ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to a technology for producing a sirocco and a propeller fan by molding an alloy having a low fusion point, such as a magnesium alloy, in use of, for example, injection molding.
DISCUSSION OF BACKGROUND
A sirocco fan made of a metal is mainly used in cases that noncombustibility is required to avoid a fire in, for example, a kitchen and that an ambient temperature becomes high. Sirocco fans are ordinarily made from a thin steel plate or a thin aluminum plate, a main plate having a rotation shaft, a side plate on an air invent side, and a plurality of vanes. These components are fixed by, for example, a caulked joint. Therefore, in a structure using the thin steel plate, the weights of the components are increased, whereby balancing becomes important. Further, in case of using the thin aluminum plate, a material cost is expanded, and it becomes difficult to weld the caulked portion for reinforcement. In Japanese Utility Model No. 1792736, Japanese Unexamined Utility Model Publication JP-A-62-14199, Japanese Unexamined Patent Publication JP-A-8-42495 disclose that a joint of a caulked portion is reinforced by successively welding after caulking by coating, or by bonding, became the joint is weak.
In Japanese Unexamined Patent Publication JP-9-126189 and Japanese Patent No. 2667748, a technology that a sirocco fan is monolithically molded out of a plastic.
In
FIG. 39
, a structure of a fan monolithically molded out of a plastic is shown. In
FIG. 39
, numerical reference
31
designates a centrifugal blower; numerical reference
33
designates an impeller, constructed by main vanes
40
, auxiliary vanes
41
, and a cone-like stiffening plate
37
, which impeller is accommodated in a case
32
and a bottom surface
42
; numerical reference
43
designates a shaft boss, directly connected to a motor
34
, for rotating the impeller; numerical reference
39
designates a stiffening ring for holding the impeller so as to be shaped like a cylinder; and numerical reference
35
and
36
respectively designate an air outlet and an air inlet, which are provided in a case.
Such an impeller is monolithically molded as a final product such that a resin is injected from a resin injecting gate, located apart from the shaft boss, into a cavity of a separated molding die and applied with heat and a temperature. Thus, the main vanes and the auxiliary vanes, both of which are thin, and the stiffening ring are monolithically formed. However, because leaves (lvs) of a metal mold is large, and a molten metal is hard to flow in a method of producing such as an aluminum die-cast, it is difficult to construct thin vanes of 1 through 2 mm.
However, because it is difficult to reuse a material of a plastic, particularly of a strengthen special plastic, in which a glass fiber is mixed like a fan. Therefore, an admixture is changed to a metal in consideration of the global atmosphere preservation. It is desired to utilize a metal having a low melting point in comparison with a combination of dissimilar metals, which are hardly separated, and also a metal requiring a high energy for producing, such as steel plate and an aluminum. In the Nikkei Mechanical 1996/12/9, Vol.495; the Nikkei Mechanical 1998/3, Vol.522; the Kogyo Zairyo 1998/5, Vol.46, No.5, and the Kogyo Zairyo 1998/10, Vol.46, No.10, a thixomolding method, by which a magnesium alloy being a representative metal having a low melting point, is subjected to injection molding, is disclosed. The thixomolding method is a coined word derived from thixotropy and injection molding, wherein the thixomolding method means a semi-molten metal injection molding method developed in U.S.A. Grain-like chips, made of a magnesium alloy ingot(igt) are used as a low material to inject into a metal mold of a product like injection molding of a plastic. Thereafter, a molded object is taken out of the metal mold. The magnesium alloy to be injected is changed depending on a use such that the magnesium alloy is in a liquid phase or contains an arbitrary solid.
FIG. 40
illustrates a structure of a thixomolding device as an injection molding device. Numerical reference
101
designates a hopper for throwing a raw material to a feeder
105
; numerical reference
107
designates an electrical heater, i.e. ceramic band heater, inside which a screw
103
is rotated; numerical reference
102
designates a cylinder heated by the electrical heater; numerical reference
104
designates a back flow prevention ring; numerical reference
106
designates an inactive atmosphere; numerical reference
109
designates a metal mold of a product; numerical reference
112
designates a nozzle for injecting a molten metal accumulated in a reservoir
122
from an injection molding machine by a rapid shot system; and numerical reference
121
designates a rotary drive.
In
FIG. 40
, a pellet-like magnesium alloy is thrown from the hopper
101
, and a part of the magnesium alloy, measured by the feeder
105
, is thrown into the cylinder
102
. An outer peripheral portion of the cylinder is heated by the electric heater
107
, i.e. the ceramic band heater, to make a semi-fusion magnesium alloy, wherein the semi-fusion magnesium alloy is separated from the magnesium alloy in the feeder by the inactive atmosphere
106
. Only an injected amount of the magnesium alloy is measured and supplied from the feeder to appropriately control the amount of the semi-fusion magnesium alloy. However, the injected amount and a supplied amount do not completely match, unlike resin molding. The magnesium alloy thrown into the cylinder
102
is forward conveyed, made to be like slurry, and injected by a rotation of the screw
103
. Thixomolding uses characteristics of thixotropy of a magnesium alloy. A magnesium alloy exists in a condition that dendrites in a solid phase are connected like branches in a solid-liquid coexisting state. Accordingly, a viscosity is high in this state. When a shear force is continuously applied by the rotating screw
103
, the dendrites are cut and minutely powdered, whereby fluidity is enhanced.
FIG. 41
illustrates a structure of a nozzle of the molding machine. Numerical reference
110
designates a coagulate plug, which prevents the semi-fusion magnesium alloy
111
from flowing out of the tip nozzle
112
; and numerical reference
113
designates a gate of the metal mold
109
. The tip nozzle
112
is shaped like a projected hemisphere. An entrance of the gate
113
of the metal mold
109
is shaped like a recessed hemisphere having an inlet a little larger than an outlet of the tip nozzle
112
. The tip nozzle
112
and the inlet of the gate
113
are in contact with each other and combined on their hemispheres. If the contact is not tight, there is a possibility that the semi-fusion magnesium alloy is brown into the atmosphere. Therefore, it is necessary to carefully adjust the contact. At a top of the semi-fusion magnesium alloy
111
, a lump formed by a metal, referred to as the coagulate plug
110
, is located. When the semi-fusion magnesium alloy is injected, the coagulate plug is projected and an injection is finished within a very short time of several dozens of microseconds through several milliseconds.
FIG. 42
illustrates a state that the injection molding machine is separated from the metal mold after completing the injection. A metallic piece chokes the gate portion
113
, and a coagulate plug
110
is left at a separated portion.
Meanwhile, a propeller fan, supplied for an ordinary use, is made of a plastic. When a propeller fan is used where a fire is used as in a kitchen, or where is a high temperature, the propeller fan is made of a metal. A method of producing the propeller fan made of a metal is such that a thin steel plate, a thin aluminum plate, or the like is used; an impeller is formed by monolithical drawing; and a rotation shaft, formed as another component, is joined to and fixed to the fan. Therefore, the impeller formed by monolithically drawing a thin steel plate is abruptly twisted at a hub of a vane.
Endo Akio
Fukuyama Jiro
Iwamura Yoshimi
Kikuchi Hitoshi
Makino Yasuyoshi
Burns Doane , Swecker, Mathis LLP
Edgar Richard
Look Edward K.
Mitsubishi Denki & Kabushiki Kaisha
LandOfFree
Fan, method for producing the fan by molding molten metal,... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Fan, method for producing the fan by molding molten metal,..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Fan, method for producing the fan by molding molten metal,... will most certainly appreciate the feedback.