Compositions – Inorganic luminescent compositions – Zinc or cadmium containing
Reexamination Certificate
2002-09-05
2004-01-27
Koslow, C. Melissa (Department: 1755)
Compositions
Inorganic luminescent compositions
Zinc or cadmium containing
Reexamination Certificate
active
06682664
ABSTRACT:
TECHNICAL FIELD
This invention relates to zinc sulfide-based electroluminescent phosphors. More specifically, it relates to orange-yellow-emitting zinc sulfide-based electroluminescent phosphors co-activated with manganese and copper.
BACKGROUND OF THE INVENTION
Orange-yellow-emitting zinc sulfide electroluminescent phosphors co-activated with manganese and copper ions (ZnS:Mn,Cu) are well known. Examples of these phosphors and their methods of manufacture are described in U.S. Pat. Nos. 4,859,361 and 5,009,808. These phosphors are significantly lower in brightness than other ZnS-based phosphors. For example, the brightness of commercially available Zn:Mn,Cu phosphors is under 10 foot-Lamberts (ft-L) whereas the brightness of commercial blue-green emitting ZnS:Cu,Cl electroluminescent phosphors is greater than 30 ft-L.
U.S. Pat. No. 5,702,643 and JP 4-270780 describe improving the half-life of copper-activated zinc sulfide (ZnS:Cu) phosphors by incorporating small amounts of gold into the phosphor. U.S. Pat. No. 6,395,196 describes increasing the half-life of a ZnS:Cu electroluminescent phosphor by heating the finished phosphor in a closed vessel in the presence of antimony vapor. However, these techniques are insufficient to achieve the brightness levels needed to meet current market requirements. In particular, higher brightness orange-yellow-emitting electroluminescent phosphors are needed for forming white-emitting phosphor blends which could be used in electroluminescent lamps for backlighting color LCD displays. Therefore, it is desirable to improve the brightness of orange-yellow-emitting zinc sulfide electroluminescent phosphors.
SUMMARY OF THE INVENTION
It is an object of the invention to obviate the disadvantages of the prior art.
It is another object of the invention to provide a high brightness orange-yellow-emitting electroluminescent phosphor.
It is a further object of the invention to provide a method of making a high-brightness orange-yellow-emitting electroluminescent phosphor.
In one aspect of the invention, an orange-yellow-emitting zinc sulfide-based electroluminescent phosphor is provided which has a brightness greater than 10 foot-Lamberts and an x color coordinate from about 0.51 to about 0.56 and a y color coordinate from about 0.42 to about 0.48.
In another aspect of the invention, the orange-yellow-emitting electroluminescent phosphor comprises zinc sulfide activated with copper, manganese, chlorine, and a metal selected from gold and antimony, wherein the phosphor contains about 0.5 to about 1.3 weight percent manganese, about 0.02 to about 0.08 weight percent copper, about 0.002 to about 0.02 weight percent chlorine, 0 to about 0.012 weight percent gold, and 0 to about 0.0007 weight percent antimony.
In yet another aspect of the invention, a method of making an orange-yellow-emitting electroluminescent phosphor is provided wherein the method comprises:
(a) forming a mixture of an amount of zinc sulfide, an amount of a copper source, an amount of a manganese source, an amount of zinc oxide, an amount of sulfur, an amount of a chloride-containing flux, and an amount of a source of a metal selected from a gold and antimony;
(b) firing the mixture at a temperature from about 1100° C. to about 1250° C. for about 3 hours to about 5 hours;
(c) mechanically working the fired material to introduce defects in the crystal structure;
(d) washing the fired mixture to remove the chloride-containing flux and copper sulfide residues;
(e) combining the fired material with an amount of a copper source, an amount of a manganese source, and an amount of zinc oxide to form a second mixture;
(f) firing the second mixture at a temperature from about 750° C. to about 950° C. for about 2 hours to about 5 hours and fast cooling the fired second mixture; and
(g) washing the second mixture to remove residual copper sulfide.
DETAILED DESCRIPTION OF THE INVENTION
For a better understanding of the present invention, together with other and further objects, advantages and capabilities thereof, reference is made to the following disclosure and appended claims.
