Epoxidation catalyst and process

Details Epoxidation catalyst and process Epoxidation catalyst and process

2000-12-07

2001-08-28

Trinh, Ba K. (Department: 1625)

Organic compounds -- part of the class 532-570 series

Organic compounds

Heterocyclic carbon compounds containing a hetero ring...

C549S532000

Reexamination Certificate

active

06281369

ABSTRACT:

FIELD OF THE INVENTION
This invention relates to the preparation of a novel epoxidation catalyst comprised of a titanium zeolite catalyst which has been modified with a noble metal such as palladium, which catalyst has enhanced stability, and to the use of the catalyst for the production of oxirane compounds such as propylene oxide.
BACKGROUND OF THE INVENTION
Oxiranes constitute an important class of chemical intermediates useful for the preparation of polyether polyols, glycols, glycol ethers, surfactants, functional fluids, fuel additives and the like. Many different methods for synthesizing oxiranes from the corresponding olefins have been described in the literature. A Japanese patent application assigned to the Tosoh Corporation and published in 1992 (Kokai No. 4-352771) proposed making propylene oxide by reacting propylene, hydrogen and oxygen using a catalyst comprising a Group VIII metal and a crystalline titanosilicate. Improvements to or variations of this basic process were subsequently described in the following published patent applications: WO 97/25143, DE 19600709, WO 96/02323, WO 97/47386, WO 97/31711, JP H8-269030, JP H8-269029, U.S. Pat. Nos. 6,005,123, 6,008,388 and 5,646,314.
As with any chemical process, it would be desirable to attain still further improvements in epoxidation methods of this type. In particular, extending the useful life of the catalyst would significantly enhance the commercial potential of such methods. A problem has been that the noble metal tends to be leached or otherwise lost from the catalyst during use which results in loss of activity and selectivity. Additionally, loss of noble metal imposes an economic penalty which may render the process uneconomic.
SUMMARY OF THE INVENTION
The present invention provides a process for the preparation and use of a catalyst comprised of a titanium zeolite and a noble metal characterized in that the catalyst has improved stability and resistance to loss from the zeolite during use, and to the use of same in epoxidations.
DETAILED DESCRIPTION OF THE INVENTION
The catalysts of the present invention are comprised of a titanium zeolite and a noble metal (preferably an element of Group VIII of the Periodic Table). Suitable zeolites are those crystalline materials having a porous molecular sieve structure with titanium atoms substituted in the framework. The choice of zeolite employed will depend upon a number of factors, including the size and shape of the olefin to be epoxidized. For example, it is preferred to use a relatively small pore titanium zeolite such as a titanium silicalite if the olefin is a lower aliphatic olefin such as ethylene, propylene, or n-butene. Where the olefin is propylene, the use of a TS-1 titanium silicalite is especially advantageous. For a bulky olefin such as cyclohexene, a larger pore titanium zeolite such as a titanium zeolite having a structure isomorphous with zeolite beta may be preferred.
The titanium-containing zeolites useful as catalysts in the epoxidation step of the process comprise the class of zeolitic substances wherein titanium atoms are substituted for a portion of the silicon atoms in the lattice framework of a molecular sieve. Such substances are known in the art.
Particularly preferred titanium-containing zeolites include the class of molecular sieves commonly referred to as titanium silicalites, particularly “TS-1” (having an MFI topology analogous to that of the ZSM-5 aluminosilicate zeolites). “TS-2” (having an MEL topology analogous to that of the ZSM-11 aluminosilicate zeolites), and “TS-3” (as described in Belgian Pat. No. 1,001,038). Also suitable for use are the titanium-containing molecular sieves having framework structures isomorphous to zeolite beta, mordenite, ZSM-48, ZSM-12, and MCM-41. The titanium-containing zeolite preferably contains no elements other than titanium, silicon and oxygen in the lattice framework, although minor amounts of boron, iron, aluminum, and the like may be present. Other metals such as tin or vanadium may also be present in the lattice framework of the zeolite in addition to the titanium, as described in U.S. Pat. Nos. 5,780,654 and 5,744,619.
Preferred titanium-containing zeolite catalysts suitable for use in the process of this invention will generally have a composition corresponding to the following empirical formula xTiO
2
(1−x)SiO
2
where x is between 0.0001 and 0.500. More preferably, the value of x is from 0.01 to 0.125. The molar ratio of Si:Ti in the lattice framework of the zeolite is advantageously from 9.5:1 to 99:1 (most preferably from 9.5:1 to 60:1). The use of relatively titanium-rich zeolites may also be desirable. The zeolite may or may not contain extra framework titanium.
As an essential aspect of the present invention, the catalyst comprises a noble metal supported on the above-described supports.
While any of the noble metals can be utilized (i.e., gold, silver, platinum, palladium, iridium, ruthenium, osmium), either alone or in combination, palladium is particularly desirable. Typically, the amount of noble metal present in the catalyst will be in the range of from 0.01 to 5 weight percent, preferably 0.05 to 2 weight percent. The manner in which the noble metal is incorporated into the catalyst is a critical feature of the invention.
The titanium silicalite used in the present invention is prepared by known procedures. An important feature is that the silicalite be subjected to an oxidative calcination as with air at elevated temperature, eg. 300 to 850° C., illustratively 550° C., in accordance with known procedures prior to use in accordance with the invention. The calcination is carried out until substantially complete removal of organic residues is accomplished. Thorough pre-washing and oxidative calcination procedures are described, for example in JP H-269029 and JP H-269030.
The titanium silicalite washing and calcination is carried out so as to remove essentially all of the residues of materials such as templating agents and the like used in the silicalite preparation, especially ammonium—type materials.
The calcined silicalite essentially free of residues is then treated as by ion exchange or impregnation procedures in order to incorporate the desired noble metal into the silicalite in appropriate amounts. Of the procedures, ion exchange is preferred with subsequent essentially complete removal of anionic residues from the resulting catalyst. Impregnation procedures can be used as is described herein later.
Removal of essentially all residues from the noble metal containing support is important and is conventionally accomplished by water washing and filtering techniques. Multiple washing and filtering steps are especially preferred. Preferably the noble metal/titanium silicalite catalyst is then dried by gentle heating, for example under vacuum.
A critical step in the preparation procedure is oxidative calcination of the noble metal/titanium silicate catalyst. Whereas prior art such as JP H8-269029 and JP H8-269030 teaches reduction of the noble metal/silicate catalyst, eg. 90° C. with a H
2
/N
2
reducing gas, before use in epoxidation reactions, it has now been found that such prior catalysts are prone to rapid leaching of noble metal during epoxidation use thus severely limiting the practical utility of such catalysts.
It has now been found that the oxidation calcination of the noble metal/silicate catalyst results in the formation of a useful catalyst composition having greatly improved stability as against noble metal loss and thus greatly improved utility in the production of oxirane product such as propylene oxide.
The oxidative calcination is carried out at temperatures of at least 150° C. for illustratively 10 minutes to 24 hours. Calcination temperature in the range 150-650° C., preferably 250-600° C., and most preferably 300-550° C. are employed. The calcination gas is preferably air by reason of cost and availability although other mixtures of oxygen and inert gas can be used. Generally during the calcination it is advantageous to ramp the temperature up at t

Affiliated with

Also associated with

Rating

Epoxidation catalyst and process does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Epoxidation catalyst and process, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Epoxidation catalyst and process will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2549445