ABSTRACT:
FIELD OF THE INVENTION
This invention relates to a flame retardant glue composition for cellulosic material and more particularly to a glue for use in the manufacture of cellulosic fiber board with enhanced fire retardant properties.
BACKGROUND FOR THE INVENTION
Cellulosic materials such as paper, wood, cotton and the like are commonly used for household and commercial applications. Such materials are highly flammable and when ignited the fire spreads rapidly. Nevertheless, such materials are commonly used. Accordingly, a number of methods for treating such materials to reduce their flammability have been developed. However, such methods may be inadequate for today's standards, may prove too costly for the commercial market, provide too little protection against fire and smoke and result in products with other shortcomings.
The use of cellulosic products which are treated with fire retardant materials frequently involve human beings, who incorporate such products in a confined space as for example in a home, kitchen or other room. Therefore the products must provide a safe environment and at the same time provide a pleasing appearance particularly when the products are made of particle board. Therefore the use of volatile or harmful solvents should be minimized and preferably avoided.
It is also important to eliminate volatile or harmful solvents which could cause problems during a process for treating cellulosic material with a flame retardant agent. Further, it is important that any treatment minimizes the likelihood of chemical exuding from the processed material. It is also important that any chemical treatment should not produce or release toxic substances onto the surface of a product.
Conventional methods for treating cellulosic materials such as particle board and the like typically include the application of salts of phosphoric acid, boric acid etc. Other methods use various organic solvent systems. Both of such methods may be economical, but often result in crystallization of salts on the surface of a wood product. In addition, such methods may result in migration of undesirable chemicals to the surface of products made thereby. The solvents used are often volatile during the application of the flame retardants and exude from the finished products.
It has also been recognized that ammonium phosphates are among the more effective inorganic fire retardants which are commonly used to treat cellulosic materials. Such phosphates are typically present as diammonium phosphate, monoammonium phosphate or simple or complex mixtures of such phosphates. Fire retardants of this type are prepared by reacting aqueous phosphorous acid with an alkaline oxide such as ethylene oxide.
A more recent approach to provide a non-blooming fire retardant composition is disclosed in the U.S. Pat. No. 4,539,045 of Wagner. As disclosed therein, an ammonium phosphate-containing fire retardant includes an effective amount of boric acid or alkali metal borate. The ammonium phosphate-containing fire retardant comprises a reaction mixture of aqueous phosphoric acid and an alkylene oxide. Boric acid or alkali metal borate is present in an amount of from about 2.5 to about 12 percent by weight of solids.
It is now believed that there may be a large commercial demand for an improved fire retardant cellulosic products in accordance with the present invention. It is believed that this demand extends to a fire retardant particle board which has improved heat and flame resistance. A demand for an improved fire retardant cellulosic material is further supported by the products' enhanced properties. For example, such products do not include toxic substances and produce minimal smoke when exposed to heat and/or open flame. Accordingly, there is no harmful vapor or toxic substance to deal with during the manufacturing process.
In addition, products in accordance with the present invention do not exude toxic substances during or after manufacture or when exposed to high temperatures and/or open flame. Further the chemicals incorporated do not migrate to the surfaces or result in unsightly blemishes. Finally it is believed that the products as disclosed herein can be manufactured in a cost effective manner and brought to market at a competitive price.
BRIEF SUMMARY OF THE INVENTION
In essence, the present invention contemplates a flame retardant glue for use in the manufacture of cellulosic particle board with enhanced flame retardant properties. The glue comprises a resin selected from the group consisting of urea formaldehyde resin and phenolic resin and mixtures thereof as a major component. The glue also contains water, monoammonium phosphate and diammonium phosphates in equal molar amounts.
In a preferred embodiment of the invention, the composition contains between about 54 and 66 percent by weight water, about 33 to about 39 percent by weight of a urea formaldehyde resin, phenolic resin or mixture thereof. The composition also includes between about 1.5 and about 2.5 weight percent monoammonium phosphate and between about 1.5 and about 2.5 weight percent diammonium phosphate wherein the monoammonium and diammonium phosphates are present in equal molar amounts. A small amount of a metal hydroxide such as aluminum hydroxide may also be added.
The invention will now be described in connection with the accompanying drawings.
REFERENCES:
patent: 4126473 (1978-11-01), Sobolev
patent: 4595414 (1986-06-01), Shutt
patent: 6042639 (2000-03-01), Valsö{umlaut over ( )}et al.
patent: 85107788 (1987-05-01), None
patent: 48021346 (1973-06-01), None
Cool Dot Ltd.
Dennison, Schultz & Dougherty
Toomer Cephia D.
LandOfFree
Flame retardant glue composition and method for making the same does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Flame retardant glue composition and method for making the same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Flame retardant glue composition and method for making the same will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3107009