A high-brightness orange-yellow-emitting electroluminescent phosphor has been invented. The phosphor comprises zinc sulfide activated with copper, manganese, chlorine, and a metal selected from gold and antimony. The phosphor exhibits a brightness of greater than 10 foot-Lamberts (ft-L), and preferably at least about 13 ft-L, when stimulated in a conventional thick-film electroluminescent lamp. The orange-yellow emission has an x color coordinate from about 0.51 to about 0.56 and a y color coordinate from about 0.42 to about 0.48.
The phosphor preferably contains from about 0.5 to about 1.3 weight percent manganese, about 0.02 to about 0.08 weight percent copper, about 0.002 to about 0.02 weight percent chlorine, 0 to about 0.012 weight percent gold, and 0 to about 0.0007 weight percent antimony. A more preferred range for the gold content of the phosphor is from about 0.002 to about 0.012 weight percent gold and a more preferred range for the antimony content is from greater than 0 to about 0.0007 weight percent antimony. It should be noted that the amount of antimony retained in the finished phosphor may be very difficult to detect. In these cases, it is assumed that because antimony was added during the first firing step some antimony is retained even though it could not be detected in the chemical analysis.
The high-brightness phosphor of this invention is made in two firing steps. In the first firing step, zinc sulfide (ZnS) is blended with appropriate amounts of a source of copper (Cu), zinc oxide (ZnO), sulfur (S), a chloride-containing flux, and a source of a metal selected from gold and antimony. Preferably, the Au source is a pre-mixture of gold chloride (AuCl
3
) and ZnS, the Cu source is anhydrous copper sulfate (CuSO
4
), and the Sb source is a pre-mixture of antimony oxide (Sb
2
O
3
) and ZnS. The chloride-containing flux can be a mixture of alkali metal and alkaline earth chlorides, preferably barium chloride (BaCl
2
), magnesium chloride (MgCl
2
), and sodium chloride (NaCl). The blended mixture preferably contains in weight percent (wt. %) relative to the weight of ZnS: 0 to 0.018 wt. % Au, 0.02 to 0.08 wt. % Cu, 0 to 0.01 wt. % Sb, 0.3 to 0.7 wt. % ZnO, 6 to 12 wt. % sulfur, and 4 to 14 wt. % chloride flux (preferably 0-4 wt. % of barium chloride, 1-5 wt. % of magnesium chloride, and 1-5 wt. % of sodium chloride). More preferably, the blended mixture contains 0.008 to 0.18 wt. % Au. Even more preferably, the blended mixture contains 0.001 to 0.01 wt. % Sb.
The blended mixture is fired in air at a temperature from about 1100° C. to about 1250° C. for about 3 to about 5 hours. A fast cooling after the first firing is preferred but is not critical. The fast cooling is achieved by placing the red hot crucible into a water bath. Water is kept running to maintain the water bath at <60° C. The fired material is then water washed, dried, and gently mulled (low-intensity milling) to induce defects in its crystal structure. The mulling time depends on the particular type of equipment used and the amount of material being mulled. An optimum mulling time can be readily determined by one skilled in the art of electroluminescent phosphors. In our case, a typical mulling time was 75 minutes for 500 to 550 g of material.
After mulling, the material is washed with acid and then a basic solution containing sodium hydroxide (NaOH), hydrogen peroxide (H
2
O
2
), and a chelating agent, such as diethylenetriaminepentaacetic acid (DTPA). In a preferred method, the basic solution contains relative to the phosphor weight: 2-4 wt. % DTPA, 2.5-3.5 wt. % NaOH, and 5-15 wt. % of a 30% H
2
O
2
solution. This chemical wash further removes flux residues and copper sulfides from the phosphor surface. A KCN solution may be used in place of the basic solution to remove the copper sulfide residue. The material is then washed with hot deionized water and then dried to complete the first firing step.
In the second firing step, the material
Belinski-Wolfe Judy A.
Chen Xianzhong
Fan Chen Wen
Huang Fuqiang
Maxwell Michael A.
Clark Robert F.
Koslow C. Melissa
Osram Sylvania Inc.
LandOfFree
High brightness orange-yellow-emitting electroluminescent... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with High brightness orange-yellow-emitting electroluminescent..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High brightness orange-yellow-emitting electroluminescent... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3253351