Metal treatment – Process of modifying or maintaining internal physical... – Heating or cooling of solid metal
Reexamination Certificate
2000-05-05
2002-03-12
Yee, Deborah (Department: 1742)
Metal treatment
Process of modifying or maintaining internal physical...
Heating or cooling of solid metal
C148S644000, C148S654000, C148S662000, C148S661000, C148S902000, C148S320000
Reexamination Certificate
active
06355119
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to a heat treatment method for producing boundary layer-hardened long products and flat products of unalloyed or low-alloy steels, comprising the following steps: a first cooling process for the workpiece for producing a martensitic grain (microstructure) in the boundary layer of the workpiece as well as a second cooling process for the workpiece with a cooling rate below the lower critical cooling rate for cooling the workpiece core. In this context, the lower critical cooling rate is that cooling rate which is just great enough to form 1% martensite, i.e., the workpiece core is cooled so slowly that a ferritic-pearlitic grain is formed and not a martensitic grain.
2. Description of the Related Art
In a known method for producing boundary layer-hardened and self-annealing long products (wire, bar stock, profiled semi-finished and finished products etc.), a hardened microstructure is produced in the boundary layer of the workpiece, usually coming from the austenite temperature, in a suitable cooling device by a single quenching process (in general, by water cooling) causing the temperature to drop below the martensite starting temperature Ms. Subsequently, after stopping the cooling process, self-annealing takes place as a result of the residual heat in the interior of the long product. This method is usually employed directly after the workpiece leaves the rolling heat. However, in principle, it can also be used after an auxiliary heat treatment performed after rolling (for example, normalizing). The steels used in this method are, in general, low-alloy construction steals with a carbon content between 0.03 and 0.25%, a manganese content of 0.3 to 1.6%, and different amounts of other alloy components. For example, the quenching of reinforcement steels for steel construction in a cooling device is known. After producing a predetermined depth of converted martensitic grain (microstructure) in the boundary layer of the long product, a self-annealing step follows because of the residual heat in the interior of the workpiece. Depending on the material analysis and the depth of the hardened boundary layer, this treatment results in a certain combination of strength and tenacity properties (ductility).
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a heat treatment for producing boundary layer-hardened long products and flat products which, in comparison to the workpieces produced according to the known method, have improved tenacity properties while their strength properties are maintained.
In accordance with the present invention, this is achieved in that the first cooling process is performed in several repeating steps, wherein each process step is comprised of cooling to a temperature below the martensite starting temperature for martensitic conversion of only a portion of the workpiece boundary layer and a subsequent temporal stress-relief phase for the already formed martensitic grain areas and/or the martensite/austenite boundary areas.
According to the suggested method, the first cooling process for converting (transforming) austenite to martensite is performed in several repeating steps wherein each process step is comprised of a cooling phase for cooling to a temperature below the martensite starting temperature for the purpose of martensitic conversion of only a respective portion of the workpiece boundary layer and a subsequent temporal stress-relief phase of the already formed martensitic grain areas and/or the martensite/austenite boundary areas.
The individual steps are repeated several times until the grain (microstructure) within the desired or predetermined depth of the boundary layer is completely converted to martensite. The improved mechanical properties obtained by the heat treatment according to the method of the invention are the result of the course of the martensite formation that is modified in comparison to the known method. By dividing the cooling process into multiple process steps with pauses in between the individual process steps, a hardened microstructure is produced that has a reduced number of microfissures and thus has a higher deformability under mechanical load (cold forming), which is noticeable, inter alia, by increased breaking elongation values observed in tensile tests.
The basic principles for understanding the invention reside in the characteristic of the martensitic conversion. When an iron alloy is heated to temperatures above A
c3
(the temperature at which the conversion of ferrites into austenite ends in heating) and then quenched with a sufficiently high cooling rate, the austenite grain will convert to a martensite structure. The special feature of the martensite conversion, in comparison to the diffusion-controlled transformation mechanisms, is that it is athermal. This means that the continuation of the transformation to martensite is not realized by maintaining a certain temperature, but it takes place in a cascade-like manner only upon further cooling. In contrast to the diffusion-controlled transformation, an isothermal holding period does not result in an increase of the proportion of martensite in the total grain structure. The size of the growing martensite crystals is limited by the former austenite grain boundaries. The transformation of the martensite itself takes place in two steps according to a model which is presently widely accepted: a lattice-transforming deformation step from a face-centered cubic (f.c.c.) to a body-centered cubic (b.c.c.) lattice and a lattice-maintaining adaptation/adjustment of the freshly formed martensite. The transformation of the lattice from face-centered cubic (f.c.c.) to body-centered cubic (b.c.c.) and the adaptation of the freshly formed martensite result mandatorily also in a deformation of the austenite because the martensite transformation is, on the one hand, accompanied by a volume increase of approximately 3% and, on the other hand, two principally different lattice types, i.e., body-centered cubic and face-centered cubic, contact one another at the phase boundary (compare FIG.
8
). When in this context material separations at the martensite/austenite phase boundary, resulting from be unavoidable adjusting stress, are to be prevented, the austenite must be able to compensate the occurring deformations by gliding dislocation or twin accommodation. In this context, only the residual austenitic grain is concerned because the yield stress of the martensite is much greater than that of the austenite.
In general, this adaptation deformation does not occur without material separations so that technical steels, as has been proven, in the martensite phase have a greater or smaller number of microfissures after quenching. These microfissures by themselves reduce the tenacity as well as the ductility of the material because upon mechanical loading (for example, in tensile tests) these fissures are the seeds for further material separation and thus induce the general failure of the material. On the other hand, a reduction of the number of microfissures overall has a positive effect on the tenacity and the ductility of the material which, in turn, is exhibited by higher values for the breakage elongation in tensile tests.
With respect to the reduction of microfissures, the present invention suggests a heat treatment method in which the martensite transformation is not carried out by a single quenching process but is performed in a stepwise manner including short stress-relief phases between the individual transformation phases. For this purpose, the workpiece is only cooled for short periods of time to the martensite phase, and, subsequently, a temperature compensation takes place, followed by another quenching process to temperatures below the martensite starting temperature.
The compensation of the temperature is performed by self-annealing of the martensitic grain areas, formed by the corresponding cooling phase, to temperatures below A
1
as a result of the residual heat in the wor
Meyer Meinert
Peters Andreas
Kueffner Friedrich
SMS Schloemann--Siemag Aktiengesellschaft
Yee Deborah
LandOfFree
Heat treatment method for producing boundary-layer hardened... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Heat treatment method for producing boundary-layer hardened..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Heat treatment method for producing boundary-layer hardened... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2875273