ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of Invention
This invention relates to polyolefin compositions and more particularly to such compositions which are halogen-free and flame retardant, and to shaped articles made from them.
2. Background Discussion
Polyvinyl chloride (PVC) products have been on the market for many years and are commonly used in a large variety of applications. With the trend toward a chlorine-free environment, certain market segments such as the construction and wires and cables industries are in need of an alternative to PVC. Several halogen-free flame-retardant compounds are already available on the market but require difficult mixing processes. These compounds often need to be produced by specialized compounders, as the wire and cable and floor tile producers, themselves, often do not have the expertise.
For wire and cable applications, halogen-free flame-retardant materials are desirable to provide both insulation and jacketing in low-voltage cables in areas where it is necessary to avoid the generation of hazardous gases in the event of fire. Such areas where halogen-free low-voltage cables are useful include hotels, hospitals, schools, theaters and other such public spaces.
Important characteristics for jacketing materials is that they are highly flame retardant, good heat performance and good physical properties.
U.S. Pat. Nos. 4,948,669, 4,430,468, 4,434,258, 4,673,620, 4,701,359 disclose PVC-free compositions that are suitable for use as coatings for electrical cables. These compositions contain several components that are similar to those described herein, but lack, i.a., the terpolymer described herein.
SUMMARY OF THE INVENTION
According to the present invention there is provided a flame retardant, halogen-free polymer composition comprising a blend of
(1) ethylene vinyl acetate carbon monoxide terpolymer containing 30-90% by weight ethylene, 10-70% by weight vinyl acetate and 1-40% by weight carbon monoxide;
(2) an ethylene vinyl acetate or polyolefin selected from the group consisting of (a) ethylene vinyl acetate containing 25-90% by weight ethylene and 10-75% by weight vinyl acetate, (b) a linear low density polyethylene, (c) a low density polyethylene, (d) a very low density polyethylene and (d) a high density polyethylene; and mixtures thereof;
(3) an ethylene vinyl acetate or polyolefin selected from the group consisting of (a) ethylene vinyl acetate containing 25-90% by weight ethylene and 10-75% by weight vinyl acetate, (b) a linear low density polyethylene, (c) a low density polyethylene, (d) a very low density polyethylene and (d) a high density polyethylene; and mixtures thereof; each of which is grafted with 0.05-3% by weight of a carboxylic acid or an anhydride thereof; and
(4) an inorganic filler.
Common additives which may be included in the composition of the present invention include antioxidants, titanium dioxide (for UV resistance and to give a white color to the product), processing aids like zinc stearate and UV stabilizers.
DETAILED DESCRIPTION OF THE INVENTION
The present invention relates to flame retardant, halogen-free thermoplastic polymer blends which are useful in wire and cable coatings or in sheet form such as for use in floor tiles. These blends generally are formed by combining an ethylene vinyl acetate carbon monoxide (EVACO) terpolymer, an ethylene vinyl acetate (EVA) copolymer or polyolefin selected from EVA copolymer, a linear low density polyethylene, a low density polyethylene, a very low density polyethylene, a high density polyethylene and mixtures thereof, an ethylene vinyl acetate (EVA) copolymer or polyolefin selected from EVA copolymer, a linear low density polyethylene, a low density polyethylene, a very low density polyethylene, a high density polyethylene and mixtures thereof, each of which is grafted with a carboxylic acid or anhydride thereof, and an inorganic filler.
Polymer blends according to the present invention can be formed into wire and cable coatings or sheet form for uses such as for floor tiles, and have many properties comparable to polyvinyl chloride (PVC) containing blends, but are free from halogen.
Unless otherwise stated, percentage weight ranges for each of the components in the composition of the present invention are calculated exclusive of any additives which may be present.
The EVACO terpolymer (component (1)) useful in this invention preferably contains 30-90% by weight of ethylene, 10-70% by weight of vinyl acetate and 1-20% by weight of carbon monoxide, more preferably 55-65% by weight of ethylene and 20-30% by weight of vinyl acetate and 5-15% by weight carbon monoxide. In general, these EVACO's have a melt flow index (MFI) in the range of 1-50 g/10 min., preferably in the range of 10-40 g/10 min. as determined by ASTM D-1238 (measured at 2,16 kg and 190° C.) and are well-known in the art.
Component (1) preferably comprises 1-60% by weight of the composition of the present invention, more preferably 5-25% by weight, still more preferably 5-15% by weight.
The EVA copolymer when used as component (2) in this invention preferably contains 25-90% by weight of ethylene and 10-75% by weight of vinyl acetate, more preferably 55-75% by weight of ethylene and 15-30% by weight of vinyl acetate. In general, these EVA's have a melt flow index (MFI) in the range of 0.05-100 g/10 min., preferably less than 50 g/10 min. as determined by ASTM D-1238 (measured at 2,16 kg and 190° C.) and are well-known in the art.
The polyolefins when used as component (2) in general will have a melt flow index (MFI) in the range of 0.05-100 g/10 min., preferably less than 50 g/10 min. as determined by ASTM D-1238 (measured at 2,16 kg and 190° C.) and are well-known in the art.
Component (2) preferably comprises 1-50% by weight of the composition of the present invention, more preferably 5-25% by weight, still more preferably 10-20% by weight.
Component (3) is as defined as for component (2), but is further grafted with 0.05-3% by weight of a carboxylic acid or anhydride thereof, preferably maleic anhydride.
In general, component (3) will have a melt flow index (MFI) in the range of 0.05-100 g/10 min., preferably less than 20 g/10 min. as determined by ASTM D-1238 (measured at 2,16 kg and 190° C.).
Component (3) preferably comprises 1-40% by weight of the composition of the present invention, more preferably 1-15% by weight, still more preferably 3-10% by weight.
Component (4) is an inorganic filler. Suitable inorganic fillers are known in the art; preferred ones will also possess flame retardant characteristics. Specific, preferred inorganic fillers include aluminum trihydrate, magnesium hydroxide, calcium carbonate, calcinated clay, talcum, mica, zinc borates and mixtures thereof.
Component (4) preferably comprises 20-85% by weight of the composition of the present invention, more preferably 50-75% by weight, still more preferably 60-70% by weight.
The grafted moities of component (3) tend to react with the inorganic filler of component (4) (c.f. K. Hausmann,
V. Flaris, Polymers
&
Polymer Composites
Vol. 5, No 2, 1997 p 113 ff. This leads to further compatibilization of the composition. Compositions with higher levels of compatibilization have higher mechanical strength, which allow for higher levels of inorganic filler and thus, compositions with higher flame retardancy.
In addition to its polymer and flame retardant filler components, the composition of the present invention can be blended with common additives such as antioxidants, UV stabilizers, lubricants (e.g., oleamide), antiblocking agents, antistatic agents, waxes, pigments, titanium dioxide, talc and other processing aids (e.g., zinc stearate) known in the polymer compounding art. The additives may comprise up to about 10 weight percent of the total composition based on polymer components, flame retardant fillers plus additives.
The blends of the invention can be prepared by mixing the polymeric ingredients flame retardant fillers and optional additives by use of conventional masticating equipment, for example, a rubber mill, B

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Flame retardant polyolefin compositions does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Flame retardant polyolefin compositions, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Flame retardant polyolefin compositions will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3347871

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.