Etching method

Details Etching method Etching method

2001-02-05

2004-06-22

Goudreau, G (Department: 1763)

Semiconductor device manufacturing: process

Chemical etching

Vapor phase etching

C438S723000, C438S724000, C438S725000, C438S734000, C438S740000

Reexamination Certificate

active

06753263

ABSTRACT:

TECHNICAL FIELD
The present invention relates to an etching method that may be adopted in a process for manufacturing a semiconductor device.
BACKGROUND ART
To keep pace with the great improvements made with respect to the degree of integration of semiconductor devices in recent years, miniaturization of various elements formed on semiconductor substrates has become one of the crucial technical requirements. In order to meet this requirement, the distances between the individual gates (electrodes) formed on a semiconductor substrate must be reduced, and if contact holes are formed between the gates, the contact holes, too, must be miniaturized. However, as the distances between the gates become increasing small, the difficulty in forming ever smaller contact holes at accurate positions increases, due to the limits of the alignment performance of the stepper and the like. Accordingly, a self-aligning contact technology, whereby self-aligned contact holes are formed within the minute space between individual gates by forming a protective film (base) constituted of, for instance, an SiN
x
film at the surfaces of the gates and thereby preventing the gates from becoming etched during the contact hole formation, has been proposed of late. It is to be noted that SiN
x
as referred to in this specification may indicate a state in which SiN and Si
3
N
4
are mixed as well as SiN or Si
3
N
4
itself.
A mixed gas containing, for instance, C
4
F
8
and CO is often used as the processing gas when forming contact holes at an a SiO
2
film (insulating film) covering the gates formed on a semiconductor substrate by employing the self-aligning contact technology described above, so that the selection ratio of the SiO
2
film layer relative to the SiN
x
film layer is improved. Namely, by using such a processing gas in which C
4
F
8
constituting the processing gas contains a relatively large number of carbon atoms compared to CF
4
or C
2
F
6
used in the prior art, a carbon film to constitute a protective film can be formed with ease at the inner wall surface of the contact holes. In addition, since CO is added in the processing gas, the formation of the carbon film is further facilitated. As a result, fluorine radicals constituting the etching ions do not readily come in contact with the SiN
x
film layer covered by the carbon film, thereby achieving an improvement in the selection ratio of the SiO
2
film layer relative to the SiN
x
film layer.
However, while the selection ratio of the SiO
2
film layer relative to the SiN
x
film layer is improved due to the presence of the carbon film formed at the inner wall surface of the contact holes by forming the contact holes using a mixed gas containing C
4
F
8
and CO as described above, carbon becomes accumulated also at the bottoms of the contact holes. This results in the carbon accumulated at the bottoms of the contact holes preventing the fluorine radicals from reaching the bottoms with ease. Consequently, it becomes difficult to mill contact holes having a depth larger than a specific measurement, to lead to a reduction in the penetration and an etching stop.
In addition, while it has become one of the technological requirements in recent years to form contact holes achieving a high aspect ratio in extremely small spaces between gates, the structure of such deep contact holes makes it difficult for fluorine radicals to reach the bottoms of the contact holes. As a result, if the contact holes are formed by using the mixed gas containing C
4
F
8
and CO as described above, the accumulation of carbon at the bottoms of the contact holes and the reduction in the quantity of fluorine radicals entering the contact holes further reduce the penetration and increases the occurrence of etching stop.
Furthermore, if contact holes are formed through a process in which carbon is accumulated readily at the bottoms of the contact holes as in the etching method in the prior art described above, it is necessary to perform over-etching on the semiconductor substrate in consideration of carbon which accumulates at the bottoms of the contact holes. However, if such an over-etching process is performed on the semiconductor substrate, the insulating film layer and the SiN
x
film layer, which are respectively provided to cover and protect the gates are also etched, to result in the insulating film layer and the gates themselves becoming exposed inside the contact holes.
Consequently, problems such as defective insulation and shorting of the gates, other wiring or electrodes may occur to lower the yield. In particular, the shoulder (corners) of the SiN
x
film layer, which often distend into the contact holes, tend to become etched very readily, and thus, if over-etching process is performed on the semiconductor substrate as described above, the worst damage is likely to occur at the comers. For this reason, the etching process can only be performed to an extent to which the shoulder of the SiN
x
film layer do not become damaged in the etching method in the prior art, which makes it extremely difficult to form contact holes achieving a high aspect ratio.
A first object of the present invention, which has been completed by addressing the problems of the prior art discussed above, is to provide a new and improved etching method which achieves an improvement in the selection ratio of the SiO
2
film layer relative to the SiN
x
film layer by forming a carbon film (protective film) at the shoulder of the SiN
x
film layer exposed inside the contact holes and makes it possible to form contact holes achieving a high aspect ratio by minimizing the accumulation of carbon at the contact hole bottoms.
A second object of the present invention is to provide a new and improved etching method that eliminates excessive etching which may cause damage to the shoulder of the SiN
x
film and achieves an improvement in yield by preventing defective insulation at the gates and the occurrence of dialectic breakdown.
DISCLOSURE OF THE INVENTION
In order to achieve the objects described above, in a first aspect of the present invention, an etching method for plasma-etching an SiO
2
film layer covering an SiN
x
film layer formed at a workpiece placed within an air-tight processing chamber by raising to plasma a processing gas induced into the processing chamber, which is characterized in that the processing gas is a mixed gas containing, at least, C
4
F
8
and CH
2
F
2
, is provided.
In this etching method in which CH
2
F
2
is used in the processing gas instead of CO, fluorine radicals can be generated from CH
2
F
2
as well as from C
4
F
8
to increase the quantity of fluorine radicals generated during the process. As a result, even when forming contact holes with a high aspect ratio, fluorine radicals can reach the bottoms of the contact holes with a high degree of reliability to make it possible to etch the bottoms while removing carbon accumulated at the bottoms of the contact holes, thereby facilitating the formation of contact holes with a specific depth.
In addition, since the bottoms of the contact holes can be etched with a high degree of reliability, it is not necessary to over-etch the workpiece and thus, damage to the SiN
x
film layer exposed inside the contact holes and, in particular, damage to the shoulder of the SiN
x
film layer can be prevented. As a result, since the insulating film layer covering the gates protected by SiN
x
film layer or the gates themselves are not exposed inside the contact holes, defective insulation at the gates and the occurrence of dialectic breakdown are prevented to achieve an improvement the yield. Furthermore, since the bottoms of the contact holes can be etched while sustaining a specific etching rate, the length of time required to perform the etching process can be reduced to achieve an improvement in throughput, as well.
Since CH
2
F
2
constituting the processing gas contains carbon atoms, a carbon film to constitute a protective film can be formed at the inner wall surface of the contact holes with a high degree of reliability

Affiliated with

Also associated with

Rating

Etching method does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Etching method, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Etching method will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3314127