ABSTRACT:
FIELD OF THE INVENTION
The invention generally relates to components and to a process for producing components.
BACKGROUND OF THE INVENTION
Components feature an optoelectronic functional unit which is generally arranged on a substrate, in particular a glass substrate. The optoelectronic functional unit may he a light-emitting diode (LED); for example, an organic light-emitting diode (OLED).
LEDs and OrEDs are composed of two or more functional layers and have, for example, the following structure (in this respect see: “Philips Journal of Research”, Vol. 51 (1998), pages 467 to 477): a thin ITO (indium tin oxide) layer as transparent electrode, a conducting polymer layer, an electroluminescent layer, i.e., a layer of light-emitting material. in particular of a light-emitting polymer, and an electrode made of a metal with a low work function.
Since some of the materials used to construct LEDs and OIDs are very sensitive toward water and oxygen, they must be protected from environmental influences by capsuling; in other words, they are arranged within a housing. This can be done, for example, by covering the LED or OLED, arranged on a glass substrate, with a glass plate and adhesively bonding this glass plate to the glass substrate (in this respect see: “Applied Physics Letters”, Vol. 65 (1994), pages 2922 to 2924). Adhesive bonding is carried out using, for example, an epoxy resin. In this case, however, a relatively thick adhesive joint is needed, with the consequence that moisture may penetrate the cavity between glass substrate and glass plate by way of the adhesive film.
Additionally, an electroluminescent system has already been disclosed in which the housing within which the electroluminescent unit, which has an electroluminescent organic layer, is enclosed comprises a layer of a low-melting metal or of a corresponding alloy which is attached using an adhesive film to a substrate which bears the electroluminescent unit (see: WO97/46052). Although the electroluminescent system can be made highly impervious by this method, the method is associated with a high degree of complexity and high cost. A further disadvantage is that the relatively high temperatures needed to process the metal or alloy from the melt may result in damage to the electroluminescent unit.
The same applies in principle to a process wherein the organic functional unit, particularly an OLED, is encapsulated using glass solder (German patent application file ref. 198 45 075.3). In OLEDs, the temperatures required for processing glass solders presently available lead to damage to the functional organic materials. In this case, furthermore an additional frame is disposed between the lid of the housing and the glass substrate in order to prevent mechanical damage to the OID structure. This, however, means additional worksteps and adhesive joints, which are associated with the risk of perviousness.
EP-A0 776 147 discloses an organic electroluminescent system in which the light-emitting diode is arranged in an airtight container in order to shield it from the external atmosphere. In the interior of the container, but separated from the diode, moreover, there is a substance for chemical absorption of moisture. The container is composed of a sealing housing, a transparent substrate which covers this housing, and a sealant which binds the substrate to the housing. Housing and substrate may be composed of glass.
Glass housings are normally produced by casting or forming, i.e., pressing. The resulting containers, however, are not very precise and the surfaces are smooth. Moreover, the surfaces are not sufficiently planar. However, when sealing OLEDs the bond surfaces must be planar, with a tolerance of a few micrometers. With containers of this kind, therefore. laborious machining of the bond surfaces is necessary.
SUMMARY OF THE INVENTION
It is an object of an embodiment of the invention to design components comprising an optoelectronic functional unit. This can be done, for example, in such a way that on the one hand the functional unit is hermetically capsuled, i.e., is not adversely affected by environmental effects such as water and air, and also cannot be damaged mechanically. Further, on the other hand, the capsuling can be realized relatively simply.
This can be achieved in accordance with an embodiment of the invention by components which comprise the following elements:
a glass substrate
an organic light-emitting diode arranged on said glass substrate, and
a glass cover which is arranged over the organic light-emitting diode and is glued at the edge to the glass substrate, said cover being produced from a glass plate by three-dimensional removal of material using a blasting method.
In the components of the embodiment of the invention, the glass cover together with the glass substrate forms a stable cavity within which the OLED is arranged; mechanical damage is hence impossible. Damage caused by environmental effects also does not occur, since the components are hermetically capsuled, i.e., imperviously sealed, for which only a very narrow adhesive joint is necessary.
The use of glass covers—instead of metal coverings—in conjunction with glass substrates has the advantage that glasses with an adapted thermal expansion coefficient can be used. As a result, it is possible to reduce the mechanical stress on the adhesive joint, such as occurs, for example, owing to a thermal loading of the component by temperature cycles.
The glass cover, which combines the functions of covering and frame, is produced from a glass plate by three-dimensional removal of material using a blasting method. In this procedure a recess of defined geometry and depth is formed with a high level of precision. A procedure of this kind is known in principle, specifically for making ink troughs and aperts in the coverglasses of ink printheads (in this respect see: DE-C40 18 132).
The glass covers may be produced by sandblasting, i.e., using quartz sand. Examples of other blasting materials that can be used include aluminum oxide, silicon oxide, silicon carbide or boron carbide.
The removal of material from the glass plate preferably takes place by blast machining. This manufacturing process and the blasting materials it uses can be found in DIN 8200. The removal rate and achievable depth of the recess are dependent on the relative movement between workpiece and blasting nozzle, on the nature of the blasting material, on its average diameter, on the blasting pressure, and on the distance of the nozzle from the substrate.
The glass covers of the invention can thus be produced simply and there is no need for any laborious subsequent machining such as is the case with glass housings produced in the customary manner. The glass housings, moreover, arm produced individually, and must therefore be individually positioned and processed for adhesive bonding. Individual processing, however, is expensive and unsuited to the mass manufacture which is normal in the display industry.
In contrast, the glass covers of the invention may be produced very simply even in large panels. In the display industry, panel sizes of 16 inch×16 inch or more are nowadays the norm. The glass covers needed for this purpose must be able to be produced in the same panel size for a mass manufacturing process. This is very easy to realize by structuring corresponding glass plates using photolithographic processes and producing, for example, up to 150 recesses—of the desired shape and depth—in the glass plate via a blasting method. Individualization may then take place by known processes and in general occurs only after the joining procedure. One particularly preferred variant of an embodiment of the invention therefore includes producing a large number of recesses in a glass panel in a single operation, in accordance with a layout which is predetermined by the display to be encapsulated, and carrying out individualization only after encapsulation. An additional advantage is that virtually any desired shape can be produced by simple photolithographic structuring.
It is furt
Ambrugger Alois
Hamann Christoph
Rogler Wolfgang
Roth Wolfgang
Harness & Dickey & Pierce P.L.C.
Siemens Aktiengesellschaft
Williams Joseph
LandOfFree
Glass cover and process for producing a glass cover does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Glass cover and process for producing a glass cover, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Glass cover and process for producing a glass cover will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3212503