ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to a tool for grinding and polishing diamond and a method for polishing diamond and/or the materials containing diamond without causing cracks and fractures therein. The diamond can be a polycrystalline diamond, a single crystal diamond, a sintered diamond compact, or a diamond thin film including a diamond thin film formed on a substrate by a gas phase synthetic method or a diamond self-standing film, foil or plate. The present invention also relates to a polished diamond including a diamond thin film, a polycrystalline diamond, etc., a polished single crystal diamond, and a polished sintered diamond compact obtained by the grinder and polishing method.
BACKGROUND OF THE INVENTION
Diamond thin films which have recently attracted considerable attention are one of the materials which utilize diamond. Diamond thin films (ie. a diamond thin film formed on a substrate and a diamond thin-film coating member) and diamond self-standing films each consist of diamond polycrystalline grains that have been produced industrially (artificially) by a gas phase synthetic method (CVD method) or the like. However, diamond thin films obtained by the above synthetic method consist of a great number of crystal grains and have a rough surface.
Thus, the rough surface of a diamond thin film formed by a gas phase synthetic method must be planarized before its use in, for example, electronic parts, optical parts, super precision parts, or machining tools.
Further, although a natural single crystal diamond and an artificial single crystal diamond formed by, for example, a high pressure synthetic method or a gas phase synthetic method are currently being used as various kinds of industrial materials, such as a grinder dresser, cutting tool, die, heat sink, and x-ray window, or used as a jewel, the diamonds require finishing to an appropriate shape suitable for their respective applications.
As for a sintered diamond compact utilizing diamond, its characteristics are being made full use of and are becoming widely used in tools for high-speed precision grinding or polishing of automobile engines, tools for precision grinding or polishing of cemented carbide, grinding or cutting tools, wear-resistant parts, heat sinks or packages for communication instruments, etc.
The sintered diamond compacts usually contain Co, WC, TiC, etc. as a binder additive; however, some contain little or no binder additive. Unless otherwise specified, “diamond sintered compacts” used herein include sintered compacts containing Co, WC, TiC, etc. as a binder additive or sintered compacts containing little or no binder additives.
It is easily understood that polishing diamond is not easy since diamond is extremely hard. It is so hard that it is commonly used for polishing other hard materials such as metals and ceramics or for fine-polishing jewelry.
As a method for planarizing a polycrystalline diamond thin film or a free-standing diamond film which each have a large amount of roughness on their surfaces, a Scaife method is utilized in which the diamond films are polished with diamond powders intervened between the diamond film and a hard cast iron plate rotating at a high speed (ie. grinding and polishing using a diamond).
This method has been used for polishing diamond as a jewel; however, as a method for polishing the foregoing artificial diamonds, its processing efficiency is extremely low and it is therefore not used.
In particular, for the foregoing diamond single crystal, its hardness varies dramatically from crystal plane to crystal plane or from orientation to orientation. The crystallographic planes which can be polished are limited to, for example, the (100) and (110) planes under present conditions, and it is extremely difficult to polish the (111) plane which is superior to any other planes in hardness and thermal conductivity. In actuality, it has been considered that it is substantially impossible to polish that crystal plane.
Thus, polishing a diamond single crystal requires such great skill that polishing is carried out while examining the crystallographic planes and orientation to locate the plane to be possibly polished. This has led to making diamond polishing complicated and expensive.
As for the sintered diamond compacts, when employing a polishing method using a diamond grinder (ie. grinding and polishing using a diamond) described above, an intense step (about several &mgr;m) is likely to occur due to a difference in hardness at grain boundaries between diamond and binder or between neighboring diamond grains, or due to a falling of many diamond grains in the sintered compact. Thus, when using a sintered diamond compact as a machining tool as described above, grinding accuracy decreases. When using the same as a wear-resistant part, the problem of deterioration in fracture properties arises, and even the problems of damage to the sintered diamond compact and falling of diamond grains in the sintered diamond compact arise.
As described above, a diamond is so hard a material that there is no substitute for it; therefore, it is only natural to consider that there is no abrasive for diamond except diamond itself (ie. grinding and polishing using diamond). Thus there have been devised grinders for polishing diamonds in which a diamond abrasive for grinding and polishing using a diamond are embedded in different kinds of binders.
Examples of such grinders include a resin bonded diamond wheel utilizing phenol resin, a metal bonded diamond wheel, a vitrified bonded diamond wheel utilizing feldspar/quartz, and an electroplated diamond grinding wheel.
The basic concept of the above methods is to scratch the surface of the diamond subject to polishing with diamond abrasive. Unless otherwise specified, “diamond” used herein means diamond itself as well as materials containing diamond, such as, diamond thin films, free-standing diamond films, single crystal diamonds, sintered diamond compacts, and polycrystalline diamonds other than the above. Thus, the wear resistance of the diamond abrasives and the amount of diamond abrasives are the points determining the processing efficiency of the grinders. In addition, any type of binder used as the holder of diamond grains must not present an obstacle to the polishing, and a new cutting edge diamond abrasive grain must appear on the polishing surface every time an old one becomes worn.
One example of the above methods is such that a new cutting edge of diamond abrasive appears automatically according to the amount of the diamond abrasive worn out in a grinder by anodic oxidation of the bond, the grinder binder such as cast iron, with the development of the wear of the diamond abrasive. In this case, as long as the diamond abrasive exists which can effectively polish the subject of polishing, iron oxide is formed on the surface of the binder so as to prevent it from being electrolyzed.
This method is considered to be the most efficient among the foregoing. However, even this method still gives rise to problems, such as complicated operation, high cost and unstable polishing quality. For high-quality diamond powders to be suitable for use as an abrasive in the above method, a suitable binder must be selected. The selected binder must be embedded in the grinder and the quality of the same must be maintained; electrolysis equipment and setting of its conditions are required; and polishing operation and its control are also required. The quality of polishing is determined by all of the above.
When the material being polished is a diamond thin film, the polishing rate and the polishing efficiency are limited due to the number of diamond grains in the material being polished being overwhelmingly large compared with the number of diamond grains of the abrasives applied during the polishing process.
As described above with the method for polishing diamond utilizing a grinding and polishing tool for diamond, problems have still persisted involving the intensive wear of the grinder and the need of an expensive polishing apparatus which
Abe Toshihiko
Hashimoto Hitoshi
Takeda Shu-Ichi
Agency of Industrial Science and Technology
Howson and Howson
Turner Archene
LandOfFree
Grinding and polishing tool for diamond, method for... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Grinding and polishing tool for diamond, method for..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Grinding and polishing tool for diamond, method for... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3060126