Flat glass annealing lehrs

Glass manufacturing – Control responsive to condition sensing means – Temperature or heater control

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C065S348000, C065S118000

Reexamination Certificate

active

06772610

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to improvements made to flat glass annealing lehrs.
BACKGROUND OF THE INVENTION
It is known that flat glass annealing lehrs are tunnel furnaces, equipped with controlled heating and cooling means making it possible to cause the glass ribbon to follow a continuous cooling thermal cycle.
A lehr according to the current state of the art has been depicted schematically in
FIGS. 1 and 2
of the appended drawings:
FIG. 1
depicts the various zones that make up this lehr and the Curve of the glass annealing thermal cycle which results from it, and
FIG. 2
is a section on a longitudinal vertical plane of this lehr.
Referring to
FIGS. 1 and 2
, it can be seen that the zones of which the lehr is composed are generally defined as follows:
Zone AO: special inlet zone for particular treatment,
Zone A: pre-annealing zone,
Zone B: annealing zone,
Zone C: post-annealing zone,
Zone D: temperate direct cooling zone,
Zone F: final direct cooling zone.
Zones A, B and C are zones in which heat exchange is by radiation and zones D and F are cooling zones in which heat exchange is by convection.
The most critical phase in the cycle of annealing the glass ribbon is in zones A and B in which the glass is in a viscoelastic state allowing the stresses generated in the glass ribbon during the operations of forming it to relax. Poor control over the cooling of the glass ribbon in these zones can give rise to temperature gradients in the glass which will generate stresses which may remain in the form of residual stresses.
Referring to
FIG. 2
in which, in this lehr according to the prior art, only the heat exchangers situated above the glass ribbon
1
are depicted (the heating means and the exchangers which are situated beneath this glass ribbon are not depicted in this figure),
2
has been used to depict the system of mechanized rollers which supports and drives the glass ribbon
1
which passes through the lehr.
In zone A, a fan
4
draws in external air at ambient temperature, through a manifold
3
which supplies several groups of exchangers
5
covering the surface of the glass ribbon
1
. The exchanger
5
consists of a certain number of groups of tubes of circular, rectangular or some other cross section, arranged across the width of the glass ribbon so as to vary the cooling across the width of this ribbon. The air flow rate drawn into each group of exchanger tubes
5
is regulated via a series of valves such as
6
which are installed upstream or downstream of each group of exchanger tubes
5
and the degree of opening of which allows the cooling air flow rate to be adjusted according to the target temperature set at the end of the zone A.
In zone B, a fan
7
recirculates air through several groups of exchanger tubes
8
distributed across the width of the glass ribbon
1
. The temperature of the recirculated air in the groups of exchangers
8
can be adjusted by providing a hot air exhaust through the manifold
9
and by regulating some valves such as
10
and
11
which control the dilution of ambient air in the recirculated air. The air flow rate passing through each group of exchangers
8
can be adjusted via valves such as
12
which are installed upstream or downstream of each group of exchanger tubes
8
and the degree of opening of which allows the cooling air flow rate to be adjusted according to the target temperature fixed at the end of this zone B.
In zone C, a fan
14
draws in external air at ambient temperature through a manifold
17
which supplies several groups of exchanger tubes
16
covering the surface of the glass ribbon
1
. The air flow rate drawn into each group of exchangers
16
is regulated via a series of valves such as
13
installed upstream or downstream of each group of exchanger tubes
16
, according to the target temperature for the end of this zone C.
All the air temperatures and flow rates of air passing through the groups of exchangers in zones A, B and C are controlled by a regulating system operating each valve such as
6
,
10
,
11
,
12
and
13
, on the basis of information transmitted by temperature sensors which are installed at the end of each zone and across the width of the glass ribbon.
A study of
FIG. 2
reveals that the obligation for the ducts connecting the exchanger tubes where zones A and B and where zones B and C meet to pass through the roof of the lehr, the bulk of the valves such as
6
,
12
,
13
, and the need to provide means for compensating for the expansion of the exchanger tubes (not depicted in the figure), make it essential to separate the groups of exchangers of zones A, B and C by distances denoted by the references X and Y in FIG.
2
and known as inter-zone regions. The length of the inter-zone regions is generally of the order of 1.5 meters.
It can be seen that over the distance of the inter-zone regions x and Y, the glass strip is not subjected to the controlled radiation of the exchangers. It is therefore evident that its cooling is not controlled during the time needed for the glass ribbon to cover these inter-zone regions. In consequence, the temperature curve does not have an even profile while the glass ribbon is passing through these inter-zone regions X and Y. The glass, in these inter-zone regions, is at a temperature level which corresponds to a critical viscoelastic state. This non-uniformity of the glass ribbon cooling curve generates stresses in this glass which may remain right up to the end of cooling, in the form of residual stresses.
FIG. 3
of the appended drawings shows the temperatures of the glass ribbon and of the air passing through the exchanger tubes of zones A, B and C and over the length of the inter-zone regions X and Y. Curve
18
shows the change in glass ribbon skin temperature and curves
19
,
20
and
21
shows that of the temperature of the air passing through the exchanger tubes in each zone.
The glass ribbon skin temperature (curve
18
) decreases between the entries and exits of zones A, B and C:
In the case of Zone A: between points A and B;
In the case of Zone B: between points C and D;
In the case of Zone C: between points E and F.
A study of curves
19
,
20
and
21
shows that the temperature of the air passing through the exchanger tubes:
In the case of Zone A: increases between points J and K;
In the case of Zone B: increases between points M and L;
In the case of Zone C: increases between points O and N.
As the inter-zone regions X and Y are not controlled, an increase in the glass ribbon skin temperature occurs therein. These increases in temperature are represented by the curve
18
:
The inter-zone region for Zone A and Zone B, between the points B and C,
The inter-zone region for Zone B and Zone C, between the points D and E.
This lack of control over the heat exchange at the inter-zone regions X and Y disturbs the glass ribbon cooling curve in a range of temperatures that correspond to the viscoelastic domain, and this may give rise to the appearance of stresses, some of which will remain after total cooling, to the detriment of the quality of the glass produced.
It will be appreciated that the temperature difference of the glass in the inter-zone regions X and Y, for a given setting of the lehr, will vary according to the thickness of the glass ribbon or according to the speed at which it travels, which is dependent on the production of the line.
The present invention sets out to provide a solution to the technical problem mentioned hereinabove by eliminating the discontinuity in the glass ribbon annealing curve, which discontinuity is generated by the presence of the inter-zone regions X and Y in the lehrs according to the current state of the art, this being so as to improve appreciably the quality of the end product.
In consequence, the present invention relates to a flat glass annealing lehr equipped with controlled heating and cooling means comprising, in particular, pre-annealing, annealing, and post-annealing zones with heat exchange by radiation and temperature direct cooling zones and final direct cooli

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Flat glass annealing lehrs does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Flat glass annealing lehrs, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Flat glass annealing lehrs will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3313271

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.