Optical waveguides – Optical fiber waveguide with cladding – Utilizing multiple core or cladding
Reexamination Certificate
2001-11-19
2004-03-23
Bruce, David V. (Department: 2882)
Optical waveguides
Optical fiber waveguide with cladding
Utilizing multiple core or cladding
Reexamination Certificate
active
06711335
ABSTRACT:
TECHNICAL FIELD
The present invention relates to a heat-resistant coated optical fiber provided with a heat-resistant coating, which is employed in high-temperature/high-humidity environments.
BACKGROUND ART
As heat-resistant coated optical fibers usable in high-temperature environments, techniques disclosed in JP 1-173006A and JP 5-127052A have been known.
The former relates to a technique in which the outer periphery of an optical fiber is coated with a polyimide resin having a thickness of at least 25 &mgr;m but not greater than 300 &mgr;m, and states that its outer periphery is preferably further coated with a heat-resistant resin, such as a fluorine resin, equivalent to the polyimide resin. The latter is a technique in which the outer periphery of the optical fiber is coated with polyimide and polytitanocarbosilane. Both of them are described as capable of maintaining a high strength even under a high temperature by using polyimide, which is a heat-resistant resin, in their coating layers as such.
DISCLOSURE OF THE INVENTION
Examples of harsh environments where optical fibers are employed include high-temperature/high-humidity environments such as the inside of nuclear power plants, oil wells, and the like. It has been seen that, in the above-mentioned heat-resistant coated optical fibers, the heat-resistant coating resins and the optical fibers therein deteriorate in such high-temperature/high-humidity environments. This is because that, in a high-humidity environment with a humidity of 60%RH, for example, the imide group is hydrolyzed, whereby aromatic polyimide resins deteriorate. It has been seen that polyamic acid, which is a glass-decomposing gas generated upon this hydrolysis, deteriorates the optical fiber glass therein.
In order to overcome the above-mentioned problem, the heat-resistant coated optical fiber in accordance with the present invention comprises a first coating layer consisting of aromatic polyimide resin, covering an outer periphery of an optical fiber; a second coating layer consisting of silicone resin, covering an outer periphery of the first coating layer; and a third coating layer consisting of moisture-resistant resin, covering an outer periphery of the second coating layer and having a heat resistance equivalent to that of the first coating layer.
In accordance with the present invention, each of the first, second, and third coating layers has a heat resistance, so that the coating would not deteriorate even in high-temperature environments. Also, since the first coating layer, which may hydrolyze in a high-humidity environment, and the second coating layer are covered with the moisture-resistant third coating layer, steam is kept from penetrating into the first and second coating layers, whereby the deterioration in strength caused by hydrolysis can be suppressed. Further, the second coating layer can enhance the adherence between the first and third coating layers.
The thickness of the first coating layer is preferably at least 0.01 &mgr;m in order to protect the surface of optical fiber glass against the moisture in atmosphere, and is preferably not greater than 20 &mgr;m in order to improve productivity.
Also, the thickness of the second coating layer is preferably at least 5 &mgr;m in order to suppress the hydrolysis and secure a favorable lateral pressure characteristic, and is preferably not greater than 200 &mgr;m in order to suppress the deterioration in transmission characteristics caused by thermal shrinkage of the coating layer and the worsening of productivity.
Further, the thickness of the third coating layer is preferably at least 0.01 &mgr;m in order to secure heat resistance/moisture resistance characteristics, and is preferably not greater than 500 &mgr;m in order to suppress the deterioration in transmission characteristics caused by thermal shrinkage of the coating layer and the worsening of productivity.
The degree of cure of the first coating layer is preferably at least 0.30 in order to suppress the hydrolysis of polyimide.
From the viewpoint of heat resistance/moisture resistance characteristics and easiness in manufacture required for the third coating layer, it is preferably made of a fluorine resin.
A carbon coating may further be provided between the optical fiber and the first coating layer. In this configuration, glass-decomposing gases are kept from reaching the optical fiber even when the polyimide resin constituting the first coating layer is hydrolyzed.
REFERENCES:
patent: 4213672 (1980-07-01), Aulich et al.
patent: 4854668 (1989-08-01), Mayr et al.
patent: 4964694 (1990-10-01), Oohashi et al.
patent: 5182785 (1993-01-01), Savegh et al.
patent: 5333229 (1994-07-01), Sayegh
patent: 6233374 (2001-05-01), Ogle et al.
patent: 2003/0077059 (2003-04-01), Chien et al.
patent: 2003/0099451 (2003-05-01), Walker et al.
patent: 53-32749 (1978-03-01), None
patent: 1-173006 (1989-07-01), None
patent: 2-48437 (1990-02-01), None
patent: 2-232611 (1990-09-01), None
patent: 5-127052 (1993-05-01), None
“Polyetherimide (PEI)” The Loctite Design Guide for Bonding Plastics, vol. 2, Copyright approximatly 1997-2000, Table of Contents and pp. 44-45.*
Gardner “An investigation of the structure-property relationships for high performance thermoplastic matrix, carbon fiber composites with a tailored polyimide interphase” Dissertation, Aug. 17, 1998, pp. 35-38, 188-190, and 227-228.
Hattori Tomoyuki
Kubo Yuji
Shimizu Makoto
Tsuneishi Katsuyuki
Bruce David V.
McDermott & Will & Emery
Suchecki Krystyna
Sumitomo Electric Industries Ltd.
LandOfFree
Heat resistant optical fiber core does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Heat resistant optical fiber core, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Heat resistant optical fiber core will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3243807