Coating processes – Electrical product produced – Condenser or capacitor
Patent
1981-05-21
1983-09-06
Smith, John D.
Coating processes
Electrical product produced
Condenser or capacitor
427125, 4271263, 4271265, 427226, 4273882, 524403, 204290R, 429 42, 252 623Q, B05D 512
Patent
active
044029969
DESCRIPTION:
BRIEF SUMMARY
BACKGROUND OF THE INVENTION
Catalytic electrodes having a valve metal base and a catalytic coating comprising at least one platinum-group metal oxide are described for example in the following patents: are currently used for the electrolytic production of chlorine and provide a high anode life with reduced energy consumption.
However, when such anodes are used in metal electrowinning processes where oxygen is produced at the anode, they tend to undergo passivation and thus have a relatively short useful life. Passivation seems to be caused in this case by diffusion of oxygen through the coating resulting in build-up of an insulating oxide layer on the valve metal substrate and/or dissolution of ruthenium in the surrounding acid medium. In U.S. Pat. Re. 29,419, a coating is described which is especially intended as an anode for electrowinning. Finely divided ruthenium dioxide used as an electrocatalyst is applied together with an organic polymer to a substrate, followed by curing to produce a coating comprising the electrocatalyst dispersed in an inert polymer matrix. The organic polymer is intended in this case to serve as a binder, to provide mechanical support for the electrocatalyst to provide adhesion to and protection of the underlying substrate. According to the application intended, the amount of electrocatalyst used per part by weight of the polymer may generally vary within the range from 6:1 to 1:1, in order to provide the desired properties of such a coating. The conductive properties of such a composite coating will thus depend essentially on the amount of electrocatalyst dispersed in the inert polymer matrix, as well as its size and distribution throughout the matrix. The electrocatalyst must moreover be prepared in the form of extremely fine particles of less than 0.1 micron size, and then applied together with the organic polymer as uniformly as possible in order to be able to ensure the desired properties of the coating.
The state of the art relating to composite electrodes comprising conductive fillers dispersed in a polymer matrix may be further illustrated by U.S. Pat. Nos. 3,629,007, 3,751,301 and 4,118,294. The German patent application Offenlegungsschrift 2035918 further relates to an electrode for electrolytic purposes, which comprises a metallic support coated with an organic semi-conductor consisting of a polymeric metal phthalocyanine. U.S. Pat. Nos. 3,792,732, 3,881,957 and 4,090,979 moreover relate to catalytic electrode materials comprising semi-conducting polymers formed on a refractory oxide and impregnated with metal catalysts.
The production of satisfactory catalytic coatings for dimensionally stable electrodes presents in fact many complex problems due to the severe technical and economic requirements of industrial electrolytic processes. These problems relate on one hand to the choice of suitable materials to provide adequate catalytic activity and conductivity, as well as being physically and electrochemically stable under the severe operating conditions of industrial electrolytic processes, such as high current density, corrosive media and products. Good electrocatalysts such as the platinum-group metal oxides are moreover very expensive so that they must generally be used in minimum amounts and combined with cheaper inert coating materials which, however, are generally catalytically inactive and electrically non-conductive (e.g. TiO.sub.2 and most organic polymers). On the other hand, many potentially interesting electrode materials may be unsuitable for the manufacture of satisfactory coatings which meet all requirements of industrial electrolytic processes. Thus, for example, various organic semi-conductors of potential interest as electrode materials, are relatively difficult to manufacture and moreover are difficult to process into satisfactory coatings.
It is an object of the present invention to provide an electrocatalytic coating comprising at least one platinum-group metal catalyst forming a uniform solid mixture with an insoluble semi-conducting polymer of an
REFERENCES:
patent: Re29419 (1977-09-01), DeCraene
patent: 3438815 (1969-04-01), Giner
patent: 3438817 (1969-04-01), Short et al.
patent: 3629007 (1970-12-01), Kilduff
patent: 3674675 (1972-07-01), Leaman
patent: 3687724 (1972-08-01), Keith et al.
patent: 3751301 (1973-08-01), Kilduff
patent: 3761679 (1973-09-01), Dall
patent: 3792732 (1974-02-01), Stewart
patent: 3881957 (1975-05-01), Hausler
patent: 4043933 (1977-08-01), Breault et al.
patent: 4090979 (1978-05-01), Ogren et al.
patent: 4118294 (1978-10-01), Pellegri
Van Veen et al., Electrochimica Acta., vol. 24, pp. 921-928, 1979.
Gauger Jurgen F.
Hinden Jean M.
Katz Michael
Bueker Richard
Diamond Shamrock Corporation
Harang B. E.
Smith John D.
LandOfFree
Electrode coating with platinum-group metal catalyst and semi-co does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Electrode coating with platinum-group metal catalyst and semi-co, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Electrode coating with platinum-group metal catalyst and semi-co will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1592488