Stock material or miscellaneous articles – Web or sheet containing structurally defined element or... – Composite having voids in a component
Reexamination Certificate
2002-03-25
2003-07-15
Dunn, Tom (Department: 1725)
Stock material or miscellaneous articles
Web or sheet containing structurally defined element or...
Composite having voids in a component
C428S158000, C428S319300, C429S231800, C429S245000
Reexamination Certificate
active
06592982
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to an article of flexible graphite sheet, having a coating of glassy carbon, which is fluid permeable in a transverse direction with enhanced isotropy with respect to thermal and electrical conductivity and enhanced resistance to chemical attack. This article can be used as an electrically conductive element in an electrical capacitor of the flow-through type. In a particular embodiment, natural cellulosic fibers are included in the glassy carbon coating and are carbonized and activated.
BACKGROUND OF THE INVENTION
Graphites are made up of layer planes of hexagonal arrays or networks of carbon atoms. These layer planes of hexagonally arranged carbon atoms are substantially flat and are oriented or ordered so as to be substantially parallel and equidistant to one another. The substantially flat, parallel equidistant sheets or layers of carbon atoms, usually referred to as basal planes, are linked or bonded together and groups thereof are arranged in crystallites. Highly ordered graphites consist of crystallites of considerable size: the crystallites being highly aligned or oriented with respect to each other and having well ordered carbon layers. In other words, highly ordered graphites have a high degree of preferred crystallite orientation. It should be noted that graphites possess anisotropic structures and thus exhibit or possess many properties which are highly directional e.g. thermal and electrical conductivity and fluid diffusion. Briefly, graphites may be characterized as laminated structures of carbon, that is, structures consisting of superposed layers or laminae of carbon atoms joined together by weak van der Waals forces. In considering the graphite structure, two axes or directions are usually noted, to wit, the “c” axis or direction and the “a” axes or directions. For simplicity, the “c” axis or direction may be considered as the direction perpendicular to the carbon layers. The “a” axes or directions may be considered as the directions parallel to the carbon layers or the directions perpendicular to the “c” direction. The natural graphites suitable for manufacturing flexible graphite possess a very high degree of orientation.
As noted above, the bonding forces holding the parallel layers of carbon atoms together are only weak van der Waals forces. Natural graphites can be treated so that the spacing between the superposed carbon layers or laminae can be appreciably opened up so as to provide a marked expansion in the direction perpendicular to the layers, that is, in the “c” direction and thus form an expanded or intumesced graphite structure in which the laminar character of the carbon layers is substantially retained.
Natural graphite flake which has been greatly expanded and more particularly expanded so as to have a final thickness or “c” direction dimension which is at least 80 or more times the original “c” direction dimension can be formed without the use of a binder into cohesive or integrated flexible graphite sheets of expanded graphite, e.g. webs, papers, strips, tapes, or the like. The formation of graphite particles which have been expanded to have a final thickness or “c” dimension which is at least 80 times the original “c” direction dimension into integrated flexible sheets by compression, without the use of any binding material is believed to be possible due to the excellent mechanical interlocking, or cohesion which is achieved between the voluminously expanded graphite particles.
In addition to flexibility, the sheet material, as noted above, has also been found to possess a high degree of anisotropy with respect to thermal and electrical conductivity and fluid diffusion, comparable to the natural graphite starting material due to orientation of the expanded graphite particles substantially parallel to the opposed faces of the sheet resulting from very high compression, e.g. roll pressing. Sheet material thus produced has excellent flexibility, good strength and a very high degree of orientation.
Briefly, the process of producing flexible, binderless anisotropic graphite sheet material, e.g. web, paper, strip, tape, foil, mat, or the like, comprises compressing or compacting under a predetermined load and in the absence of a binder, expanded graphite particles which have a “c” direction dimension which is at least 80 times that of the original particles so as to form a substantially flat, flexible, integrated graphite sheet. The expanded graphite particles which generally are worm-like or vermiform in appearance, once compressed, will maintain the compression set and alignment with the opposed major surfaces of the sheet. The density and thickness of the sheet material can be varied by controlling the degree of compression. The density of the sheet material can be within the range of from about 5 pounds per cubic foot to about 125 pounds per cubic foot. The flexible graphite sheet material exhibits an appreciable degree of anisotropy due to the alignment of graphite particles parallel to the major opposed, parallel surfaces of the sheet, with the degree of anisotropy increasing upon roll pressing of the sheet material to increased density. In roll pressed anisotropic sheet material, the thickness, i.e. the direction perpendicular to the opposed, parallel sheet surfaces comprises the “c” direction and the directions ranging along the length and width, i.e. along or parallel to the opposed, major surfaces comprises the “a” directions and the thermal, electrical and fluid diffusion properties of the sheet are very different, by orders of magnitude, for the “c” and “a” directions.
This very considerable difference in properties, i.e. anisotropy, which is directionally dependent, can be disadvantageous in some applications. For example, in gasket applications where flexible graphite sheet is used as the gasket material and in use is held tightly between metal surfaces, the diffusion of fluid, e.g. gases or liquids, occurs more readily parallel to and between the major surfaces of the flexible graphite sheet. It would, in most instances, provide for improved gasket performance, if the resistance to fluid flow parallel to the major surfaces of the graphite sheet (“a” direction) were increased, even at the expense of reduced resistance to fluid diffusion flow transverse to the major faces of the graphite sheet (“c” direction). With respect to electrical properties, the resistivity of anisotropic flexible graphite sheet is high in the direction transverse to the major surfaces (“c” direction) of the flexible graphite sheet, and substantially less in the direction parallel to and between the major faces of the flexible graphite sheet (“a” direction). In applications such as certain components for electrochemical cells, it would be of advantage if the electrical resistance transverse to the major surfaces of the flexible graphite sheet (“c” direction) were decreased, even at the expense of an increase in electrical resistivity in the direction parallel to the major faces of the flexible graphite sheet (“a” direction).
With respect to thermal properties, the thermal conductivity of a flexible graphite sheet in a direction parallel to the upper and lower surfaces of the flexible graphite sheet is relatively high, while it is relatively very low in the “c” direction transverse to the upper and lower surfaces.
Another carbon based material having unique properties is glassy carbon.
As used herein and as described in U.S. Pat. No. 5,476,679, the disclosure of which is incorporated herein by reference, glassy carbon is a monolithic non-graphitizable carbon with a high isotropy of the structure and physical properties and with a low permeability for gases and liquids. Glassy carbon typically also has a pseudo-glassy appearance. Glassy carbon can be formed from a non-graphitizing carbon-containing thermosetting resin such as synthetic or natural resins. Thermosetting resins that become rigid on heating and do not significantly soften upon reheating and are particularly effective. The principal groups of resins suita
Calarco Paul
Mercuri Robert Angelo
Weber Thomas William
Chirgott Paul S.
Cooke Colleen P.
Dunn Tom
Graftech Inc.
LandOfFree
Flexible graphite capacitor element does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Flexible graphite capacitor element, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Flexible graphite capacitor element will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3102077