Elastomeric gloves

Details Elastomeric gloves Elastomeric gloves

2001-04-13

2003-05-20

Wu, David W. (Department: 1713)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

At least one aryl ring which is part of a fused or bridged...

C524S430000, C524S478000, C524S560000, C524S562000, C525S478000, C002S168000, C128S844000

Reexamination Certificate

active

06566435

ABSTRACT:

This invention relates to elastomeric gloves, particularly but not exclusively medical and surgical gloves, and to a method of making them.
Close fitting rubber gloves are well known and are used for a number of purposes, principally medical and surgical. It is especially important in some uses for the gloves to fit closely on the hand, at least in the finger and palm regions. To ensure this close fitting, it is customary for users to wear gloves of slightly smaller dimensions than their hands in order to ensure a close snug fit. However, some discomfort can arise during use of the gloves, from the continued application of pressure by the glove on the hand.
It has been proposed in EP-B-0456333 to overcome this problem by making such gloves of nitrile butadiene rubber since this material has long been known to show stress relaxation properties. In particular, the patent describes gloves made of a carboxylated elastomeric material comprising 0.1 to 0.5 parts zinc oxide per 100 parts carboxylated nitrile butadiene rubber, the material being such that when stretched 100% of its length with an initial stress and the 100% stretch maintained, the material relaxes within 6 minutes of the initial stress so that the 100% stretch is maintained by a reduced stress which is less than 80%, more preferably less than 50%, of the initial stress. The effect of this is that whilst the gloves are fight fitting when initially donned, the stress subsequently relaxes within six minutes so as to relieve the pressure applied to the user's hands and so provide greater comfort and sensitivity. In the only Example in the patent, the stress retention of a carboxylated nitrile butadiene rubber glove was 0% after six minutes.
Whilst this basic approach of using the known stress relaxation properties of carboxylated nitrile rubbers does provide some alleviation of the problem of user discomfort due to stress retention in rubber gloves, it does not provide a wholly satisfactory answer. In particular, we have found that the stress retention which occurs in known carboxylated nitrile rubbers such as taught by EP-B-0456333 is actually too low such that its use can result in poor fitting of gloves to the hands and fingers as the gloves gradually become loose with time because of creep due to stress relaxation. In particular, we have found that stress retention of less than 50% as is found in known such rubbers, can give rise to problems and that, surprisingly, far improved user comfort and satisfaction is achieved with a stress retention of from about 50 to about 70%.
Copolymer latices containing carboxyl-modified nitrile rubber and a diene are disclosed in EP 0559150A. Such latices can be used to provide rubber articles having high oil resistance and high mechanical strength.
Accordingly, in one aspect, the present invention provides an elastomeric glove made of a carboxylated nitrile rubber having from 2 to 6% by weight methacrylic acid equivalent and which exhibits a stress retention of from 50 to 70%, said stress retention being the percentage retention of the initial stress after six minutes at 100% extension. Gloves of the invention give better fitting to the hands and fingers and hence improved sensitivity of touch on extended wearing compared with those that have low stress retention of less than 50%.
The stress retention of the gloves produced according to the present invention is higher than that illustrated and obtained by EP-B-0456333, but lower than that of gloves made from natural rubber latex or polychloroprene latex. The gloves of the invention can be made to be good fitting and yet not to cause fatigue to the hands on extended wearing.
Gloves made of conventional carboxylated nitrile rubbers have a low stress retention, i.e. well below 50%. Accordingly, gloves of the present invention cannot be made by simply using known nitrile rubber glove technology since the stress retention would then be too low. We have found, however, that stress retention can be controllably increased to the levels required in the present invention by using prevulcanised nitrile butadiene rubber latex, i.e. latex in which some vulcanisation of the rubber by sulphur has been effected before the gloves are made. Prevulcanisation (or maturation) of the rubber in this way then enables the desired stress retention of 50 to 70% to be obtained following a conventional dipping production process.
The gloves of the invention can be non-chlorinated or chlorinated or polymer-coated, as desired. The carboxylated nitrile rubber latex used to make the gloves is preferably a copolymer of acrylonitrile, butadiene, and an unsaturated carboxylic acid. The unsaturated carboxylic acid is of acrylic acid type and may be, for example, acrylic acid, methacrylic acid, crotonic acid, itaconic acid, fumaric acid, or sorbic acid. Methacrylic acid is preferred. The ratio of acrylonitrile to butadiene in the copolymer will depend upon the use to which the glove is to be put. For an industrial glove requiring good resistance to organic solvents, the acrylonitrile content may be as high as 37 to 40% of the polymer. For surgical and other medical gloves, solvent resistance is much less important than softness and flexibility. In this case, a copolymer of much lower acrylonitrile content is used, usually about 26 to 30% of the polymer. The preferred amount of unsaturated carboxylic acid is 2-6% methacrylic acid equivalent, most preferably 3-5.5% methacrylic acid equivalent.
In the gloves of the invention, the nitrile rubber is cross-linked both by conventional vulcanisation (i.e. by sulphur, vulcanisation accelerators and zinc oxide), and by ionic crosslinking using polyvalent metal oxides, preferably zinc oxide. The amount of polyvalent metal oxide (eg. zinc oxide) used for the ionic cross-linking is preferably from about 0.1 to 0.5 phr (per hundred parts of nitrile rubber, dry basis), more preferably from 0.2 to 0.4 phr. The polyvalent metal oxides effect crosslinking ionically between carboxylate groups in the polymer chain. The amount of sulphur used for crosslinking is from 1 to 3 phr, preferably from 2 to 3 phr. The crosslinking of the nitrile polymers achieved by sulphur crosslinks (both during the process and during prevulcanisation) is the major effect and the ionic crosslinking via the polyvalent metal oxide and the carboxyl groups is the minor effect. The selection of a low level of carboxylation and of a low polyvalent metal oxide level keep the level of ionic crosslinks in the nitrile rubber relatively low. Ionic crosslinks exhibit higher stress relaxation characteristics than do sulphur crosslinks. The stress retention achieved can be controlled by varying the amounts of, and balance between, the two types of crosslink.
According to the invention, the carboxylated nitrile rubber latex is subjected to a prevulcanisation (or maturation) step. Preferably, this is at least at 30° C. for a minimum of 16 hours for fully compounded latex. As will be clear to those skilled in the art, however, different temperatures and times can be used to provide essentially the same effect and the invention encompasses these equivalents. In general, lower temperatures will require longer times, and higher temperatures shorter times. The practical minima and maxima will be readily determinable by those skilled in the art with any particular latex formulation, bearing in mind the ultimate purpose of providing gloves with a stress retention of from 50 to 70%.
In order that the invention may be more fully understood, the following Examples are given by way of illustration only.
Carboxylated acrylonitrile butadiene latices with a carboxylation level of 4%-6% methacrylic acid equivalent content were compounded according to Formulation A given in Table 1. Formulation B given in Table 2 has also been used. The latex was prevulcanized for 40° C. for various periods of time. Prevulcanization at 50° C. of has also been used. After the required heating time, the latex was cooled. Gloves were prepared from the prevulcanized latex by well-know procedures, involving the

Affiliated with

Also associated with

Rating

Elastomeric gloves does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Elastomeric gloves, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Elastomeric gloves will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3056543