ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to resistive thin films, particularly to metal-oxide thin film resistors, and more particularly to Ti—Cr—Al—O thin film resistors and a process for fabricating same.
The development of metal-oxide materials has been widely pursued in the electronics industry for use as resistive thin films. The use of multiple phases provides a path to change the film resistivity. See C. A. Neugebauer, “Resistivity of Cermet Films Containing Oxides Of Silicon”, Thin Solid Films, 6 (1970), 443-447. The dependence of sheet resistivity on composition is well established for systems such as Cr—Si—O. See. R. Glang et al., “Resistivity and Structure of Cr—SiO Cermet Films”,
J. Vac. Sci. Technol
., 4 (1967), 163-70; A. A. Milgram et al., “Electrical and Structural Properties of Mixed Chromium and Silicon Monoxide Films”,
J. Appl. Phys
. 39 (1968), 4219-4224; N. C. Miller et al., “Co-sputtered Cermet Films”,
Solid State Tech
. 11 (1968), 28-30; and H. Steemers et al., “Stable Thin Film Resistors For Amorphous Silicon Integrated Circuits”,
Mat. Res. Soc. Symp. Proc
., 118 (1988), 445-449. The conduction mechanism for these cermet materials (materials composed of ceramics and metals) can be considered quantum mechanical. See. J. E. Morris, “Structure and Electrical Properties of Au—SiO Thin Film Cermets”,
Thin Solid Films
, 11 (1972), 299-311. For low metallic concentrations, the charge transport is proposed to be by electron tunneling between the metallic particles. See B. E. Springett, “Conductivity Of A System Of Metallic Particles Dispersed In An Insulating Medium”,
J. Appl. Phys
., 44 (1973), 2925-2926. In general, conduction may be considered to be by means of an activated charge transport process. For film resistivities >10
−2
Ohm-cm, the microstructure is usually comprised of a continuous insulating matrix in which metallic particles are dispersed. An increase in metallic content produces a decrease ion sheet resistivity. For the Cr—Si—O system, the insulating matrix is based on the oxide phase of SiO
2
, with Cr, silicides, and monoxides serving as conductors/semiconductors. A general observation by Neugebauer, Supra, suggests that the SiO
2
composition alone could be used to determine the cermet film resistivity to within two orders of magnitude irrespective of deposition technique or conditions. Whereas this summation may represent a general trend, it is not an inclusive statement for the resistivity behavior of Cr—Si—O cermets. Initial work at the Lawrence Livermore National Laboratory with the Cr—Si—O cermet system has shown a widely varying range of resistivities that span more than twelve-orders of magnitude and are often accompanied by a non-linear current-voltage behavior. See A. Jankowski et al., “Resistivity Behavior Of Cr—Si—O Thin Films”, Chem. Phys. Nanostructures and Related Non-Equilibrium Materials, ed. E. Ma. et al., The Minerals, Metals and Materials Soc. Proc. (1997), pg. 211-219. In addition, post-deposition vacuum annealing can cause changes in the resistivity by several orders of magnitude rendering unreliable use of the Cr—Si—O film as a resistor layer of constant value. Due to the limitations of producing a consistent resistivity from 10
5
to 10
8
Ohm-cm for the Cr—Si—O system, an alternate material has been sought which would have a well-defined and stable behavior as a resistor layer.
The present invention provides the sought for alternate for the Cr—Si—O system, and it has been determined that the system of the present invention has a well-defined and stable behavior as a resistor layer. The Ti—Cr—Al—O cermet of the present invention is being developed for use as a thin film resistor since its properties in bulk form are favorable and controllable. The Ti—Cr—Al—O films are radio frequency (rf) sputter deposited to transfer the target composition to the growing cermet film. The films are rf sputter deposited from ceramic targets using a reactive working gas mixture of Ar and O
2
. The film resistivity can be discretely selected through target composition and the control of the deposition parameters.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide metal-oxide resistive thin films which have a well-defined and stable behavior.
A further object of the invention is to provide a metal-oxide thin film which is thermodynamically stable.
A further object of the invention is to provide Ti—Cr—Al—O thin film resistors.
Another object of the invention is to provide a Ti—Cr—Al—O cermet which can be effectively utilized as a resistor material.
Another object of the invention is to provide a process for fabricating Ti—Cr—Al—O thin film resistors.
Another object of the invention is to provide a process for producing Ti—Cr—Al—O ceramic targets and films by rf sputter deposition from the ceramic targets using a reactive working gas mixture of Ar and O
2
.
Another object of the invention is to provide a process for fabricating Ti—Cr—Al—O films wherein the resistivity of the film can be discretely selected through control of the deposition parameters.
Other objects and advantages of the invention will become apparent from the following description and accompanying drawings. The present invention is directed to Ti—Cr—Al—O cermets which can be utilized as a resistor material, and to a process for fabricating Ti—Cr—Al—O thin film resistors. The films are rf sputter deposited from ceramic targets using a reactive working gas mixture of Ar and O
2
, and having, for example, a ceramic powder blend of 2-12% TiO
2
, 30-40% Al
2
O
3
, and 50-65% Cr
2
O
3
, with a film composition, for example, of 1-3 at.% Ti, 15-20 at.% Cr, 10-20 at.% Al, and 58-70 at.% O. The films are deposited to a thickness >0.2 &mgr;m in order to avoid effects often seen in metalxide films <0.1 &mgr;m thick. See T. Filutowicz et al., “The Effects Of Film Thickness On Certain Properties Of Cr—SiO Cermet Thin Films”,
Electron Technology
. 10 (1977), 117-126; and H. S. Hoffman et al., “Cermet Resistors On Ceramic Substrates”,
IEEE Trans. On Components. Hybrids And Manufacturing Technol
., 4 (4) (1981), 387-395. The film resistivity can be discretely selected through control of the target composition and the sputter deposition parameters. The application of Ti—Cr—Al—O as a thin film resistor has been found to be thermodynamically stable, unlike other metal-oxide material systems.
REFERENCES:
patent: 2590893 (1952-04-01), Sanborn
patent: 5001454 (1991-03-01), Yamadera et al.
patent: 5142184 (1992-08-01), Kane
patent: 5532548 (1996-07-01), Spindt et al.
patent: 5783315 (1998-07-01), Schaeffer et al.
patent: 5789851 (1998-08-01), Turlot et al.
patent: 5990613 (1999-11-01), Ageno et al.
patent: 63147305 (1988-06-01), None
Jankowski Alan F.
Schmid Anthony P.
Carnahan L. E.
Patel Nimeshkumar D.
Roy Sikha
The Regents of the University of California
Thompson Alan H.
LandOfFree
Flat panel display using Ti-Cr-Al-O thin film does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Flat panel display using Ti-Cr-Al-O thin film, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Flat panel display using Ti-Cr-Al-O thin film will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2906503