Solid anti-friction devices – materials therefor – lubricant or se – Lubricants or separants for moving solid surfaces and... – Organic sulfur compound
Reexamination Certificate
2002-01-16
2003-12-02
Howard, Jacqueline V. (Department: 1764)
Solid anti-friction devices, materials therefor, lubricant or se
Lubricants or separants for moving solid surfaces and...
Organic sulfur compound
C508S577000, C508S579000
Reexamination Certificate
active
06656890
ABSTRACT:
This application is a 371 of PCT/6B00/00360
TECHNICAL FIELD
This invention relates to a lubricating grease which is intended primarily for use in constant velocity universal joints which are used in the drivelines of motor vehicles.
BACKGROUND ART
The motions of components within constant velocity joints (CVJ) are complex with a combination of rolling, sliding and spinning. When the joints are under torque, the components are loaded together which can not only cause wear on the contact surfaces of the components, but also rolling contact fatigue and significant frictional forces between the surfaces. The wear can result in failure of the joints and the frictional forces can give rise to noise, vibration and harshness (NVH) in the driveline. NVH is normally “measured” by determining the axial forces generated in plunging type CVJ. Ideally the greases used in constant velocity joints need not only to reduce wear, but also have to have a low coefficient of friction to reduce the frictional forces and to reduce or prevent NVH.
Constant velocity joints also have sealing boots of elastomeric material which are usually of bellows shape, one end being connected to the outer part of the CVJ and the other end to the interconnecting or output shaft of the CVJ. The boot retains the grease in the joint and keeps out dirt and water.
Not only must the grease reduce wear and friction and prevent the premature initiation of rolling contact fatigue in a CVJ, it must also be compatible with the elastomeric material of which the boot is made otherwise there is a degradation of the boot material which causes premature failure of the boot, allowing the escape of the grease and ultimately failure of the CVJ. The two main types of material used for CVJ boots are polychloroprene rubber (CR) and ether-ester block co-polymer thermoplastic elastomer (TEEE).
Typical CVJ greases have base oils which are blends qf naphthenic (saturated rings) and paraffinic (straight and branched saturated chains) mineral oils. Synthetic oils may also be added. It is known that these base oils have a large influence on the deterioration (swelling or shrinking) of CR boots. All mineral and synthetic base oils extract the plasticisers and other protective agents from the rubber boot materials. Paraffinic mineral oils and poly &agr;-olefin (PAO) synthetic base oils diffuse very little into the CR causing shrinkage, but on the other hand naphthenic mineral oils and synthetic esters diffuse into the CR and act as plasticisers and can cause swelling. The plasticisers used in the CR used for boots typically have pour points below −50° C. and this gives the CR good low temperature properties. The naphthenic mineral oils used in CVJ greases have a pour point which is typically around −35° C., although this can depend on the viscosity and refining process of the naphthenic oils. The exchange of the rubber plasticiser(s) for the naphthenic mineral oil can therefore significantly reduce the rubber performance at low temperatures and may cause the rubber boots to fail by cold cracking, ultimately resulting in failure of the CVJ. If significant swelling or softening occurs, the maximum high speed capability of the boot is reduced due to poor stability at speed and/or excessive radial expansion.
The addition of a plasticiser to grease base oil is effective in retaining the cold temperature performance of the CR after ageing by reducing the loss of plasticiser from the CR but has the following deleterious effects:
1. it increases the volume change of the CR after ageing; and
2. it reduces the base oil viscosity and hence increases friction and wear and may promote rolling contact fatigue in the CVJ.
The object of the invention is to provide a lubricating grease, primarily for CVJ, which has a good compatibility with CR boot materials and which also gives low wear and low friction and prevents the premature initiation of rolling contact fatigue in the joint.
