Enhanced machinability precipitation-hardenable stainless...

Alloys or metallic compositions – Ferrous – Nine percent or more chromium containing

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C420S061000, C148S325000

Reexamination Certificate

active

06576186

ABSTRACT:

FIELD OF THE INVENTION
This invention relates to high strength stainless steel alloys and, in particular, to a precipitation-hardenable, martensitic stainless steel alloy having a unique combination of strength, ductility, toughness, and machinability.
BACKGROUND OF THE INVENTION
Aerospace material specification AMS 5659 describes a 15Cr-5Ni precipitation hardenable, corrosion resistant steel alloy for use in critical aerospace components. AMS 5659 specifies minimum strength and ductility requirements which the alloy must meet after various age-hardening heat treatments. For example, in the H900 condition (heated at about 900 F. (482 C.) for 1 hour and then air cooled), a conforming alloy must provide a tensile strength of at least 190 ksi (1310 MPa) in both the longitudinal and transverse directions together with an elongation of at least 10% in the longitudinal direction and at least 6% in the transverse direction. However, products manufactured to meet that specification typically lack the ease of machinability desired by component fabricators.
As the alloy specified in AMS 5659 continues to be used in many structural components for aerospace applications, a need has arisen for an alloy that meets all of the mechanical requirements of AMS 5659, but which also provides superior machinability. It is generally known to add certain elements such as sulfur, selenium, tellurium, etc. to stainless steel alloys in order to improve their machinability. However, the inclusion of such “free-machining additives”, without more, will adversely affect the mechanical properties of the alloy, such as toughness and ductility, to the point where the alloy becomes unsuitable for the critical structural components for which it was designed. Consequently, a need exists for a precipitation-hardenable martensitic stainless steel having good ductility, toughness, and notch tensile strength to be useful for critical applications and which also provides superior machinability compared with alloy compositions currently utilized for fracture-critical components.
SUMMARY OF THE INVENTION
The present invention is directed to a precipitation-hardenable martensitic stainless steel which provides mechanical properties (tensile and notch strength, ductility, and toughness) that meet the requirements of AMS 5659 and which also provides significantly better machinability compared to the known grades of 15Cr-5Ni precipitation-hardenable stainless steels. The broad, intermediate, and preferred weight percent compositions of the alloy according to this invention are set forth in the following table.
Weight percent
Element
Broad
Intermediate
Preferred
C
0.030 max. 
0.025 max.
0.010-0.025
Mn
1.00 max.
 0.50 max.
 0.50 max.
Si
1.00 max.
 0.60 max.
 0.50 max.
P
0.030 max. 
0.030 max.
0.025 max.
S
0.005-0.015
0.005-0.015
0.007-0.013
Cr
14.00-15.50
14.00-15.50
14.25-15.25
Ni
3.50-5.50
3.50-5.50
4.00-5.50
Mo
1.00 max.
 0.50 max.
0.50 max.
Cu
2.50-4.50
2.50-4.50
3.00-4.00
Nb + Ta
(5 × C) − 0.30
(5 × C) − 0..25
(5 × C) − 0.20
Al
0.05 max.
0.025 max.
0.025 max.
B
0.010 max. 
0.005 max.
0.005 max.
N
0.030 max. 
0.025 max.
0.010-0.025
Fe
Bal.
Bal.
Bal.
The foregoing tabulation is provided as a convenient summary and is not intended thereby to restrict the lower and upper values of the ranges of the individual elements for use in combination with each other, or to restrict the ranges of the elements for use solely in combination with each other. Thus, one or more of the ranges can be used with one or more of the other ranges for the remaining elements. In addition, a minimum or maximum for an element of a broad, intermediate, or preferred composition can be used with the minimum or maximum for the same element in another preferred or intermediate composition. Here and throughout this specification the term “percent” or the symbol “%” means percent by weight unless otherwise specified.
DETAILED DESCRIPTION OF THE INVENTION
The interstitial elements carbon and nitrogen are restricted to low levels in this alloy in order to benefit the machinability of the alloy. Therefore, the alloy contains not more than about 0.030% each of carbon and nitrogen and preferably not more than about 0.025% of each of those elements. Carbon and nitrogen are strong austenite stabilizing elements and limiting them to levels that are too low leads to the formation of undesirable amounts of ferrite in this alloy. Therefore, at least about 0.010% each of carbon and nitrogen is preferably present in the alloy.
This alloy contains a controlled amount of sulfur to benefit the machinability of the alloy without adversely affecting the ductility, toughness, and notch tensile strength of the alloy. To that end, the alloy contains at least about 0.005% and preferably at least about 0.007% sulfur. Too much sulfur adversely affects the ductility, toughness, and notch tensile strength of this alloy. Therefore, sulfur is restricted to not more than about 0.015% and preferably to not more than about 0.013% in this alloy.
At least about 14.00% and preferably at least about 14.25% chromium is present in the alloy to provide an adequate level of corrosion resistance. However, when chromium is present in excess of about 15.50% the formation of undesirable ferrite results. Therefore, chromium is restricted to not more than about 15.50% and preferably to not more than about 15.25% in this alloy.
At least about 3.50%, preferably at least about 4.00%, nickel is present in the alloy to maintain good toughness and ductility. Nickel also benefits the austenite phase stability of this alloy at the low levels of carbon and nitrogen used in the alloy. The strength capability of the alloy in the aged condition is adversely affected when more than about 5.50% nickel is present because of incomplete austenite-to-martensite transformation (i.e., retained austenite) at room temperature. Therefore, this alloy contains not more than about 5.50% nickel.
At least about 2.50%, preferably at least about 3.00%, copper is present in this alloy as the primary precipitation hardening agent. During the age hardening heat treatment, the alloy achieves substantial strengthening through the precipitation of fine, copper-rich particles from the martensitic matrix. Copper is present in this alloy in amounts ranging from 2.50 to 4.50% to provide the desired precipitation hardening response. Too much copper adversely affects the austenite phase stability of this alloy and can lead to formation of excessive austenite in the alloy after the age hardening heat treatment. Therefore, copper is restricted to not more than about 4.50% and preferably to not more than about 4.00% in this alloy.
A small amount of molybdenum is effective to benefit the corrosion resistance and toughness of this alloy. The minimum effective amount can be readily determined by those skilled in the art. Too much molybdenum increases the potential for ferrite formation in this alloy and can adversely affect the alloy's phase stability by promoting retained austenite. Therefore, while this alloy may contain up to about 1.00% molybdenum, it preferably contains not more than about 0.50% molybdenum.
A small amount of niobium is present in this alloy primarily as a stabilizing agent against the formation of chromium carbonitrides which are deleterious to corrosion resistance. To that end the alloy contains niobium in an amount equivalent to at least about five times the amount of carbon in the alloy (5×%C). Too much niobium, particularly at the low carbon and nitrogen levels present in this alloy, causes excessive formation of niobium carbides, niobium nitrides, and/or niobium carbonitrides and adversely affects the good machinability provided by this alloy. Too many niobium carbonitrides also adversely affect the alloy's toughness. Furthermore, excessive niobium results in the formation of an undesirable amount of ferrite in this alloy. Therefore, niobium is restricted to not more than about 0.30%, better yet to not more than about 0.2

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Enhanced machinability precipitation-hardenable stainless... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Enhanced machinability precipitation-hardenable stainless..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Enhanced machinability precipitation-hardenable stainless... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3103384

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.