ABSTRACT:
FIELD OF THE INVENTION
The present invention is directed to golf balls having metallocene catalyzed polyolefin cores and relatively thick covers comprising one or more layers that are durable and resistant to cracks and fractures.
In another aspect, the present invention is directed to golf balls having a thick multi-layer cover where at least one of the cover layers has at least one high acid ionomer resin.
BACKGROUND OF THE INVENTION
Top grade golf balls sold in the United States generally comprise a central core with one or more cover layers formed thereover. A golf ball cover is particularly influential in effecting the compression (feel) and durability (i.e., impact resistance, etc.) of the resulting ball. Various cover compositions have been developed in order to optimize desired properties of the resulting golf balls.
FIGS. 1 and 2
illustrate a conventional golf ball
10
having a single cover layer
14
molded about a golf ball core
16
.
FIG. 2
illustrates (in an exaggerated view) stress lines
12
extending partially, or entirely across the thickness of the cover layer
14
. Stress lines
12
typically result in a crack or fracture across the thickness of the golf ball cover.
FIGS. 1 and 2
illustrate one problem that may occur when a very thick, single layer cover is formed about a golf ball core.
Although not wishing to be bound to any particular theory, it is believed that stress lines in a golf ball cover, such as stress lines
12
in cover
14
, result from repeated strikes with a golf club, particularly drivers, and temperature effects. Stress lines often serve as initiation sites for crack or fracture propagation in a golf ball cover material. Such cracks or fractures, and their related stress lines, are undesirable in golf ball covers. Moreover, it is particularly undesirable for such stress lines and the resulting cracks or fractures to extend across the entire thickness of a golf ball cover since such damage significantly impairs golf ball performance. And, such cracks or fractures greatly reduce the durability of a golf ball cover.
When a multi-layer cover is employed, each cover layer traditionally has had a significantly different Shore D hardness than an adjacent cover layer in order to impart to the golf ball a particular desired combination of spin and distance characteristics. Although the use of a multi-layer cover configuration reduces the tendency of stress lines, and thus cracks and fractures, propagating across the entire thickness of the cover, such multi-layer arrangement of cover materials, each having its own particular set of properties and characteristics, has associated design and manufacturing problems.
For instance, in order to produce a multiple cover layer golf ball that exhibits a desired set of performance characteristics, it is necessary to design and anticipate an overall performance profile for the set of cover layers. This involves analyzing each of the individual cover layers and any and all effects between the individual cover layers. Even if such daunting design analysis is performed, the increased number of variables may lead to unanticipated difficulties in manufacturing or with the final product golf ball.
In addition, although, once again, not wishing to be bound to any particular theory, it is believed that although a multiple cover layer configuration may reduce the tendency for cracks or fractures that extend through the entire thickness of the cover, such configuration may lead to an increase in the number or frequency of fractures, particularly in applications in which the various cover layers constituting the multi-layer cover each have different physical properties such as hardness and flexural characteristics.
Accordingly, there is a need for an improved golf ball which is less susceptible to cracking or fracturing across the thickness of the cover than currently known single cover layer golf balls. And, there is a need for an improved multiple cover layer golf ball that is simpler to design and manufacture, and which is less susceptible to cracking or fracturing of one or more of the individual cover layers that constitute the multiple cover layer of the ball.
In addition to the features sought above, it would also be useful to develop the above golf balls having reduced amounts of polybutadiene in the core in order to improve mechanical properties and durability, while maintaining desirable feel.
BRIEF SUMMARY OF THE INVENTION
The present invention is directed to a golf ball comprising a solid core and a multi-layer cover disposed about the core. The solid core comprises a metallocene catalyzed polyolefin and has a PGA compression of about 85 or less. The multi-layer cover has an overall cover thickness of at least about 3.6 mm (0.142 inches).
The present invention is further directed to a golf ball comprising a core and multi-layer cover disposed about the core. The core comprises a metallocene catalyzed polyolefin, has a coefficient of restitution of at least 0.650 and a PGA compression of no greater than 85. The multi-layer cover has at least one cover layer comprising an ionomer. The multi-layer cover also has a thickness of at least about 3.8 mm (0.150 inches) and a Shore D hardness of at least about 60. The golf ball has a coefficient of restitution of at least about 0.770.
The present invention is yet further directed to a golf ball comprising a core, a first cover layer disposed about the core, and a second cover layer disposed about the first cover layer. The core comprises a metallocene catalyzed polyolefin and has a PGA compression of no greater than 85. The first cover layer includes a first resin composition and a filler material. The second cover layer includes a second resin composition. The second resin composition is different from the first resin composition and the difference between the Shore D hardness of the first cover layer and second cover layer is less than about 2.
In another aspect, the present invention is directed to a golf ball having a solid core and a multi-layer cover disposed about the core. The core has a PGA compression of no greater than about 85. The multi-layer cover has an overall thickness of at least about 3.6 mm (0.142 inches) and a Shore D hardness of at least about 60. At least one layer of the multi-layer cover comprises a high acid ionomer having at least 16% by weight of an alpha, beta-unsaturated carboxylic acid.
In yet a further aspect, the present invention is directed to a golf ball comprising a core and multi-layer cover disposed about the core. The core comprises at least one member selected from the group consisting of polybutadiene and natural rubber. The core has a coefficient of restitution of at least about 0.650 and a PGA compression of no greater than about 85. The multi-layer cover comprises at least one layer having a high acid ionomer having at least 16% by weight of an alpha, beta-unsaturated carboxylic acid. The multi-layer cover has a thickness of at least about 3.8 mm (0.150 inches) and a Shore D hardness of at least about 60. The golf ball has a coefficient of restitution of at least about 0.770.
In a further aspect, the present invention is directed to a golf ball comprising a core, a first cover layer disposed about the core, and a second cover layer disposed about the first cover layer. The first cover layer has a first resin composition and the second cover layer has a second resin composition, and the difference in Shore D hardness between the first and second cover layers is less than about 2. The overall thickness of the first and second layers is at least 3.6 mm. At least one of said first cover layer and second cover layer comprises a high acid ionomer having at least 16% by weight of an alpha, beta-unsaturated carboxylic acid.
In yet another embodiment, the present invention is directed to a golf ball comprising a core and a multi-layer cover disposed about the core. The solid core comprises a metallocene catalyzed polyolefin. The multi-layer cover has an overall thickness of at least about 3.6 mm (0.142 inches) and a Shore D ha
Binette Mark L.
Sullivan Michael J.
Callaway Golf Company
Gorden Raeann
Graham Mark S.
LandOfFree
Golf ball with multi-layer cover does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Golf ball with multi-layer cover, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Golf ball with multi-layer cover will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3186628