Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Treating polymer containing material or treating a solid...
Reexamination Certificate
2000-06-06
2002-07-16
Teskin, Fred (Department: 1713)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Treating polymer containing material or treating a solid...
C528S481000, C528S503000, C526S065000, C526S067000, C526S068000, C526S070000, C159S047100
Reexamination Certificate
active
06420516
ABSTRACT:
The present invention relates to polymerization of olefins in a solution process. More specifically, the invention relates to recovery techniques for removing the polymer products from the polymer solution.
Solution polymerization of monomers containing ethylenic unsaturation is used to prepare many polymers, including polyethylene, polypropylene and a variety of copolymers. Existing solution polymerization units were designed and constructed at a time when catalyst activity was low compared to currently available catalysts. Many such polymerization units were originally designed to have adequate polymer recovery units for each reactor, or each series of reactor stages, based on the polymer yields from catalysts available at the time. Ziegler-Natta catalysts, such as those described in U.S. Pat. Nos. 4,314,912, 4,250,288, 4,319,011, and 4,547,475, provide higher yields of improved polymers such as DOWLEX™ linear low density polyethylene (LLDPE) polymers, which are available from The Dow Chemical Company.
Polymer recovery units are known in the prior art. U.S. Pat. No. 4,686,279 (equivalent to EP-A-0 102 122) discloses a device on a process of recovering polymer from solution. In particular, solutions obtained from the polymerization of ethylene, with or without one or more &agr;-olefins having at least three carbon aroms, can be directly fed into the evaporating zone of the device. The melted polymer mass is then passed on to an extruder and a resulting polymer melt may be obtained whose content of volatile components may be lower than 500 parts per million.
Another polymer recovery design is taught in German patent DE-A-21-16-939 wherein a solution obtained from the polymerization of ethylene is heated, flashed to concentrate the solution, reheated, and fed into a finishing device.
Conversion of the solution polymerization process from using Ziegler-Natta catalysts to more advanced catalysts may not increase polymer production rates because of the limited capacity of the polymer recovery units. Absent additional polymer recovery units, the solution polymerization units must be operated below reactor capacity. Furthermore, the cost of an additional polymer recovery unit may not be justified in a competitive market.
Considerable research has been devoted to improving the profitability of existing solution polymerization units by providing more controllable catalysts to produce more valuable ploymers. For example, the single site constrained geometry catalysts described in U.S. Pat. Nos. 5,470,933, 5,556,928, and 5,512,693 provide polymers having substantially improved properties. Success with new catalysts can improve profitability of existing solution polymerization units. However, it would be desired to enjoy the higher activity of the catalysts without adding additional polymer recovery units.
An existing solution polymerization unit for making polyolefins, e.g., ethylene homopolymers and interpolymers, propylene homopolymers and interpolymers, etc., is shown in
FIG. 1
(Prior Art). While
FIG. 1
may be applied to other polyelefins, for simplicity it is discussed herein with respect to polyethylene. The existing unit includes a first stage continuous stirred tank reactor (CSTR)
10
and a second stage CSTR
12
. Raw materials, including solvent, ethylene, 1-octene, trace amounts of hydrogen, and catalyst, are fed to the first stage reactor
10
through one or more feed lines
14
. An interim polymer solution produced in the first stage reactor
10
then passes from the first reactor
10
to the second reactor
12
through a connecting line
16
. The interim polymer solution typically has a temperature below about 200° C. and a polymer content from 3 percent to 16 percent by weight.
The polymer solution from the second stage reactor
12
typically has a temperature below about 220° C. and a polymer content from 3 percent to 24 percent by weight. The polymer typically comprises polyethylene or copolymers of ethylene and other &agr;-olefin monomers. A second feed line
18
optionally feeds raw materials, for example, ethylene, &agr;-olefin, solvent, hydrogen, etc., to the second stage reactor
12
to raise the polydispersity of the polymer product. The weight average molecular weight of the polymer ranges from 2,000 to 1,000,000, occasionally more, and, typically, in the case of polyethylene, 2,000 to 500,000. The polydispersity of the polyethylene ranges from 1.5 to 10.0.
The polymer solution from the second stage reactor
12
flows through a discharge line
20
to a first stage heat exchanger
22
, and then flows through an entry line
24
to a first stage polymer finishing unit such as a devolatilization vessel
26
. A polymer product exits the devolatilization vessel
26
through a product line
30
and gaseous monomer and vapor exit the vessel
26
through a recycle line
28
. Devolatilization could occur in one or more stages although only a single stage is shown in the drawings. Alternatively, polymer recovery could be achieved by one or more hot water washes. Prior to entering the heat exchanger
22
, the polymer solution is heated only by the exothermic polymerization reaction, that is the heat of polymerization. Heating and devolatilization of the polymer solution during polymer recovery can be done in one or more stages to maintain the polymer temperature below 260° C.
To minimize polymer degradation which leads to gel formation, the polymer temperature exiting the devolatilization vessel
26
is preferably less than 200° C. Furthermore, unreacted raw materials exiting the devolatilization vessel
26
through the recycle line
28
must be cooled for recycling.
Using Ziegler-Natta catalysts, such as TiCl
3
/MgCl
2
catalysts, in the solution polymerization unit of
FIG. 1
, results in increased polymer yield until the heat exchangers
22
run at maximum capacity for polymer recovery. Additional heat exchangers could be added, however, additional cooling would also be required for cooling of recycled raw materials. Moreover, the polymer would have to be heated to higher temperatures or remain at high temperatures for a longer period of time, and would result in greater polymer degradation.
Replacing Ziegler-Natta catalysts with metallocene catalysts or constrained geometry catalysts in the solution polymerization unit of
FIG. 1
improves profitability of the unit by making a more valuable product although at a lower yield than could be achieved with the Ziegler-Natta catalysts. However, the yield remains high in comparison to original design criteria such that the heat exchangers
22
still run at maximum capacity and are still a bottleneck in the process. Thus, profitability could be further improved by increasing polymer recovery capacity to match increases in polymer production capacity.
Therefore, there is a need for an improvement to existing solution polymerization units which provides for increased polymer recovery capacity to increase reactor utilization. Ideally, the improvement would increase the energy efficiency of the process without requiring a substantial redesign of the polymer recovery units. It would be desirable if such an improvement could be retrofitted with minimum capital cost or included in future construction of this and other solution polymerization units.
The present invention improves the polymer recovery capacity of solution polymerization units by flashing a polymer solution exiting polymerization reactors to produce a concentrated polymer solution having a reduced temperature and a polymer content from 10 percent to 40 percent by weight. The concentrated polymer solution can be prepared without the addition of thermal energy and can be devolatilized in conventional polymer recovery units without increasing the risk of gel formation.
One aspect of the invention provides a solution polyolefin process, comprising the steps of: polymerizing one or more olefins in a sufficient amount of solvent to produce a polymer solution having a polymer content from 3 percent to 24 percent by weight, preferably 6 percent to 18 percent by weight, wherei
Jain Pradeep
Kao Che-I
Swindoll Robert O.
Tau Li-Min
Teskin Fred
The Dow Chemical Company
LandOfFree
Finishing design to increase the polymer content in an... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Finishing design to increase the polymer content in an..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Finishing design to increase the polymer content in an... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2910864