ABSTRACT:
Dual phase steel sheet is made using a time/temperature cycle including a soak at about AC1+45° F. to AC1+135° F. and a hold at 850-940F, where the steel has the composition in weight percent, carbon: 0.02-0.20; aluminum: 0.010-0.150; titanium: 0.01 max; silicon: 0.5 max; phosphorous: 0.060 max; sulfur: 0.030 max; manganese: 0.8-2.40; chromium: 0.03-1.50; molybdenum: 0.03-1.50; with the provisos that the amounts of manganese, chromium and molybdenum have the relationship: (Mn+6Cr+10 Mo)=at least 3.5%. The sheet is preferably in the form of a strip suitable for coating in a continuous galvanizing or galvannealing line, and the product is predominantly ferrite and martensite. The strip may be galvanized or galvannealed at a temperature within thirty degrees F. of the temperature of the bath.
REFERENCES:
patent: 4544419 (1985-10-01), Irie et al.
patent: 4759807 (1988-07-01), Sippola
patent: 5019460 (1991-05-01), Yasuda et al.
patent: 6306527 (2001-10-01), Ikeda et al.
patent: 6312536 (2001-11-01), Omiya et al.
patent: 6316127 (2001-11-01), Ikeda et al.
patent: 6440584 (2002-08-01), Nagataki et al.
patent: 6517955 (2003-02-01), Takada et al.
patent: 6586117 (2003-07-01), Nomura et al.
patent: 6635313 (2003-10-01), Pradhan et al.
patent: 6641931 (2003-11-01), Claessens et al.
patent: 6811624 (2004-11-01), Hoydick
patent: 4-26744 (1992-01-01), None
patent: 4-128320 (1992-04-01), None
patent: 4-128321 (1992-04-01), None
patent: 4-173945 (1992-06-01), None
patent: 5-331537 (1993-12-01), None
patent: 9-25537 (1997-01-01), None
patent: 9-263883 (1997-10-01), None
Yoichi Tobiyama et al, “Development of 590 MPa Grade Galvannealed Sheet Steels with Dual Phase Structure,” Kawasaki Steel Technical Report, Kawasaki Steel, p. 19-23, ( May 14, 2000).
L.F.Porter and P.E. Repas, “The Evolution of HSLA Steels,” Journal of Metals, p. 14-21, ( Apr. 14, 1982).
Jayanta S. Rege, Toru Inazumi et al, “Development of HDGI/HDGA Dual Phase Steel Family . . . at National Steel Corporation,” 44th MWSP Conference Proceedings, Iron and Steel Society, p. 391-403, ( May 28, 2002).
A. Pichler, G. Hribernig et al, “Aspects of the Production of Dual Phase and Multiphase Steel Strips,” MWSP Conference Prodceedings, Iron and Steel Society, p. 37-59, ( May 28, 1999).
Krayer William L.
United States Steel Corporation
Wyszomierski George P.
LandOfFree
Dual phase steel strip suitable for galvanizing does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Dual phase steel strip suitable for galvanizing, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Dual phase steel strip suitable for galvanizing will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3863394