ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of Invention
The invention relates to a heatable mirror having a specifically designed heat-conducting layer made from conductive particles, a process for applying heat-conducting layers to substrates and the use of this process for producing heatable mirrors.
2. Description of the Related Art
Heatable mirrors having a heat-conducting layer made from conductive material are known. Hence a heatable mirror is described in U.S. Pat. No. 3,686,437 in which a heat-conducting layer has been applied to a glass substrate under vacuum or by sputtering. This United States patent proposes the use of a nickel-chromium alloy as the heat-conducting layer.
The disadvantage of this mirror is that firstly, the technologies for applying the heat-conducting layer are very complex. As described in the United States patent, application of the nickel-chromium alloy should be carried out either under vacuum or using a sputtering process. Both process steps are too complex and too expensive for mass production. Furthermore, it has been shown that a mirror of this type obviously also does not have adequate heat capacity due to the only very thin layers. This leads to the time span for keeping a mirror free of condensation being too long. Also it is not possible using mirrors of this type to heat certain areas specifically more strongly than others, which is required [is] in many cases because of the construction of the mirror.
SUMMARY OF THE INVENTION
The object of the present invention is therefore to propose a heatable mirror, the heat-conducting layer of which permits high heat capacity and any design of layout for the heat-conducting layer. The object of the invention is also to provide a cost-effective and simple process for mass production by means of which a heat-conducting layer may be applied to a substrate.
[The object is achieved with regard to the heatable mirror by the features of patent claim 1 and with regard to the process by the features of patent claim 17. The sub-claims show advantageous further developments of the solution according to the invention.]
It is thus proposed according to the invention that the heat-conducting layer is formed by conductive particles at least partially embedded in the surface of the substrate and/or the reflective layer. It is thus essential for the heatable mirror of the invention that the particles have an average diameter of 3 to 100 &mgr;m.
FIGS. 4-6
show scanning electron-microscope images in 30, 100 and 1,000 time magnification, from which particle formation can be seen. Accordingly, the heat-conducting layer has a “rough surface:.
FIG. 6
in particular shows that the particles have obviously only been changed insignificantly by the application process.
FIGS. 4
to
6
also show that the particles have partially penetrated into the surface of the substrate, here a mirror. Adhesion of the particles to the substrate is thus essentially produced by the penetration of particles into the surface of the substrate. Of course partial sintering of the particles with one another and with the surface also takes place. It is important for the heatable mirror having the heat-conducting layer as described above, that a certain roughness, that is an average particle diameter or 3 to 100 &mgr;m is maintained, and that a thus cohering conductive layer is produceD. The heat-conducting layer of the mirror of the invention thus differs from those which are known hitherto from the state of the art, which have been applied conventionally via sputtering processes or evaporation methods. In all these cases a very finely divided homogeneous conducting layer is thus produced which has the disadvantages of the state of the art outlined in the introduction.
The particles themselves are preferably selected from the metals Al, Zn, Sn, Cu, Ni and/or alloys thereof. It is most particularly preferred for the heatable mirror of the invention if the particles consist of aluminum and/or an aluminum alloy having at least 96% aluminum. A further preferred embodiment of the mirror of the invention is characterized in that the substrate for the heatable mirror is glass. The material pairing glass and aluminum and/or aluminum alloy in particular as particles has proved to be particularly superior in its properties with regard to the mechanical adhesion and electrical heat capacity.
For the mirror of the invention, the heat-conducting layer may be designed to be both over the entire surface or strip-like. For the embodiment in which a strip-like heat-conducting layer is present, it is thus important that the regions between the heat-conducting strips consist of an insulating separating layer. This insulating separating layer is preferably a thin film having a width of 0.2 mm to 1 mm. The minimum width is important because otherwise bridging may occur during spraying. The separating layer is produced from a formulation containing resins and solvents. Preferred resins are thus shellac, gum arabic or colophony. The insulating separating layer may thus also contain further additives, as known per se from the state of the art. This separating layer is applied; in the required form by spreading-on, spraying or brushing.
It has also proved to be advantageous if the layer thickness of the heat-conducting layer lies in the range from 10 &mgr;m to 100 &mgr;m, preferably in the range from 40 to 60 &mgr;m. A particular advantage of the heatable mirror of the invention is that the layer thickness of the heat-conducting layer may be selected to be different, so that increased heat capacity is then obtained at particularly critical points in the mirror area, so that condensation is also prevented there. For the case that strip-like heat-conducting layers are used, the strip widths of the heat-conducting layer are 2-20 mm. Also the strip width of the heat-conducting layer may be selected to correspond to the width so that a wider strip width is selected at particularly critical points at which dehumidification of the mirror is only possible with difficulty. Of course the invention also includes all embodiments in which both the layer thickness of the layer and also the strip width is varied.
The heat-conducting layer of the heatable mirror of the invention also shows considerable improvement compared to the state of the art apart from the advantages described above. It has also been shown to the expert in a manner which could not be foreseen, namely that the heat-conducting layer [as defined in patent claim 1] may be provided with a polymer coating which serves as chip protection, for thermal and electrical insulation as well as also as adhesive for fixing the mirror frame.
It was hitherto namely conventional in the state of the art to apply chip protection which was present in the form of adhesive films or foils and which had to be produced in a separate working step and then adhered to the mirror. In the mirror of the invention it is now possible to apply a polymer coating very simply, for example by spraying, particularly because of the surface formed by the particles. It has thus proved to be particularly advantageous if as the polymer coating such a one is selected which consists of a self-curing silane-modified polymer. This now produces the advantage that the mirror is coated over the entire surface with the polymer on the side on which the heat-conducting layer is applied in a single working step, and that simple curing in air then takes place. Silane-modified alkyd resin systems are preferably used as polymers of this type. They are characterized particularly in that they are single-component systems and cross-link in air moisture to give a flexible product. A further advantage of such a coating is that this coating acts as a steam barrier and is UV stable and functions as a sealing material with very good workability.
In the heatable mirror of the invention provision is made, as already known from the state of the art, in that contract points are present for contacting with a voltage source. These contact points are thus pre
Macher David
Stark Johann
Zorn Heinz
Clark Hill PLC
Fuqua Shawntina
Magna Auteca Zweigniederlassung
LandOfFree
Heatable mirror, method for producing a heat conductive... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Heatable mirror, method for producing a heat conductive..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Heatable mirror, method for producing a heat conductive... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3204876