Optical waveguides – With optical coupler – Input/output coupler
Reexamination Certificate
1996-09-30
2001-02-27
Bovernick, Rodney (Department: 2874)
Optical waveguides
With optical coupler
Input/output coupler
C385S049000, C385S050000, C065S441000, C359S566000
Reexamination Certificate
active
06195483
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to fiber Bragg gratings and more particularly to a method of writing fiber Bragg gratings in infrared transmitting chalcogenide-based or chalcohalide-based fibers.
2. Description of Related Art
Since the discovery and description of photodarkening in chalcogenide glasses in 1971 by Berkes et al. (“Photodecomposition of Amorphous As
2
Se
3
and As
2
S
3
”, J. Appl. Phys.
Vol. 42, No. 12, pp. 4908-4916, November 1971), much effort has been put forth to understand the detailed mechanisms of this effect. Sulfide based chalcogenide glass, specifically arsenic sulfide (As
2
S
3
), exhibits a wealth of interesting permanent and reversible photoinduced changes when illuminated with light that has an energy near the Tauc gap of 2.3 eV. These changes include photodarkening, and photoinduced birefringence and dichroism. Photodarkening is discussed in “Mechanisms of Photodarkening in Amorphous Chalcogenides”, K. Tanaka,
Journal of Non
-
Crystalline Solids,
Vol. 59-60, Part II, pp 925-928, (1983). Photoinduced birefringence and dichroism are discussed at greater length in “Photoinduced Optical Anisotropy in Chalcogenide Vitreous Semiconducting Films”, V. G. Zhdanov et al.,
Physica Status Solidi
(
a
), Vol.52, No. 1, pp 621-626, (March 1979) and in “Anisotropy of Photoinduced Light-Scattering in Glassy As
2
S
3
”, V. Lyubin et al.,
Journal of Non
-
Crystalline Solids,
Vols. 164-166, pp 1165-1168, North-Holland (1993).
Although a unified theoretical microscopic description of these effects is not complete, it is believed that photodarkening is produced as carriers break As—S bonds when they recombine, causing an increase in As—As and S—S bonding, which in turn causes a lowering of the band-gap energy by as much as 0.05 eV at room temperature. (See “The Origin of Photo-Induced Optical Anisotrophies in Chalcogenide Glasses”, H. Fritzsche,
Journal of Non
-
Crystalline Solids,
Vols. 164-166, pp. 1169-1172, North-Holland, 1993.) Since only a finite number of As—S bonds have a local environment which allows this process to happen, the effect saturates with total illumination energy. Regardless of the model, however, these effects are experimentally well characterized: the total refractive index change at 600 nm is about 0.01. (See “Photodarkening Profiles and Kinetics in Chalcogenide Glasses”, S. Ducharme et al.,
Physical Review B,
Vol. 41, No.17, pp. 12 250-12 259, Jun. 15, 1990.) A simple Kramers-Kronig analysis predicts that this index change will decrease linearly with photon energy in the transparent region of the glass, thus allowing large amplitudes (&Dgr;n~10
−3
) to be induced in the infrared.
The technique of side writing fiber Bragg gratings in germanium-doped silica fibers is well established and was first described by Meltz, et al. (“Formation of Bragg Gratings in Optical Fibers By A Transverse Holographic Method”,
Optics Letters,
Vol. 14, No. 15, pp 823-825, August 1989.) Two “writing” beams are crossed at some angle &thgr;, with the intersection point coinciding with the core of the silica fiber. The crossed beams form an intensity grating along the axis of the fiber with period &Lgr;=&lgr;
W
/(2 sin &thgr;), where &lgr;
W
is the wavelength and &thgr; is the half-angle between the writing beams, respectively. The writing beams change an absorption line due to the germanium doping of the core, causing a change &Dgr;n in the index of refraction n at lower photon energies. The index change amplitude is around &Dgr;n~10
−5
-10
−6
for silica glass. This grating forms a Bragg reflector at the vacuum wavelength &lgr;
B
for light launched down the core of the fiber at &lgr;
B
=2n&Lgr;. The “photonic band gap” energy, &Dgr;v
B
, which corresponds to the full-width of the reflectance between the first two zeros of the reflectivity, is &Dgr;v
B
/v
B
=&Dgr;n
where V
B
=c/&lgr;
B
and c is the speed of light. See “Propagation Through Nonuniform Grating Structures”, J. E. Sipe et al.,
J. Opt. Soc. Am. A,
Vol. 11, No. 4, pp. 1307-1320 (April 1994).
