Extrusion tool, process for the production thereof and use...

Metal deforming – Tool and/or tool holder – Tool comprising closed periphery deforming passageway

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C072S253100

Reexamination Certificate

active

06370934

ABSTRACT:

The present invention concerns an extrusion tool—in particular a disk-shaped pressing or extrusion die with at least one shaping opening for the extrusion of metal such as aluminum or an aluminum alloy—comprising a steel material with a surface coating. The invention also concerns a process for the production of an extrusion tool of that kind, and the use thereof.
The hardness of conventional pressing tools—which are used for example for the production of shaped aluminum parts—is often not adequate for industrial use in order to achieve satisfactory resistance to wear and thus economically meaningful service lives. For that reason such extrusion tools are hardened using known hardening processes.
Extrusion tools produced from hot-machining steels are more commonly hardened after machining production thereof to between about 46 and 50 HRC and are then finished by grinding, cavity sinking by EDM and wire-EDM; the tool is then usually subjected to a trial in the aluminum pressing machine and—if necessary—a correction is made. If then an extrusion tool is ready for the extrusion operation, it is set to a surface hardness of about 1000 VH in the prescribed manner by nitriding; practice has shown that this hardness value affords adequate resistance to wear, in use in a practical context.
The known nitriding processes include salt bath nitriding using cyanide salts. That process however involves serious environmental problems so that the industrial future thereof is doubtful. Nitriding by means of a gas suffers from the disadvantage that the hardening layer produced is relatively thick and as a result has only a limited level of toughness. Finally there is the possibility of plasma nitriding, but that process is not suitable in particular for tools with thin slots as the openings therethrough.
The known hardening processes involving nitriding also suffer from the common disadvantage that the hardening layer diffuses away with increasing temperature; at a temperature of about 500° C. for example a layer which is produced by salt bath nitriding is no longer present after about fifteen hours.
If then in a pressing operation the nitriding layer has disappeared due to the effect of diffusion, the pressing operation has to be interrupted; the tool is pickled free, cleaned and re-nitrided. With frequent post-nitriding near the tempering temperature of the steel used, its hardness and basic strength also continuously decrease, and that results in premature failure. Thus for example in the case of thin-walled tools, the service life which can be achieved is only between about 30 and 100 pressing operations before renewed post-nitriding, with its attendant cost disadvantage, becomes necessary.
In consideration of that state of the art the inventor set himself the aim of providing an extrusion tool which not only affords effective durable protection from wear—and accordingly a markedly increased service life—but also involves good suitability in particular for thin-wall tools. The invention seeks to provide that the production process can be implemented in a simple fashion and without environmental pollution.
That object is attained by the teachings of the independent claims; the appendant claims set forth advantageous developments.
In accordance with the invention the coating of the extrusion tool is made from a coating material which is selected from the group containing titanium carbide, titanium nitride, titanium boride, vanadium carbide, chromium carbide, aluminum oxide, silicon nitride and combinations thereof; that coating material has been applied by a CVD-gas deposition process—preferably at temperatures over 1000° C.—to the surface of the extrusion tool whose base material is in particular a low-distortion hot-working steel.
A process having the following steps is also in accordance with the invention
cutting shaping of the extrusion tool from a steel material in the desired configuration;
hardening and final machining of the extrusion tool;
coating the shaped steel material at predetermined locations with at least one above-mentioned coating material by means of the so-called CVD-process; and
hardening the coated steel material.
The thermally activated CVD-process—Chemical Vapor Deposition—is known per se for the production of single crystals, the impregnation of fiber structures with carbon or ceramics and generally for the deposition of thin layers—either by growth onto a surface or by the diffusion of borides, carbides, nitrides, oxides.
The procedure in accordance with the invention results in a wear-resistant layer for the extrusion tool, which outlasts the service life of the tool itself, without further post-treatments. That surprising property is afforded by virtue of the coating which is applied by the CVD-process and which is applied at temperatures of preferably more than 1000° C.; advantageously in that respect the invention comes in above the conventional hardening processes which basically remain below temperatures of between about 500 and 600° C.—that is to say the tempering limit of the steel material used.
Admittedly, CVD-coating requires hardening of the finished tool after the coating operation; however by accurately controlling the flow phenomena in the tools and the selection in accordance with the invention of in particular low-distortion hot-working steels to carry the invention into effect, that technology can be managed in a surprising and unforeseeable manner and affords outstanding properties in terms of hardness and resistance to wear.
As already mentioned above, in an advantageous development of the invention, in particular titanium carbide, titanium nitride, titanium boride, vanadium carbide, chromium carbide, aluminum oxide and silicon nitride are suitable for the coating; depending on the material involved, it is possible to achieve microhardness levels of between VH=about 2000 and VH=about 4000. In particular titanium carbide or aluminum oxide—applied by means of the CVD-process—have outstanding toughness properties while for example chromium carbide is particularly resistant to abrasive wear and less susceptible to cracks or pores. In particular also titanium carbide is additionally distinguished by advantageous frictional properties.
The CVD-coating process which is used in accordance with the invention, namely direct deposition of the stated solid materials out of the gaseous phase affords the present field of use of the extrusion dies numerous advantages which besides resistance to wear—that is to say a long service life—afford hardness and toughness:
accurate and uniform and regular coating, even on tools of complicated shape; due to the scatter capability inherent in CVD-procedures it is possible in particular to apply a uniform regular coating with a high degree of accuracy;
advantageous ratio of defect rates and tools quality; in the production and coating of the extrusion die in accordance with the invention, the CVD-process which can be well-managed affords considerably procedural reliability and good reproducibility, so that it is possible to produce tools of extremely high-grade quality, with a very low level of rejects; and
high layer adhesion; a very good bond is produced between the base material and the coating by the CVD-process, by virtue of the metallurgical character of the bond.
Preferably the starting materials used for the production of the extrusion die according to the invention are tough steels with good high-temperature characteristics and which are alloyed for example with Cr. Mo or with tungsten and which are melted for example by ESR (Electro-Slag Remelting) for a high level of toughness.
The above-mentioned coating materials, any combinations thereof, even in a multi-layer structure, or however alternative suitable materials, are then deposited by means of a CVD-process at temperatures of between about 700 and about 1050° C. for a period of between 5 and 6 hours.
The tool produced in that way is hardened again after that coating procedure.
The steel alloy used is preferably so selected that no substantial

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Extrusion tool, process for the production thereof and use... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Extrusion tool, process for the production thereof and use..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Extrusion tool, process for the production thereof and use... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2870802

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.