Filter media

Details Filter media Filter media

2000-10-27

2003-04-29

Simmons, David A. (Department: 1724)

Gas separation

Specific media material

Fibrous or strand form

C156S062400, C156S062600, C156S062800, C264SDIG004, C055SDIG003, C428S219000, C428S311110, C428S311510, C428S315500, C428S338000, C428S359000, C428S364000, C428S373000

Reexamination Certificate

active

06554881

ABSTRACT:

FIELD OF THE INVENTION
This invention relates generally to air filters, and more specifically to a non-woven filter composite and a method for forming the composite.
BACKGROUND OF THE INVENTION
The removal of air borne contaminants from the air is a concern to everyone. Gas phase filtration has traditionally been accomplished by methods which utilize activated carbon. One approach has been to use a carbon/adhesive slurry to glue the carbon to a substrate. However, the adhesive decreases carbon performance by forming a film on its surface. A second approach involves carbonizing an organic based web by heating, followed by carbon activation. This material has a high cost and has relatively low adsorption capacity. A third approach involves forming a slurry of carbon powders and fibers into sheets by a process analogous to a wet papermaking process. This material is medium-to-high cost, and has an undesirable high pressure drop.
Alternatively, carbon particles have been treated with chemicals to increase uptake of air contaminants. However, chemical treatment is not efficient when used in conjunction with an aqueous process, as the aqueous nature of the process either washes away the chemical used to impregnate the carbon, or reacts undesirably with the impregnating chemical rendering it useless. However, filter materials which do not incorporate chemical absorbents into the carbon particles perform far less effectively than those which do include chemically impregnated absorbents.
Another approach to entrain air contamination has been to produce low, medium and high efficiency pleatable composite filter media which include either a low, medium or high efficiency fibrous filtration layer of randomly oriented fibers; and one or more permeable stiffening layers which enable the composite filter media to be pleated and to sustain its shape. Such filtration devices serve as vehicle passenger compartment air filters, high performance engine air filters and engine oil filters. ASHRAE (American Society of Heating Refrigeration and Air Conditioning Engineers) pleatable filters and the like typically use a pleated high efficiency filtration media for the filtration element.
Currently, the pleated high efficiency media normally used in these filtration devices are made from ASHRAE filter media or paper products. These paper products are made by a wet-laid technique wherein fibers, e.g. glass or cellulosic fibers, are dispersed in an aqueous binder slurry which is stirred to cause the fibers to become thoroughly and randomly mixed with each other. The fibers are then deposited from the aqueous binder slurry onto a conventional paper making screen or wire as in a Fourdrinier machine or a Rotoformer machine to form a matted paper which includes a binder resin, e.g., a phenolic resin. Pleated filter elements made from such papers can exhibit high efficiencies. However, these pleated filter elements have low dirt-holding capacities and exhibit high pressure drops.
Electrostatically charged synthetic filter media is also used in these filtering applications, and these can attain very high filtration versus pressure drop performance characteristics, at least in their initial charge state. However, during use many of these products lose their electrostatic charge, or it is masked by deposits, causing filtration efficiency to drop substantially, sometimes to levels below what is acceptable.
Accordingly, there remains a need to provide a relatively low cost, high efficiency filter media for these filtration applications which exhibit relatively high dirt-holding and/or air contaminant capacities and relatively low pressure drops as well as low and medium efficiency filter media which exhibit relatively high dirt-holding capacities and relatively low pressure drops.
SUMMARY OF THE INVENTION
The present invention circumvents the problems described above by providing fiber webs and filter composites which retain particles, air borne contaminants, and/or oil without reduction in filtration performance below a high base threshold even after prolonged filtration challenges. In a particular embodiment, the filter media of the present invention is a polymeric fiber web having a fine fiber layer on a coarser support, and which, after decay of any charge which may be present, possesses an alpha above about 11, i.e. 13 or 14. The web can include an antioxidant within the web matrix. Accordingly, the present invention provides filter media, useful in filtering applications such as air conditioning, ventilation and exhaust ducts as bag filters or pleated panel filters, which relies upon mechanical filtration properties rather than electrostatic charge for its base level of filtration efficiency, thus providing filter media which have enhanced filtration performance characteristics, such as efficiency versus pressure drop characteristics over time.
The present invention comprises a cost effective, high efficiency, low pressure drop, adsorptive, non-woven filter media comprising a high surface area synthetic microfiber, e.g., melt blown, fine fiber layer. The filter media can also include one or more non-woven spun bond layers and can be combined with a coarse fiber support layer. The coarse fiber support layer can itself be a low pressure drop synthetic microfiber, e.g., melt blown, layer adhered to a spun bond layer, and can serve as a prefilter to enhance overall performance. The invention also contemplates a method for forming the filter media comprising dry application of the non-woven fine fiber filter media to the non-woven carrier material. Various layers can be calendared, and the complete multilayer web assembled with heat, with or without a cover sheet.
In one exemplary method of manufacture, a polypropylene resin is extruded by a melt pump through a die having a plurality of extrusion holes to produce large diameter fibers into a stream of hot air which stretches the fibers to a diameter well below several microns and carries them toward a collector belt passing over a vacuum box opposite the extrusion head. Preferably a spun bond mat or web is carried by the collector belt so that the melt-blown fine fibers land on and accumulate on the spun bond layer to produce a large area matrix of filtration material on a support. This material can be used directly on a suitable structural support, or can be further bonded to another layer of course non-woven fibrous support material to form a large area filter media suitable for a variety of commercial uses. Alternatively, the synthetic microfiber fine fibers can be used alone, and the web carried on the collector belt is used only to collect the blown fibers. The synthetic microfiber fine fibers of the invention have an alpha value of at least about 11 or more, i.e., 13 or 14. In a particularly preferred embodiment, the synthetic microfiber fine fibers have an alpha value which remains constant or stable over time. The synthetic microfiber fine fiber web can be calendered to enhance fiber entanglement. In a preferred embodiment, the synthetic microfiber is a melt blown fiber.
In one embodiment, the present invention pertains to filter media which include an effective filtration layer of synthetic microfiber which need not be charged. The actual diameter of the fibers of the synthetic microfiber material is between about 0.8 to about 1.5 microns, i.e. 1.0 microns, as measured by scanning electron microscopy, and in a preferred embodiment, the synthetic microfiber, e.g., melt blown, polymeric material is a polypropylene, e.g., Exxon PP3456G (Exxon, Houston, Tex.) having a melt flow of about 1200, which contains an antioxidant. Preferably the fine fiber has a web basis weight of between about 6 g/m
2
and about 25 g/m
2
, and is generally applied over a coarser support or strengthening layer of low solids such that the web has an alpha value of at least about 11 or more, i.e., 13 or 14. The synthetic microfiber fine fibers of the invention have a 60-65% ASHRAE (at a basis weight of about 6 to about 12 g/m
2
, e.g., 8 g/m
2
), 80-85% ASHRAE (at a basis weight of a

Affiliated with

Also associated with

Rating

Filter media does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Filter media, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Filter media will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3072646