It has been previously demonstrated by Shiramine et al. (“Photoinduced Bragg Reflector In As
2
S
3
Glass”,
Appl. Phys. Lett.,
Vol. 64 (14), pp 1771-1773, Apr. 4, 1994) that Hill gratings may be written in As
2
S
3
glass flakes. Hill gratings are formed from absorption of the peaks of the standing wave produced by multiple reflections from parallel end-surfaces. (See “Photosensitivity In Optical Fiber Waveguides: Application To Reflection Filter Fabrication”, K. C. Hill et al.,
Appl. Phys. Lett.,
Vol. 32 (10), pp. 647-649, May 15, 1978.) The period of the standing wave sets the Bragg reflection condition, which gives a reflection maximum at the wavelength of the writing beam. Since the energy of the writing beam needs to be near the Tauc gap in order to photoinduce carriers, Hill gratings will not be useful at infrared wavelengths which are not significantly absorbed in the material.
SUMMARY OF THE INVENTION
It is therefore an object of the invention to provide variable-bandwidth, high reflectance fiber Bragg gratings for mid-infrared integrated optics applications.
Another object of the invention is to write reflective Bragg gratings into infrared transmitting fibers.
Another object of the invention is to side write fiber Bragg gratings into infrared transmitting fibers.
Another object of the invention is to provide fiber Bragg gratings in chalcogenide or chalcohalide-based infrared optical fibers with reflectances peaked at one or more wavelengths between 1.5 and 15 microns in the infrared.
A further object of the invention is to side write highly-reflective, fiber Bragg gratings into sulfide-based chalcogenide infrared optical fibers.
A further object of the invention is to provide fiber Bragg gratings in infrared transmitting sulfide-based fibers.
These and other objects of this invention are achieved by forming reflective fiber Bragg gratings in the interior of an infrared transmitting glass fiber, such as a chalcogenide or chalcohalide-based infrared optical fiber, by side illuminating the fiber with two same-wavelength, laser writing beams which intersect at some angle in the fiber to form an intensity grating by way of interference along the length of the fiber, maintaining the infrared transmitting glass fiber at the intersection of the two writing beams to produce a reflective Bragg grating in the core and cladding of the glass fiber, and repeating this operation for each reflective fiber Bragg grating that is desired.
REFERENCES:
patent: 4993812 (1991-02-01), Matsuoka et al.
patent: 5066133 (1991-11-01), Brienza
patent: 5136677 (1992-08-01), Drexhage et al.
patent: 5218651 (1993-06-01), Faco et al.
patent: 5309452 (1994-05-01), Ohishi et al.
patent: 5364434 (1994-11-01), Sanghera et al.
patent: 5388173 (1995-02-01), Glenn
patent: 5400422 (1995-03-01), Askins et al.
patent: 5559907 (1996-09-01), Inniss et al.
patent: 5627927 (1997-05-01), Udd
patent: 5629953 (1997-05-01), Bishop et al.
patent: 5636304 (1997-06-01), Mizrahi et al.
Aggarwal Iswar D.
Busse Lynda E.
Moon John A.
Sanghera Jasbinder S.
Bovernick Rodney
Ferrett Sally A.
Karasek John J.
Kim Ellen E.
The United States of America as represented by the Secretary of
LandOfFree
Fiber Bragg gratings in chalcogenide or chalcohalide based... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Fiber Bragg gratings in chalcogenide or chalcohalide based..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Fiber Bragg gratings in chalcogenide or chalcohalide based... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2606395