Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – At least one aryl ring which is part of a fused or bridged...
Reexamination Certificate
2001-12-03
2003-04-15
Sanders, Kriellion A. (Department: 1714)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
At least one aryl ring which is part of a fused or bridged...
C525S420000, C525S432000
Reexamination Certificate
active
06548591
ABSTRACT:
The invention relates to a polyamide composition with improved flow behaviour that comprises at least 80-99.5 wt. % high-molecular polyamide and 0.5-20 wt. % low-molecular polyamide, the amounts being relative to the total weight of the polyamide present in the composition.
Such a composition is known from JP-A-5214246 (Toray, 1992), which describes a composition that comprises 100 parts by weight polyamide-6 and 0.001-10 parts by weight of a polyamide oligomer based on stearic acid, methylenediamine and sebacic acid, having a M
w
of at most 5,000 and comprising modified end groups.
Said composition presents the drawback that the mechanical properties are not, or to an insufficient extent, retained after the addition of the polyamide oligomer according to JP-A-5214246. Another drawback is that modifying the polyamide end groups is a laborious procedure and implies an additional process step in the preparation of the oligomer. Another drawback is that the polyamide oligomer is not commercially available, as a result of which the invention has had no commercial or large-scale implementation up to now.
Obtaining a high-molecular polyamide composition with good flow behaviour and with the typical polyamide properties being retained is of great importance for the purpose of obtaining films, fibres or moulded parts, in particular thin-walled moulded parts, that are obtained with the aid of the injection-moulding process. High-molecular polyamides generally have a high melt viscosity and poor flow behaviour. High-molecular polyamides do however have very good mechanical properties, in particular a high impact resistance, stiffness, deformation resistance and dimensional stability on heating, elongation at break and modulus of elasticity. For the purpose of improving the mechanical properties even further, in particular the stiffness or impact resistance the polyamide is often mixed with inorganic fillers such as glass fibres or impact modifiers. However, this leads to even further deterioration of the flow behaviour, so that it becomes difficult to injection-mould large or thin-walled moulded parts that also have an optically perfect surface, using for example glass-fibre-filled polyamide compositions.
An improvement in the flow behaviour is generally obtained by adding flow-promoting agents. Examples of flow-promoting agents mentioned in the literature are branched fluid crystalline oligoesters or oligoesteramides (EP-A-444295), low-molecular polyester (DE-A-4127720), polyolefinic waxes, modified with polar side chains (BE-A-820472) or salts of magnesium, zinc and aluminium (WO 97/19131).
The inventors have now surprisingly found that the drawbacks of the state of the art can be avoided and a high-molecular polyamide composition with good flow behaviour and with good mechanical properties can be obtained if this composition contains at least 0.5-20 wt. % low-molecular polyamide (a polyamide oligomer) having a melting point that is higher than the melting point of the high-molecular polyamide, the amount being relative to the polyamide's total weight. The high-molecular polyamide has a different chemical composition than the polyamide oligomer in the composition according to the invention.
From WO 98/24836 is known a process for the production of a polyamide moulded part with improved crystallisation behaviour from a polyamide composition containing 0.01-5 wt. % polyamide-4,6 and 99.99-95 wt. % of a polyamide having a melting point that is lower than that of polyamide-4,6. A composition containing a low-molecular polyamide 4,6 is not described, neither is the advantage of any associated improved flow behaviour acknowledged.
