Easily fibrillatable fiber

Details Easily fibrillatable fiber Easily fibrillatable fiber

1998-01-20

1999-10-26

Edwards, Newton

Stock material or miscellaneous articles

Coated or structually defined flake, particle, cell, strand,...

Rod, strand, filament or fiber

428373, D02G 300

Patent

active

059725010

DESCRIPTION:

BRIEF SUMMARY
BACKGROUND OF THE INVENTION

1. Field of the Invention
The present invention relates to a readily fibrillatable fiber comprising a vinyl alcohol based polymer (abbreviated to "PVA" hereinafter) and a cellulose polymer; more specifically, the present invention relates to a fiber and a fibril, characterized in that the fiber is readily modified into a superfine fibril through the single action of chemically swelling force or mechanical stress or the combination thereof and is therefore preferable for use in wet laid or dry laid nonwoven fabrics, separators in alkaline batteries, reinforcing fibers for friction materials and reinforcing fibers for cement products.
2. Description of the Prior Art
Nonwoven fabrics comprising PVA fibers have been used conventionally as the separators of alkaline manganese batteries due to their strong alkaline resistance. Following the development of electronics a nd information and communication systems in recent years, far advanced performance has been demanded toward batteries, while mercury-free batteries have also been needed from the respect of pollution-free battery production and disposal. Additionally, more outstanding separating potency has been required for separators for use in batteries because of the demand for higher performance without mercury. Therefore, PVA fibers of a finer denier have been prepared for use in the separators of alkaline manganese batteries, and a PVA fiber of 0.3 denier is now commercially available. The absorptivity of alkaline solutions (namely, absorption in weight of aqueous KOH solution) as a very significant property for the separators in alkaline manganese batteries cannot sufficiently be satisfied by simply preparing a PVA fiber of a finer denier.
In order to overcome these problems, use has been made of a separator comprising a mixture of a PVA fiber of a finer denier and a polynosic fiber as one cellulose fiber with great absorptivity of alkaline solutions which is readily fibrillatable into a superfine fibril through beating. Disadvantageously, however, the polynosic fiber may cause public hazards in the production process. Additionally, the polynosic fiber has such poor beatability that the central part of the fiber remains as a thick stem in the resulting fibril. Thus, it is very difficult to recover a fibril sufficiently finely disintegrated to such an extent that the stem is also disintegrated. Hence, it has been desired a PVA fiber fibrillatable into a superfine fibril and having greater absorptivity of alkaline solutions and higher alkaline resistance.
As the reinforcing fibers of a variety of friction materials for use in automobile brakes and clutch plates, conventionally, asbestos has been used commonly in terms of the trapping performance of inorganic particles, thermal resistance, heat fusion resistance, reinforcing properties and the like. However, the use of asbestos has been put under strict regulations because of concern that asbestos may be harmful for human health. In recent years, therefore, the fibril of costly aramide fiber has been replacing asbestos. However, aramide fiber is so costly that it is only used in a limited fashion. Thus, low-cost materials with insufficient reinforcing performance, such as natural pulp, are used practically. Accordingly, a fiber has been desired which is less expensive than aramide fiber and fibrillatable so that the fiber might procure particle trapping performance, thermal resistance, heat fusion resistance and reinforcing properties in combination.
Asbestos has been used conventionally as a reinforcing fiber for cement products such as slate plate, but the use thereof is strictly regulated by the same reason as described above. PVA fibers have been used as an alternative to asbestos because the fibers have greater resistance to the alkalis in cement, but because PVA fibers have larger fiber sizes than that of asbestos, the green strength of the slate reinforced with the fibers is low. In order to supplement the strength, the fibers should be used in combination with fibrils of n

REFERENCES:
patent: 5229057 (1993-07-01), Ohmory et al.
patent: 5238995 (1993-08-01), Fukunishi et al.
patent: 5455114 (1995-10-01), Ohmory et al.
patent: 5486418 (1996-01-01), Ohmory et al.

Affiliated with

Also associated with

Rating

Easily fibrillatable fiber does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Easily fibrillatable fiber, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Easily fibrillatable fiber will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-761646