provide an adhesion promoter which ultimately provides a textile-reinforced rubber product which does not exhibit adhesive failure. Yet another object of this invention is to provide a stable aqueous primer composition that, when applied before an RFL treatment, activates the textile substrate in order to provide greatly improved adhesion to various rubber compounds.
Accordingly, this invention concerns a composition for promoting the adhesion between a rubber composition layer and a textile reinforcing layer comprising
a mixture of at least two different silane compounds, at least one compound selected from (I) and at least one compound selected from (II); wherein (I) and (II) include the following:
(I) aminosilanes selected from the group consisting of
 wherein R is C
1
-C
6
alkyl, R
2
is an amine functional group, and R′ is an alkyl- or aromatic-acyl group;
(II) organo-functional silanes selected from the group consisting of
 wherein R
2
is a group containing a radical selected from the group consisting of a mercapto moiety, a sulfide moiety, an isocyanate moiety, an epoxy moiety, a pyridine moiety, a hydrophobic saturated alkyl moiety, and a moiety having at least one unsaturated carbon-carbon bond, and R and R′ are defined as for (I) above. Nowhere within the prior art has such a specific adhesion promotor composition been disclosed or practiced, particularly for activating textile substrates in order to improve adhesion to rubbers. Furthermore, nor has such a specific composition or method of utilizing such a composition been taught or fairly suggested. Such compositions and methods provide significant advantages over the standard adhesion compositions and methods of the state of the art.
Also, it has been discovered that a stable aqueous dispersion of the composition (a) above can be obtained without the use of any dispersing agents or surfactants. Component (II) of the inventive composition is not water soluble (some of the covered compounds can even react with water and thus are not stable in aqueous solution). Although a water dispersion of the component (II) can be produced utilizing surfactants, such dispersions have very limited shelf life. Besides, the surfactants necessary to make such dispersions tend to affect adhesion adversely since surfactants are known to migrate to the interfaces and interfere with the microscopic intimate contact between two uniting materials. However, by mixing components (I) and (II) together, then slowly adding water to the mixture, a stable aqueous dispersion/solution can be obtained without utilizing any potentially deleterious surfactants or dispersing agents.
The relative cost of the inventive compositions is very low at the preferred level of usage, particularly when compared with the pre-activated textiles mentioned above. All of these characteristics and improvements with the inventive compositions and methods thus translate into lower costs for the user. Additionally, the inventive compositions and methods can be utilized with any rubber compositions and with any type of smooth filament textile normally utilized as a rubber reinforcement material. Examples of rubber compositions include, and are not limited to, natural rubber, polyurethane rubber, styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR), butyl rubbers, fluorinated rubbers, and ethylene-propylene-diene rubber (EPDM). Modified rubbers which are potentially useful, though more expensive, include hydrogenated SBR, hydrogenated NBR, and carboxylated NBR. Suitable textiles include, and are not limited to, those comprising polyester, polyester/cotton blends, polyamides, such as nylon-6 or -6,6, polyaramids (such as Kevlar®, available from DuPont), polypropylene, boron derivatives, glass fibers, and carbon fibers. The textile component may be dyed or colored various shades and hues in order to facilitate categorizing the different widths, lengths, etc., of products such as, without limitation, timing belts, and the like, for automobiles. Finally, the inventive compositions and methods, when utilized and/or practiced as intended, result in a textile-reinforced rubber product which does not exhibit textile/rubber adhesive failure.
Preferably, the inventive composition comprises (I) an am

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

High peel strength rubber/textile composites does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with High peel strength rubber/textile composites, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High peel strength rubber/textile composites will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3311090

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.