Stock material or miscellaneous articles – Layer or component removable to expose adhesive – Release layer
Reexamination Certificate
1999-09-09
2002-12-17
Ahmad, Nasser (Department: 1772)
Stock material or miscellaneous articles
Layer or component removable to expose adhesive
Release layer
C428S040100, C428S042100, C428S042200, C428S192000, C428S194000, C602S054000, C602S055000, C602S058000, C602S059000, C602S077000
Reexamination Certificate
active
06495230
ABSTRACT:
BACKGROUND OF THE INVENTION
The invention relates to a film-based bandage material which is treated so as to be self-adhesive on one side and formed onto which there is at least one non-adhesive grip tab.
Adhesively coated backing systems which de-adhere when the backing is pulled are known. They are generally based on elastic systems, which in many cases constitute laminates.
DE-A 27 28 346 describes an adhesive tape of this kind which consists of an extensible film and an adhesive composition based on A-B-A block copolymers. The completely adhering laminate can easily be detached from the substrate by stretching. The adhesive composition is applied over the whole area. No grip tab is provided for stretching the bonded tape.
DE-A 195 31 696 describes an adhesive-tape laminate which is produced from an extensible backing and an acrylate adhesive composition.
WO 95/06691 discloses a redetachable adhesive tape whose backing material comprises a foam.
WO 92/11333 describes a system which can be removed nondestructively and which possesses a high tensile strength.
DE 40 26 755 A1 discloses a film-based bandage material which is covered on one side with a support material which is the same size as the film and has at least one grip strip, and on the other side is provided with a self-adhesive layer. The grip strips for removing the backing material are arranged within its peripheral limits. Preferably, only one grip strip is attached to the backing material.
DE 43 14 834 C2 discloses a film-based bandage material which is covered on one side with a backing material which is the same size as the film and has at least one grip strip, and on the other side is provided with a self-adhesive layer. The grip strips for removing the backing material are arranged within its peripheral limits. Preferably, only one grip strip is attached to the backing material.
With both of the abovementioned bandages the problem arises, following application, of how to detach them from the skin, since they are bonded over their entire area. The patient is therefore forced to lift up a section of the film in the marginal region from the skin by inserting a fingernail, for example, under the film. This procedure firstly is very unsatisfactory and secondly can be painful, especially in the case of relatively large wounds and the irritated skin that accompanies them.
EP 0 747 027 A2 discloses an adhesive tape section consisting of an adhesive composition lined on one side with a thin cover film. On the opposite side there are two further sections of a film on the adhesive composition, so producing, in the marginal region, two grip tabs by means of which the adhesive tape section can be detached from the substrate by pulling in the bond plane.
The object of the invention is to avoid the disadvantages known from the prior art and to provide a film-based bandage material which is treated so as to be self-adhesive on one side and which can be detached again from the skin, following application, easily and painlessly by stretching.
This object is achieved by a film-based bandage material as set out in the main claim. The subclaims relate to advantageous developments of the bandage material.
SUMMARY OF THE INVENTION
Accordingly, the invention proposes a film-based bandage material in which the film is comprised of polyurethane, is treated so as to be self-adhesive on one side and has at least one non-adhesive grip tab formed onto it, so that following application the bandage material can be detached from the substrate by pulling on the grip tab in the direction of the bond plane.
The bandage film itself is comprised of elastic, thermoplastic polyurethanes, as described in DE-C 19 34 710 (=U.S. Pat. No. 3,645,835), which feature good skin compatibility and also permeability to oxygen and water vapour. Aliphatic polyester urethanes have proved to be particularly advantageous.
A preferred film is about 30 to 40 &mgr;m thick, transparent, has an elongation at break of more than 450% and a water vapour permeability of more than 500 g/m
2
in 24 h at 38° C. and 95% relative humidity in accordance with DAB [German Pharmacopoeia].
The thickness of this film can be from about 15 to 300, preferably from 15 to 80 &mgr;m, the weight, accordingly, from about 15 to 350 g/m
2
, preferably from 15 to 100 g/m
2
, the maximum tensile force in the longitudinal direction from about 5 to 100 N/cm, preferably from 2 to 40 N/cm, and the elongation at break in the longitudinal direction from about 100 to 1000%.
The adhesion of the film to the backing material, which need only be low (from about 0.01 to 0.5 N/cm, preferably from 0.01 to 0.05 N/cm), is preferably brought about by producing the thin film directly on the backing by casting, knifecoating, extrusion or other known methods of producing films. If necessary, the backing material can be roughened on the coating side or given some other adhesion-promoting treatment. An adhesion-promoting coating may also be advantageous.
What is important in this context is that the adhesion of the finished bandage to the skin is substantially stronger than the adhesion of the backing to the film.
The grip tabs are present, in particular, at the marginal region of the film, so as not to complicate further the production of the bandage material. Preferably, only one grip tab is present. By pulling on the grip tab essentially in the direction of the bond plane, the film becomes stretched and at the same time detaches itself from the underlying skin with, surprisingly, no pain.
In order to minimize the amount of sealing paper and/or other packaging material employed in the case of individual punched plasters, the grip tab can be folded so that it lies on the side of the film that is not coated with the adhesive.
In one preferred embodiment the film is covered on one side with a backing material which has the same size as the film and possesses at least one grip strip.
The backing material, which has a supporting action for the film, remains on the film during application of the bandage and is not removed until afterwards; it is preferably comprised of a polyethylene film about 80 &mgr;m thick which is slightly roughened on its side facing the film and thus has a matt but still translucent appearance.
It is also possible to use other films made, for example, of polypropylene, polyester of PVC, or suitable thin, coated paper, so long as they are sufficiently pliable not to interfere during application of the bandage.
Their technical data can be within the following ranges:
Thickness:
30-300 &mgr;m
Weight:
30-350 g/m
2
Maximum tensile force, longitudinal:
5-100 N/cm
Elongation at break, longitudinal:
10-3000%
Their surface facing the film can be smooth, roughened or slightly embossed.
The grip strips are preferably comprised of an LDPE (low-density polyethylene) film 80 &mgr;m thick. So as to be easily visible, it is coloured—blue, for example—and for improved grip is provided with matt embossing on the outside.
Instead of this film, it is also possible to use other materials, such as HDPE, polypropylene, PVC, PU or polyester films, and also nonwovens, paper or wovens, so long as they are again sufficiently flexible and pliable.
Depending on the material, the thickness can be between 10 and 300 &mgr;m, the weight, accordingly, from 10 to 350 g/m
2
. The surface can be matt, glossy, rough, smooth or printed. The maximum tensile force in the longitudinal direction can vary between about 3 and 100 N/cm and the resultant elongation can be between 5 and 500%.
The grip strips can be attached to the backing material in a wide variety of ways depending on the material and processing machines, but preferably by adhesive bonding or welding. Adhesive bonding takes place, for example, by introducing a strip of a double-sided adhesive tape between the backing material and the grip strips in the region to be bonded, or a coating of adhesive composition consisting of a hot-melt or self-adhesive composition of a solvent or dispersion.
The grip strips may extend over the entire length or width of the
Ahmad Nasser
Beiersdorf AG
Norris & McLaughlin & Marcus
LandOfFree
Film-based bandage material does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Film-based bandage material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Film-based bandage material will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2926357