Suitable polyamides, both with a high-molecular weight and with a low-molecular weight (oligomers), are all the polyamides known to a person skilled in the art, comprising crystalline, semi-crystalline and amorphous polyamides. Examples of suitable polyamides according to the invention are aliphatic polyamides, for example PA-6, PA-11, PA-12, PA-4,6, PA-4,8, PA-4,10, PA-4,12, PA-6,6, PA-6,9, PA-6,10, PA-6,12, PA-10,10, PA-12,12, PA-6/6,6-copolyamide, PA-6/12-copolyamide, PA-6/11-copolyamide, PA-6,6/11-copolyamide, PA-6,6/12-copolyamide, PA-6/6,10-copolyamide, PA-6,6/6,10-copolyamide, PA-4,6/6-copolyamide, PA-6/6,6/6,10-terpolyamide, and copolyamides obtained from 1,4-cyclohexanedicarboxylic acid and 2,2,4- and 2,4,4-trimethylhexamethylenediamine, aromatic polyamides, for example PA-6,I, PA-6,I/6,6-copolyamide, PA-6,T/6-copolyamide, PA-6,T/6-copolyamide, PA-6,I/6,T-copolyamide, copolyamides obtained from terephthalic acid, 2,2,4- and 2,4,4-tri-methylhexamethylenediamine, copolyamide obtained from isophthalic acid, laurinlactam and 3,5-dimethyl-4,4-diamino-dicyclohexylmethane, copolyamides obtained from isophthalic acid, azelaic acid and/or sebacic acid and 4,4-diaminodicyclohexylmethane, copolyamides obtained from caprolactam, isophthalic acid and/or terephthalic acid and 4,4-diaminodicyclohexylmethane, copolyamides obtained from caprolactam, isophthalic acid and/or terephthalic acid and isophoronodiamine, copolyamides obtained from isophthalic acid and/or terephthalic acid and/or other aromatic or aliphatic dicarboxylic acids, optionally alkyl-substituted hexamethylenediamine and alkyl-substituted 4,4-diaminodicyclohexylamine, or copolyamides or mixtures of the aforementioned polyamides.
Preferably polyamides are chosen from the group comprising PA-6, PA-6,6, PA-6,10, PA-4,6, PA-11, PA-12, PA-12,12, PA-6,I, PA-6,T/6,6-copolyamide, PA-6,T/6-copolyamide, PA-6/6,6-copolyamide, PA-4,6/6-copolyamide or mixtures or copolyamides of the aforementioned polyamides. More preferably PA-6, PA-6,6 or PA-4,6 is chosen, or mixtures or copolyamides thereof.
The polyamides in the composition according to the invention may optionally contain modified end groups, for example amine end groups modified with carboxylic acid.
The high-molecular polyamide has a weight-average molecular weight of at least 10,000 g/mol, preferably at least 15,000 g/mol, more preferably at least 20,000 g/mol.
The low-molecular polyamide has a weight-average molecular weight that is preferably lower than the “molecular weight between entanglements” of the high-molecular polymer. This “molecular weight between entanglements” is for example 5,000 g/mol in the case of PA-6. Preferably the weight average molecular weight is at most 5,000 g/mol, preferably at most 4,000 g/mol, more preferably at most 3,000 g/mol. The molecular weight may not be too low either, to avoid the risk of for example the glass transition temperature being lowered. Preferably the weight-average molecular weight is greater than approximately 1,000 g/mol.
Preferably, the composition comprises a high-molecular weight polyamide with a molecular weight of at least 10,000 g/mol and a low-molecular oligomer with a molecular weight of at most 5,000 g/mol.
More preferably, the composition comprises a high-molecular weight polyamide with a molecular weight of at least 15,000 g/mol and a low-molecular oligomer with a molecular weight of at most 4,000 g/mol.
The composition according to the invention comprises 0.5-20 wt. % oligomer, relative to the total amount of polyamide. The amount of oligomer can be chosen by a person skilled in the art within the given range, depending on the desired properties of the composition. Larger amounts of the oligomer result in a better flow behaviour, but too large amounts adversely affect the mechanical properties. Preferably an amount of 1-10 wt. % is chosen, relative to the total amount of polyamide.
The composition according to the invention preferably comprises a high-molecular polyamide, chosen from the group comprising PA-6, PA-6,6, PA-6,10, PA-4,6, PA-11, PA-12, PA-12,12, PA-6,I, PA-6,T/6,6-copolyamide, PA-6,T/6-copolyamide, PA-6/6,6-copolyamide, PA-4,6/6-copolyamide or copolyamides or mixtures thereof and a polyamide oligomer chosen from the group comprising PA-6,6, PA-4,6, PA-4,6/6-copolymer or copolyamides or mixtures thereof.
In the context of this application “PA-4,6” is understood to be a polyamid
Crevecoeur Jeroen J.
De Koning Gerardus J. M.
Koning Cornelis E.
DSM N.V.
Pillsbury & Winthrop LLP
Sanders Kriellion A.
LandOfFree
High-molecular polyamide composition with improved flow... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High-molecular polyamide composition with improved flow..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High-molecular polyamide composition with improved flow... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3020333