DISCLOSURE OF THE INVENTION
According to the invention we provide a lubricating grease composed of:
a. a base oil combination comprising 10 to 35% of one or more poly &agr;-olefins, 3 to 15% of one or more synthetic organic esters, 20 to 30% of one or more naphthenic oils, the remainder of the combination being one or more paraffinic oils, the percentages being by weight of the total base oil combination and the ratio of the weight of the ester(s) in the combination to the weight of the poly &agr;-olefin(s) therein being no greater than 1:3 (preferably approximately 1:4)
b. between 2 and 15% by weight of the total grease of a lithium soap thickener;
c. between 1 and 5% (preferably between 1 and 2%) by weight of the total grease of a molybdenum dithiophosphate of the following general formula:
wherein X or Y represents S or O and each of R
1
to R
4
inclusive may be the same or different and each represents a primary (straight chain) or secondary (branched chain) alkyl group having between 1 and 24 carbon atoms or an aryl group having between 6 and 30 carbon atoms;
d. between 1 and 5% (preferably between 1 and 2%) by weight of the total grease of a zinc dialkyldithiophosphate of the following general formula:
(R
5
O)(R
6
O)SP—S—Zn—S—PS(OR
7
)(OR
8
)
wherein each of R
5
to R
8
inclusive may be the same or different and each represents a primary or secondary alkyl group having 1 to 24, preferably 3 to 8 carbon atoms;
e. between 1 and 5% (preferably between 1 and 2%) by weight of the total grease of a sulphur-free friction modifier; and
f. some or all of the normal grease additives such as anti-oxidants, corrosion inhibitors, extreme pressure additives, and tackiness agents.
We have found that the use of the above mentioned base oil combination together with the inclusion of the molybdenum dithiophosphate (MoDTP), the zinc dialkyldithiophosphate (ZDTP) and the sulphur-free friction modifier gives a grease which has significantly less deleterious effect on the CR material of the boots, and which gives both very good wear and friction properties, prevents the initiation of rolling contact fatigue and reduces the axial forces in plunging type CVJ.
The preferred organic synthetic esters are di-carboxylic acid derivatives with sub-groups based on aliphatic alcohols. Preferably the di-carboxylic acid is sebacic acid and the alcohols have primary, straight or branched carbon chains with 2 to 20 carbon atoms. The preferred synthetic ester is therefore dioctyl sebacate (DOS) but dioctyl adipate (DOA), dioctyl phthalate (DOP), or dioctyl azelate (DOZ), which are also used as plasticisers in the CR boot materials, may also be used.
Preferably the sulphur-free friction modifier is an organo-molybdenum complex, preferably a complex of an organo-amide as described for example in U.S. Pat. No. 4,889,647 the disclosure of which is imported herein by reference.
The molybdenum dithiophosphate may be sulphurised oxymolybdenum-2-ethylhexyl phosphorodithioate and the zinc dialkyldithiophosphate may be a mixture of primary and secondary alkyl dithiophosphates with carbon chains of between 3 and 14 atoms.
The thickener may be a simple lithium soap formed from stearic acid, 12-hydroxy stearic acid or from other similar fatty acids or mixtures thereof or methyl esters of such acids. Alternatively a lithium complex soap may be used formed e.g. from a mixture of long chain fatty acids together with a complexing agent, e.g. a borate or one or more dicarboxylic acids. The use of complex lithium soaps allows the grease to operate up to a temperature of about 180° C. whereas with simple lithium soaps the grease will only operate up to a temperature of about 120° C.
The grease may include between 0.5 to 3.0% by weight of a calcium sulphonate salt as a corrosion inhibitor. Typically, the last operation before assembly of a CVJ is a wash to remove machining debris, it is therefore necessary for the grease to absorb any traces of remaining water and to prevent that water from causing corrosion and adversely affecting the performance of the CVJ.
The grease may also include between 0.10 to 3.0% by weight of a
Cooper Jennifer Sarah
Davies Trevor David
E Jisheng
Fish Gareth
Isaac Gareth Robert
GKN Automotive GmbH
Howard Jacqueline V.
LandOfFree
Grease composition for constant velocity joints does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Grease composition for constant velocity joints, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Grease composition for constant velocity joints will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3130655