Freestanding microporous separator including a gel-forming...

Details Freestanding microporous separator including a gel-forming... Freestanding microporous separator including a gel-forming...

2001-02-05

2003-07-01

Ryan, Patrick (Department: 1745)

Chemistry: electrical current producing apparatus, product, and

Current producing cell, elements, subcombinations and...

Separator, retainer, spacer or materials for use therewith

C429S247000, C429S248000, C429S250000

Reexamination Certificate

active

06586138

ABSTRACT:

TECHNICAL FIELD
This invention relates to the field of separators for electrochemical cells and more particularly to microporous polyolefin separators for such cells.
BACKGROUND OF THE INVENTION
Lithium-ion batteries are the preferred power source for most portable electronics devices. This is so because lithium-ion batteries exhibit higher energy density, longer cycle life, and higher operational voltage as compared to nickel cadmium, nickel metal hydride, and other rechargeable battery systems. Lithium-ion batteries also provide advantages when compared to lithium primary batteries in that they generally use a carbon-based anode as opposed to highly reactive metallic lithium. The carbon-based anode functions via the intercalation of lithium ions between graphene sheets. Lithium-ion batteries are typically produced in spiral wound and prismatic configurations in which a separator is sandwiched between anode and cathode ribbons. The pores of the separator are then filled with an ionically conductive electrolyte. Lithium-ion polymer batteries are produced using electrode ribbons of similar type with a gel electrolyte sandwiched between them.
Thus battery separators are an integral part of the operation, performance, and safety of lithium-ion batteries. The principal function of the separator is to prevent electrical conduction (i.e., “shorts”) between the anode and the cathode while permitting ionic conduction via the electrolyte. In addition to providing good mechanical properties for winding and low electrical resistivity for device performance, separators play an important role in the overall safety of lithium-ion cells. During a thermal excursion above about 120° C., a liquid electrolyte-filled separator is expected to “shutdown” so that ionic conduction between the anode and cathode is eliminated. Separator composition is the variable that largely determines the shutdown temperature.
In general, polypropylene separators have a shutdown temperature that is too high (>150° C.) for use in lithium-ion applications, while high density polyethylene (HDPE) separators often do not fully shutdown because of “hole formation” that results from shrinkage and poor mechanical integrity under pressure and high temperature. Ultrahigh molecular weight polyethylene (UHMWPE) separators are usually transformed into a nonporous, clear film upon shutdown. Another advantage of UHMWPE separators is that they can be modified with linear low density polyethylene (LLDPE) or other forms of polyethylene to manipulate the shutdown temperature without compromising mechanical integrity. Therefore, UHMWPE separators offer desirable safety features for use in liquid electrolyte lithium-ion batteries.
Polyolefin separators are generally prepared using either a “dry” or “wet” method of manufacture, and which of these methods is employed has a profound effect on the porosity, pore size distribution, and tortuosity of the separator. Separators manufactured using the “dry” method generally have a distinct slit-pore microstructure with a pore width of approximately 40 nm. Separators manufactured using the “wet” process have interconnected spherical and/or elliptical pores with diameters of 50-100 nm. UHMWPE separators have outstanding mechanical properties and exhibit excellent wettability with organic electrolytes.
One physical property of battery separators that is of special concern to battery manufacturers is separator thickness because there exists a need for improved energy and power density in lithium-ion batteries. These concerns have caused battery manufacturers to consider thinner separators. Most separators have thicknesses of 20-50 micrometers, but advances in lithium-ion battery technology have made it desirable for separator manufacturers to provide separators as thin as 8 micrometers. Separator thickness is largely dependent on the manufacturing process employed.
There are two types of electrolyte system commonly used in lithium-ion batteries. The first type of commonly used electrolyte system is a liquid electrolyte system in which a liquid electrolyte is used to provide sufficient ionic conduction between electrodes that are packaged in a cylindrical or prismatic metal can. Liquid electrolyte systems have the advantage of providing a thin electrolyte-filled separator with excellent conductivity. However, the use of a liquid electrolyte system necessitates the use of a metal can to contain the liquid electrolyte system. The use of metal cans limits a battery manufacturer's options in terms of battery shape and size.
The second type of commonly used electrolyte system is a gel electrolyte system in which a gel electrolyte is sandwiched between the electrodes. One method of creating a gel-electrolyte system entails heating a mixture of liquid electrolyte and semi-crystalline polymer(s). Cooling the liquid electrolyte/polymer mixture forms a gel. A major advantage of this approach is that the electrolyte has been immobilized, much like water is immobilized in the gelatin polymer used to produce the Jell-O™ gelatin. The gel electrolyte system also enables battery manufacturers to bond the electrodes together and utilize a flexible pouch rather than a metal can to package the battery, resulting in increased form factor options (i.e., battery shape and size). However, a major disadvantage of the gel electrolyte system is its increased thickness (approximately two to three times thicker than the liquid electrolyte system), which leads to reduced energy and power density. Also, the gel electrolyte system suffers from (1) poor mechanical properties, making assembly difficult and increasing the incidence of shorting between the electrodes, (2) a tendency to swell at elevated temperatures, and (3) lower conductivity as a compared to liquid electrolyte systems.
It is thus desirable to create an electrolyte system that maximizes the advantages of both the liquid and gel electrolyte systems while minimizing their disadvantages. One prior art attempt to achieve this objective entailed coating a porous separator with a nonporous gel-forming polymer and then sandwiching the resulting separator between two electrodes. The electrode and separator combination was then placed in a flexible pouch and liquid electrolyte was introduced. The liquid electrolyte wicked into the electrodes and then into the edges of the polymer web, and the electrolyte then diffused throughout the polymer web and the polymer web coating. The flexible pouch was heated under pressure to bond the electrodes together and to form a homogeneous gel electrolyte system.
In a second prior art attempt, a slurry of gel-forming polymer and liquid electrolyte was coated onto a polyolefin web. Thereafter, the paste was heated such that the gel-forming polymer seeped or was drawn into the pores of the polyolefin web. Upon cooling, the gel-forming polymer became a rigid gel electrolyte. Thus the pores in the bulk region of the resultant separator were completely filled with gel electrolyte.
The gel electrolyte systems resulting from these two prior art attempts exhibit sufficient ionic conductivity, flexibility, and thickness to allow the user to implement new battery shapes. However, both procedures suffer from increased manufacturing cycle time and a consequent inefficient manufacturing process as a result of the dramatic increase in time required to achieve uniform electrolyte distribution.
Accordingly, there exists a need for use as a lithium-ion battery separator a microporous, thin, open-cell structure that maximizes electrolyte wetting and filling and exhibits high ionic conductivity.
SUMMARY OF THE INVENTION
An object of the present invention is to provide a microporous polymer web for use in lithium-ion batteries that contains passageways which foster expedient and uniform electrolyte distribution, thereby resulting in reduced cycle time and resistivity and increased wettability.
The present invention is a freestanding battery separator comprising a microporous polymer web with passageways that provide overall fluid permeability. The poly

Affiliated with

Also associated with

Rating

Freestanding microporous separator including a gel-forming... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Freestanding microporous separator including a gel-forming..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Freestanding microporous separator including a gel-forming... will most certainly appreciate the feedback.