Coating processes – Applying superposed diverse coating or coating a coated base – Metallic compound-containing coating
Reexamination Certificate
1998-05-29
2001-01-30
Turner, Archene (Department: 1775)
Coating processes
Applying superposed diverse coating or coating a coated base
Metallic compound-containing coating
C427S419200, C427S419700, C427S431000, C427S190000, C427S126100
Reexamination Certificate
active
06180182
ABSTRACT:
FIELD OF THE INVENTION
The invention relates to the application of refractory materials to carbon cathode blocks of cells for the electrowinning of aluminium by electrolysis of alumina dissolved in a cryolite-based molten electrolyte. The invention also relates to the cathode blocks and to such cells incorporating them.
BACKGROUND OF THE INVENTION
Aluminium is produced conventionally by the Hall-H{acute over (e)}roult process, by the electrolysis of alumina dissolved in cryolite-based molten electrolytes at temperatures up to around 950° C. A Hall-H{acute over (e)}roult reduction cell typically has a steel shell provided with an insulating lining of refractory material, which in turn has a lining of carbon which contacts the molten constituents. Conductor bars connected to the negative pole of a direct current source are embedded in the carbon cathode substrate forming the cell bottom floor. The cathode substrate is usually a carbon lining made of prebaked anthracite-graphite or all graphite carbon blocks, joined with a ramming mixture of anthracite, coke, and coal tar.
In Hall-H{acute over (e)}roult cells, a molten aluminium pool acts as the cathode. The carbon lining or cathode material has a useful life of three to eight years, or even less under adverse conditions. The deterioration of the cathode bottom is due to erosion and penetration of electrolyte and liquid aluminium as well as intercalation of sodium, which causes swelling and deformation of the cathode carbon blocks and ramming mix. In addition, the penetration of sodium species and other ingredients of cryolite or air leads to the formation of toxic compounds including cyanides.
Difficulties in operation also arise from the accumulation of undissolved alumina sludge on the surface of the carbon cathode beneath the aluminium pool which forms insulating regions on the cell bottom. Penetration of cryolite and aluminium through the carbon body and the deformation of the cathode carbon blocks also cause displacement of such cathode blocks. Due to cracks in the cathode blocks, aluminium reaches the steel cathode conductor bars causing corrosion thereof leading to deterioration of the electrical contact, non uniformity in current distribution and an excessive iron content in the aluminium metal produced.
A major drawback of carbon as cathode material is that it is not wetted by aluminium. This necessitates maintaining a deep pool of aluminium (100-250 mm thick) in order to ensure a certain protection of the carbon blocks and an effective contact over the cathode surface. But electromagnetic forces create waves in the molten aluminium and, to avoid short-circuiting with the anode, the anode-to-cathode distance (ACD) must be kept at a safe minimum value, usually 40 to 60 mm. For conventional cells, there is a minimum ACD below which the current efficiency drops drastically, due to short-circuiting between the aluminium pool and the anode or to oxidation of the aluminium produced. The electrical resistance of the electrolyte in the inter-electrode gap causes a voltage drop from 1.8 to 2.7 volts, which represents from 40 to 60 percent of the total voltage drop, and is the largest single component of the voltage drop in a given cell.
To reduce the ACD and associated voltage drop, extensive research has been carried out with Refractory Hard Metals or Refractory Hard Materials (RHM) such as TiB
2
as cathode materials. TiB
2
and other RHM's are practically insoluble in aluminium, have a low electrical resistance, and are wetted by aluminium. This should allow aluminium to be electrolytically deposited directly on an RHM cathode surface, and should avoid the necessity for a deep aluminium pool. Because titanium diboride and similar Refractory Hard Metals are wettable by aluminium, resistant to the corrosive environment of an aluminium production cell, and are good electrical conductors, numerous cell designs utilizing Refractory Hard Metal have been proposed, which would present many advantages, notably including the saving of energy by reducing the ACD.
The use of titanium diboride and other RHM current-conducting elements in electrolytic aluminium production cells is described in U.S. Pat. Nos. 2,915,442, 3,028,324, 3,215,615, 3,314,876, 3,330,756, 3,156,639, 3,274,093 and 3,400,061. Despite extensive efforts and the potential advantages of having surfaces of titanium diboride at the cell cathode bottom, such propositions have not been commercially adopted by the aluminium industry.
The non-acceptance of tiles and other methods of applying layers of TiB
2
and other RHM materials on the surface of aluminium production cells is due to their lack of stability in the operating conditions, in addition to their cost. The failure of these materials is associated with penetration of the electrolyte when not perfectly wetted by aluminium, and attack by aluminium because of impurities in the RHM structure. In RHM pieces such as tiles, oxygen impurities tend to segregate along grain boundaries leading to rapid attack by aluminium metal and/or by cryolite. To combat disintegration, it has been proposed to use highly pure TiB
2
powder to make materials containing less than 50 ppm oxygen. Such fabrication further increases the cost of the already-expensive materials. No cell utilizing TiB
2
tiles as cathode is known to have operated for long periods without loss of adhesion of the tiles, or their disintegration. Other reasons for failure of RHM tiles have been the lack of mechanical strength and resistance to thermal shock.
Various types of TiB
2
or RHM layers applied to carbon substrates have failed due to poor adherence and to differences in thermal expansion coefficients between the titanium diboride material and the carbon cathode block.
PCT patent application WO93/25731 describes a carbon-containing component of a cell for the production of aluminium by the electrolysis of alumina dissolved in a cryolite-based molten electrolyte, which cell component is protected from attack by liquid and/or gaseous components of the electrolyte or products produced during cell operation by a coating of particulate refractory hard metal boride and a colloid bonding applied from a slurry of the boride in a colloidal carrier which comprises at least one of colloidal alumina, silica, yttria, ceria, thoria, zirconia, magnesia, lithia, monoaluminium phosphate or cerium acetate.
The method of applying the refractory coating of WO93/25731 involved applying to the surface of the component a slurry of particulate refractory boride in the colloidal carrier, followed by drying and a heat treatment to consolidate the boride coating without any reaction taking place, this heat treatment preferably being in air or other oxidising atmospheres or alternatively in inert or reducing atmospheres. A heat treatment in air at about 80-200° C., for half an hour to several hours was found to be sufficient.
WO 95/13407 discloses manufacturing an aluminium electrowinning cell component having a refractory coating on a carbon body starting from a refractory coating precursor and a green carbon body that are baked together, to simultaneously produce the coating and bake the carbon body.
SUMMARY OF THE INVENTION
The invention aims to further improve the refractory coatings described in WO93/25731 as surface coatings on carbonaceous substrates, for protecting the substrates from the corrosive attacks of liquids and gases when used as cell components for aluminium production cells, especially for use as cathodes.
An object of the invention is to provide improved hard coatings containing borides that have exceptional adherence to the carbon-containing substrates, provide the required protection to the cell components and have improved mechanical, physical, chemical, and electrochemical characteristics.
Another object of the invention is to provide an improved method of applying refractory borides to carbon-containing cell components to form a hard coating wherein a part of the boride is reacted by heat treatment before use of the cell component to improve its protection.
A
De Nora Vittorio
Sekhar Jainagesh A.
Deshmukh Jayadeep R.
Moltech Invent S.A.
Turner Archene
LandOfFree
Hard and abrasion resistant surfaces protecting cathode... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Hard and abrasion resistant surfaces protecting cathode..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Hard and abrasion resistant surfaces protecting cathode... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2526459