Compositions: coating or plastic – Coating or plastic compositions – Dental
Reexamination Certificate
1999-06-10
2001-08-07
Koslow, C. Melissa (Department: 1755)
Compositions: coating or plastic
Coating or plastic compositions
Dental
C106S400000, C106S485000, C428S372000, C428S378000, C428S300100, C523S115000, C523S200000, C523S202000, C523S216000, C523S217000, C523S220000, C523S221000, C433S201100, C433S212100, C433S222100, C433S223000
Reexamination Certificate
active
06270562
ABSTRACT:
TECHNICAL FIELD
The present invention relates generally to filler materials and methods of manufacture thereof and more specifically to filler materials for use in dental composite materials.
BACKGROUND OF THE INVENTION
Compositions useful for repairing damaged teeth in situ are known in the art as direct filling materials, and include alloys and resin composites. Dental amalgam alloys have widely been used as direct filling material, and provide excellent handling characteristics, and physical properties. The technique of mechanically packing and condensing a material into a tooth cavity is previously known to the dental profession in connection with the use of dental amalgams as a direct filling material. It has well known advantages in that it permits a close adaptation of the filling material to the cavity walls and also makes it possible to make firm contacts between the restored tooth and its neighbor. Further, it makes it possible to give the restoration its final anatomic form before hardening, thereby avoiding the time consuming and difficult finishing work with rotating instruments required with composite materials. However, there are perceived health hazard concerns regarding the use of high amounts of mercury or gallium present in amalgam alloys.
Dental resins have accordingly been developed, which comprise polymeric matrices, for example polyamides, polyesters, acrylates, polyolefins, polyimides, polyarylates, polyurethanes, vinyl esters, or epoxy-based materials. Other polymeric matrices include styrenes, styrene acrylonitriles, ABS polymers, polysulfones, polyacetals, polycarbonates, polyphenylene sulfides, and the like. The most popular polymeric matrices are based on monomers having at least one ethylenically unsaturated group, in particular acrylate and methacrylate groups. One commonly used monomer of this class is the reaction product of bisphenol A with glycidyl methacrylate (hereinafter BIS-GMA). In addition, these resins have also been used to make artificial teeth and denture bases.
Unfilled (i.e., pure) curable acrylic and methacrylic resins generally suffer from polymerization shrinkage and poor durability. These drawbacks have been reduced in direct filling applications, in part, through the addition of inert fillers. See, for example, U.S. Pat. No. 3,066,112 which is herein incorporated by reference. The combination of binder plus filler is commonly referred to as a composite direct filling material. Currently used fillers for curable dental resins generally are inert materials in the form of finely divided irregular particles, fibers or beads, present in an amount from about 35 to about 80 percent by weight of the total composite direct filling material.
Commonly used inorganic fillers include fumed silica, quartz, glass, various mineral silicates (e.g., B-eucryptite, lepidolite, petalite, spondumene, beryl, topaz and zircon), silicon carbide, alumina, and mixtures thereof Commonly-assigned U.S. Pat. No. 4,544,359 to Waknine, for example, discloses a filler mixture comprising barium silicate, borosilicate glass, and colloidal silica. In general composite direct filling materials which are fully loaded with inorganic fillers (i.e. combined with the highest workable volume loading) having particles in the range of 0.01-1.2 microns are the most wear-resistant currently available composite direct filling materials. However, these composite direct filling materials containing finely divided inorganic fillers and acrylic binder resins may not polish as easily as unfilled dental resin.
U.S. Pat. No. 5,707,440 to Hengchang et al. is directed to finely divided inorganic filler comprising macro-filler particles and micro-filler particles. Each macro-filler particle has a number of micro-filler particles covering it and connected to it by sintering. In addition to mixing and sintering the macro-filler and micro-filler particles together, the method of making the filler mixture requires dispersing the resultant mixture in a liquid and using ultrasonic waves to separate the coarser particles to settle from the dispersion, and centrifuging the dispersion to claim the finely divided inorganic filler. A commercial product comprising filler based on this technology is available from Heraeus Kulzer GmbH under the name Solitare.
Organic materials have also been used as fillers. For example, U.S. Pat. No. 3,923,740 discloses a direct filling material containing finely divided cured polymethyl methacrylate, alone or in conjunction with an inorganic filler. Composite direct filling materials which are wholly or partly filled with finely divided polymethyl methacrylate have better polishability (i.e. better surface finish after polishing with ordinary dental tools) than composite direct filling materials which are fully loaded with inorganic fillers, but generally have poorer durability (i.e. poorer wear resistance in vivo) than composite direct filling materials having inorganic fillers only.
Regarding fibrous fillers in particular, U.S. Pat. No. 2,477,268 to Saffir discloses short glass fibers randomly dispersed in dental resin materials, as does U.S. Pat. No. 2,514,076 to Kelly. Use of long, fully wetted fibers in structural components for dental restorations and the like are disclosed in U.S. Pat. No. 4,894,102 to Goldberg et al. However, none of these patents discloses a composite having the feel of amalgam.
Fused-fibrous filler compositions in the dental arts are also known. Such fused fibrous fillers are of particular interest because they reportedly provide a feel similar to that of amalgam when used by the dentist, and may be applied using similar techniques. In U.S. Pat. Nos. 4,381,918 and No. 4,392,828 to Ehlnford there is disclosed a filler comprising porous inorganic particles which are completely or partially impregnated with a resin material. The porous inorganic particles are formed by heating inorganic fibers under pressure to fuse the fibers at their points of contact, thereby forming a rigid three-dimensional network of inorganic fibers. Fused-fibrous filler compositions are also disclosed in U.S. Pat. No. 5,621,035 to Lyles et al. Such fillers comprise silica fibers together with either alumina or aluminosilicate fibers which are fused in the presence of a fusion source such as boron nitride. The presence of boron lowers the melting point of the fibers sufficiently to allow formation of a porous, interconnected network. The network is then ground to particles having a size of about 180 microns, and used as fillers in dental composites. Unfortunately, use of the aforementioned fused-fibrous filler compositions requires multiple steps and extensive preparation time.
Accordingly, there is a need in the dental arts to develop a dental resin composite which is similar to or approaching dental amalgam alloys in handling characteristics, physical properties, and applications without the drawbacks and deficiencies associated with dental amalgam alloys, and without the multiple preparation steps required for fused-fibrous compositions.
SUMMARY OF THE INVENTION
These and other objects and advantages are accomplished by the composition and method of manufacture of the present invention directed to a filler material comprising a fibrous material and one or more forms of surface-modifying particles. The surface-modifying particles are bonded to the fibrous material to increase the surface area of the fibrous material and improve the bonding properties of the fibrous material to enable it to better bond to a resin matrix material in a dental composite. In accordance with the present invention, the fibrous material possesses a lower melting temperature than the surface-modifying particles. The surface-modifying particles and the fibrous material are heated to a temperature below the softening temperature of the fibrous material but at a temperature and time sufficient to soften the surface of the fibrous material in order to chemically bond the surface-modifying particles thereto.
The resulting filler material can be used in dental composites and dental restoration
Jeneric/Pentron Inc.
Knab Ann M.
Koslow C. Melissa
LandOfFree
Filler material for dental composites does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Filler material for dental composites, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Filler material for dental composites will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2500787